Phthalonitrile polymers have potential for high-temperature applications in polymer matrix composites as electronic encapsulation compounds. To investigate the effect of inclusion of an organosilicon moiety, a tetraphenylsilane-containing phthalonitrile monomer was synthesized in high yields. The monomer possessed a high melting point of 222–223°C, while no hydrolytic sensitivity was observed. Cured polymers exhibited glass transitions in the range of 290–325°C and coefficients of thermal expansion of 73–77 µm/(m °C). In thermogravimetric analysis (TGA), 5 wt% loss was observed at 482–497°C and 519–526°C, under air and nitrogen, respectively. Infrared (IR)-TGA of evolved gases revealed multiple degradations in both nitrogen and air. The material possessed good thermo-oxidative stability (TOS) when aged in air at 250°C. After aging for 5000 h, oxidative degradation was characterized using Fourier transform IR microscopy, energy dispersive spectroscopy, optical microscopy, and Knoop hardness testing. Four zones were identified in aged samples. The cleavage of Si-phenyl bonds and the formation of Si–O phases and carbonyl groups were observed.
LaskoskiMDominguezDDKellerTM. Synthesis and properties of a bisphenol a based phthalonitrile resin. J Polym Sci A Polym Chem2005; 43: 4136–4143.
3.
LaskoskiMNealAKellerTM, et al.Improved synthesis of oligomeric phthalonitriles and studies designed for low temperature cure. J Polym Sci A Polym Chem2014; 52: 1662–1668.
4.
LaskoskiMNealASchearMB, et al.Oligomeric aliphatic–aromatic ether containing phthalonitrile resins. J Polym Sci A Polym Chem2015; 53: 2186–2191.
5.
TongLJiaKLiuX. Novel phthalonitrile-terminated polyarylene ether nitrile with high glass transition temperature and enhanced thermal stability. Mater Let2014; 128: 267–270.
6.
LiuY. Packaging of silicon carbide high temperature, high power devices - processes and materials. Electrical and computer engineering. Auburn: Auburn University, 2006, p. 132.
7.
DominguezDDKellerTM. Low-melting phthalonitrile oligomers: preparation, polymerization and polymer properties. High Perform Polym2006; 18: 283–304.
PengXShengHGuoH, et al.Synthesis and properties of a novel high-temperature diphenyl sulfone-based phthalonitrile polymer. High Perform Polym2014; 26: 837–845.
10.
MatthewLClarkeJSAriannaN, et al.Sustainable high-temperature phthalonitrile resins derived from resveratrol and dihydroresveratrol. Chem Select2016; 1: 3423–3427.
11.
PandeyMKKhanARSaxenaAK. Synthesis and thermal analysis of phosphonitrile-core-bearing aromatic nitriles for high-temperature applications. J Therm Anal Calorim2017; 129: 1453–14562.
12.
KellerTMDominguezDDLaskoskiM. Oligomeric bisphenol A-based PEEK-like phthalonitrile-cure and polymer properties. J Polym Sci A Polym Chem2016; 54: 3769–3777.
13.
ShengHZhaoFYuX, et al.Synthesis and thermal properties of high-temperature phthalonitrile polymers based on 1,3,5-triazines. High Perform Polym2016; 28: 600–609.
14.
LiuTYangYWangT, et al.Synthesis and properties of poly(aryl ether ketone)-based phthalonitrile resins. Polym Eng Sci2014; 54: 1695–703.
15.
LaskoskiMDominguezDDKellerTM. Synthesis and properties of aromatic ether phosphine oxide containing oligomeric phthalonitrile resins with improved oxidative stability. Polymer2007; 48: 6234–6340.
16.
DominguezDDKellerTM. Properties of phthalonitrile monomer blends and thermosetting phthalonitrile copolymers. Polymer2007; 48: 91–97.
17.
LaskoskiMKellerTMRicks-LaskoskiHL, et al.Improved synthesis of oligomeric sulfone-based phthalonitriles. Macromol Chem Phys2015; 216: 1808–1815.
18.
LaskoskiMSchearMBNealA, et al.Improved synthesis and properties of aryl ether-based oligomeric phthalonitrile resins and polymers. Polymer2015; 67: 185–1891.
