Abstract
Meta-poly(phthalazinone ether ketone ketone) copolymers with 4,4′-dihydroxybiphenyls (meta-PPBEKK) was synthesized with 4,4′-dihydroxybiphenyls (BP), 1,3-bis(4-fluorobenzoyl)benzene (meta-DFKK) and 4-(4-hydroxyphenyl)-2,3-diazaphthalene-1-one (DHPZ). The copolymers are high-temperature resistant and have good solubility in many solvents. With increasing molar ratio of BP to meta-DFKK from 0 to 0.2, the addition of BP improves number-average molecular masses, intrinsic viscosity, mechanical properties and fluidity of meta-PPBEKKs. When the molar ratio of BP to meta-DFKK is 0.2, the intrinsic viscosity reaches 1.14 dL g−1, the number-average molecular mass reaches 44700 g mol−1, the maximum thermal elongation ratio reaches 14 with strength of 127.1 MPa and Young’s modulus of 2.4 GPa. With increasing molar ratio of BP to meta-DFKK from 0 to 0.2, meta-PPBEKKs have improved comprehensive properties, and make sense in many fields.
Keywords
Get full access to this article
View all access options for this article.
References
Supplementary Material
Please find the following supplemental material available below.
For Open Access articles published under a Creative Commons License, all supplemental material carries the same license as the article it is associated with.
For non-Open Access articles published, all supplemental material carries a non-exclusive license, and permission requests for re-use of supplemental material or any part of supplemental material shall be sent directly to the copyright owner as specified in the copyright notice associated with the article.