19.
KellerTMDominguezDD. High temperature resorcinol-based phthalonitrile polymer. Polymer2005; 46: 4614–4618.
20.
ZhaoEHuJWangJ, et al.Preparation and properties of phthalonitrile resins promoted by melamine. High Perform Polym2018; 30: 561–570.
21.
LiuTYanWSuY, et al.Synthesis and characterization of hyperbranched poly(aryl ether ketone) terminated with phthalonitrile group. High Perform Polym2016; 28: 263–270.
22.
WarzelMLKellerTM. Tensile and fracture properties of a phthalonitrile polymer. Polymer1993; 34: 663–666.
23.
BulgakovBABabkinAVDzhevakovPB, et al.Low-melting phthalonitrile thermosetting monomers with siloxane- and phosphate bridges. Eur Polym J2016; 84: 205–217.
24.
AndrewJGuenthnerVVHaddadTS, et al.Silicon-containing tri-and tetra-functional cyanate esters: synthesis, cure kinetics, and network properties. Edwards AFB CA: Air Force Research Lab Aerospace Systems Directorate, 2014, p. 58, ADA598433.
25.
GuenthnerAJYandekGRWrightME, et al.A new silicon-containing bis(cyanate) ester resin with improved thermal oxidation and moisture resistance. Macromolecules2006; 39: 6046–6053.
26.
GuenthnerAJVijVHaddadTS, et al.Silicon-containing trifunctional and tetrafunctional cyanate esters: synthesis, cure kinetics, and network properties. J Polym Sci A Polym Chem2014; 52: 767–779.
27.
ZhuoDXGuAJLiangGZ, et al.Flame retardancy materials based on a novel fully end-capped hyperbranched polysiloxane and bismaleimide/diallylbisphenol a resin with simultaneously improved integrated performance. J Mater Chem2011; 21: 6584–6594.
28.
ChenXXYeJHYuanL, et al.Multi-functional ladderlike polysiloxane: synthesis, characterization and its high performance flame retarding bismaleimide resins with simultaneously improved thermal resistance, dimensional stability and dielectric properties. J Mater Chem2014; 2: 7491–7501.
RegnierNGuibeC. Methodology for multistage degradation of polyimide polymer. Polym Degrad Stab1997; 55: 165–172.
31.
FitzgeraldJJTunneySELandryMR. Synthesis and characterization of a fluorinated poly(imide-siloxane) copolymer: a study of physical properties and morphology. Polymer1993; 34: 1823–1832.
32.
XiKMengZHengL, et al.Polyimide–polydimethylsiloxane copolymers for low-dielectric-constant and moisture-resistance applications. J Appl Polym Sci2009; 113: 1633–1641.
33.
GhoshABanerjeeSKomberH, et al.Synthesis and characterization of fluorinated poly(imide siloxane) block copolymers. Eur Polym J2009; 45: 1561–1569.
SaxenaKBisariaCSKalraSJS, et al.Synthesis of some novel silicone-imide hybrid inorganic–organic polymer and their properties. Prog Org Coat2015; 78: 234–238.
36.
DamaceanuMRusuRBrumaM, et al.Thin polyimide films for dielectric interlayer application. In: Semiconductor Conference, 2009 CAS 2009 International, Sinaia, Romania, 12–14 October 2009, pp. 351–354. IEEE.
37.
DamaceanuMDMusteataVECristeaM, et al.Viscoelastic and dielectric behaviour of thin films made from siloxane-containing poly(oxadiazole-imide)S. Eur Polym J2010; 46: 1049–1062.
38.
TiwariANemaAKDasCK, et al.Thermal analysis of polysiloxanes, aromatic polyimide and their blends. Thermochim Acta2004; 417: 133–142.
ZhuoDXGuAJLiangGZ, et al.Flame retardancy and flame retarding mechanism of high performance hyperbranched polysiloxane modified bismaleimide/cyanate ester resin. Polym Degrad Stab2011; 96: 505–514.
41.
MorganABPutthanaratS. Use of inorganic materials to enhance thermal stability and flammability behavior of a polyimide. Polym Degrad Stab2011; 96: 23–32.
42.
YudasakaITanakaHMiyasakaM, et al.27.2: poly-si thin-film transistors using polysilazane-based spin-on glass for all dielectric layers. SID Sympos Dig Tech Paper2004; 35: 964–967.
43.
JovanovicJDGovedaricaMNDvornicPR, et al.The thermogravimetric analysis of some polysiloxanes. Polym Degrad Stab1998; 61: 87–93.
44.
KhazakaRLocatelliMLDiahamS, et al.Effects of mechanical stresses, thickness and atmosphere on aging of polyimide thin films at high temperature. Polym Degrad Stab2013; 98: 361–367.
45.
ZhangZBLiZZhouH, et al.Self-catalyzed silicon-containing phthalonitrile resins with low melting point, excellent solubility and thermal stability. J Appl Polym Sci2014; 131: 40919.
46.
BabkinAVZodbinovEBBulgakovBA, et al.Low-melting siloxane-bridged phthalonitriles for heat-resistant matrices. Eur Polym J2015; 66: 452–457.
47.
WangMNingY. Oligosilylarylnitrile: the thermoresistant thermosetting resin with high comprehensive properties. ACS Appl Mater Interfaces2018; 10: 11933–11940.
48.
DzhevakovPBKorotkovRFBulgakovBA, et al.Synthesis and polymerization of disiloxane Si–O–Si-linked phthalonitrile monomer. Mendeleev Commun2016; 26: 527–529.
49.
LiXYuBZhangD, et al.Cure behavior and thermomechanical properties of phthalonitrile–polyhedral oligomeric silsesquioxane copolymers. Polymers2017; 9: 334.
50.
TerrazaCATagleLHTundidor-CambaA, et al.Synthesis and characterization of aromatic poly(ether-imide)S based on bis(4-(3,4-dicarboxyphenoxy)phenyl)-R, R-silane anhydrides (R = Me, Ph) - spontaneous formation of surface micropores from the solutions. RSC Adv2016; 6: 49335–49347.
51.
HardrictSN. Novel novolac-phthalonitrile and siloxane-phthalonitrile resins cured with low melting novolac oligomers for flame retardant structural thermosets. Chemistry Blacksburg: Virginia Polytechnic Institute and State University, 2003, p. 126.
52.
MayaEMSnowAWShirkJS, et al.Synthesis, aggregation behavior and nonlinear absorption properties of lead phthalocyanines substituted with siloxane chains. J Mater Chem2003; 13: 1603–1613.
53.
MartinRTHughLNMMartinER. High-temperature properties and applications of polymeric materials. In: MartinRTConnellJWHughLNM (ed.), High-temperature properties and applications of polymeric materials. Washington, DC: American Chemical Society, 1995, pp. 1–20.
54.
BeattieSR. The thermal decomposition of some silphenylene siloxane polymers. Glasgow: Chemistry Department. University of Glasgow, 1981.
55.
YangZHanSZhangR, et al.Effects of silphenylene units on the thermal stability of silicone resins. Polym Degrad Stab2011; 96: 2145–2151.
56.
SunJTHuangYDCaoHL, et al.Effects of ambient-temperature curing agents on the thermal stability of poly(methylphenylsiloxane). Polym Degrad Stab2004; 85: 725–731.
57.
YangFLiYMaT, et al.Synthesis and characterization of fluorinated polyimides derived from novel unsymmetrical diamines. J Fluorine Chem2010; 131: 767–775.
58.
LiawDJWangKLHuangYC, et al.Advanced polyimide materials: syntheses, physical properties and applications. Prog Polym Sci2012; 37: 907–974.
LeeDCTobiasHKorgelAB. The role of precursor-decomposition kinetics in silicon-nanowire synthesis in organic solvents. Angew Chem Int Ed2005; 44: 3573–3537.
61.
LeeENelsonNCADonaldR. Weyenberg. The free radical-catalyzed disproportionation of arylsilanes. A new homolytic aromatic displacement reaction. J Am Chem Soc1963; 85: 2662–2623.
62.
DavidsohnWLaliberteBRGoddardCM, et al.Organometallic bis(P-hydroxyphenyl) derivatives of group IV elements and related compounds. J Organomet Chem1972; 36: 283–291.
63.
TagleLHVegaJCDiazFR, et al.Polymerization by phase transfer catalysis. 25. synthesis of polycarbonates and polythiocarbonates derived from diphenols containing germanium and silicon in the main chain. J Macromol Sci A2000; 37: 997–1008.
64.
TerrazaCATagleLHConchaF, et al.Synthesis and characterization of new bi-functional monomers based on germarylene or silarylene units: 4,4′-(R1R2-silylene)bis(phenyl chloroformates) and 4,4′-(R1R2-germylene)bis(phenyl chloroformates). Des Mono Polym2007; 10: 253–261.
65.
GilmanHGoodmanJJ. Some monomeric organosilicon compounds of high thermal stability. J Org Chem1957; 22: 45–47.
66.
SchnabelWJ. Bis-aryloxyphenyl-dialkylsilanes. Augusta: Olin Mathieson Chem, 1961, p. 3.
67.
ZhaoFLiuRKangC, et al.A novel high-temperature naphthyl-based phthalonitrile polymer: synthesis and properties. RSC Adv2014; 4: 8383–8390.
68.
LiuTWangYSuY, et al.Preparation and properties of film materials of poly(aryl ether ketone)–based phthalonitrile resins. J Polym Sci2015; 55: 2313–2321.
SatyaBSastriJPAKellerTM. Flame resistant phthalonitrile composites. In: International fire and cabin safety research conference Atlantic city, NJ, 1998.
71.
MouritzAPGibsonAG. Fire properties of polymer composite materials (solid mechanics and its applications). Dordrecht: Springer, 2006.
72.
SorathiaU. 19 - Flame retardant materials for maritime and naval applications. In: HorrocksARPriceD (eds.), Advances in fire retardant materials. Sawston: Woodhead, 2008, pp. 527–572.
73.
Properties of unreinforced cyanate ester matrix resins. In: HamertonI (ed.), Chemistry and technology of cyanate ester resins, 1th ed. Chapman & Hall: Department of Chemistry University of Surrey, 1994, pp. 193–229.
74.
LyonREWaltersRNGandhiS. Combustibility of cyanate ester resins. Fire Mater2006; 30: 89–106.
75.
ChenMZhouBLiaoY, et al.Synthesis and investigation of the properties of a star-shaped polysilane. Mater Lett2009; 63: 2032–2034.
76.
DeshpandeGRezacME. Kinetic aspects of the thermal degradation of poly(dimethyl siloxane) and poly(dimethyl diphenyl siloxane). Polym Degrad Stab2002; 76: 17–24.
77.
DeshpandeGRezacME. The effect of phenyl content on the degradation of poly(dimethyl diphenyl) siloxane copolymers. Polym Degrad Stab2001; 74: 363–370.
78.
PochirajuKVTandonGP. Modeling thermo-oxidative layer growth in high-temperature resins. J Eng Mater Technol2005; 128: 107–116.
79.
ZhouWYangHGuoX, et al.Thermal degradation behaviors of some branched and linear polysiloxanes. Polym Degrad Stab2006; 91: 1471–1475.
80.
SteeleWV. The standard enthalpy of formation of tetraphenylsilane and the Ph-M mean bond-dissociation energies of the group IV elements. J Chem Thermodyn1978; 10: 445–452.
81.
CoutantWRArthurL. A kinetic study of the thermal decomposition of selected cyclohexyl and phenylsilanes. Air force research laboratories, office of aerospace research, wright patterson air force base. Ohio: Battelle Memorial Inst Columbus Ohio Columbus Labs, 1969.
82.
GilmanHMilesD. Communications - disproportionation reaction of diphenylsilane in the absence of any added catalyst. J Org Chem1958; 23: 326–328.
Supplementary Material
Please find the following supplemental material available below.
For Open Access articles published under a Creative Commons License, all supplemental material carries the same license as the article it is associated with.
For non-Open Access articles published, all supplemental material carries a non-exclusive license, and permission requests for re-use of supplemental material or any part of supplemental material shall be sent directly to the copyright owner as specified in the copyright notice associated with the article.