A series of isomeric poly(thioether imide)s (PTIs) containing thioether linkages were prepared by aromatic nucleophilic substitution reaction of isomeric bis(chlorophthalimide)s (BCPIs) and bisthiophenols. The glass transition temperatures (Tgs) of the isomeric PTIs were 190–264°C, the 5% weight loss temperature (T5%) reached up to 441–508°C under nitrogen and 472–520°C in air atmospheres, respectively. It was found that the Tg values of the PTIs from three isomeric BCPIs with the same bisthiophenol increased in the order of 4,4′-BCPI < 3,4′-BCPI < 3,3′-BCPI, while the T5% values gradually decreased in the order of 4,4′-BCPI > 3,4′-BCPI > 3,3′-BCPI. Flexible films that could be cast from the polymer solutions exhibited good mechanical properties with tensile strengths of 91–121 MPa, elongations at break of 8–12%, and tensile moduli of 2.2–2.6 GPa. The minimum melt viscosity of isomeric PTIs decreased with increasing the content of asymmetric 3,4′-substituted phthalimide unit, and the PTI (2c) showed the lowest melt viscosity about 760 Pa·s at 264°C among these isomeric polymers.
GhoshMKMittalKL. Polyimide: Fundamentals and application. NewYork: Marcel Dekker.
5.
HasegawaMHorieK. Photophysics, photochemistry, and optical properties of polyimides. Prog Polym Sci2001; 26: 259–335.
6.
HsiaoSHHuangPC. Synthesis and characterization of polyimides based on isopropylidene-containing bis(ether anhydride)s. J Polym Res1997; 4: 183–190.
7.
HsiaoSHDaiLR. Synthesis and properties of poly(ether imide)s based on the bis(ether anhydride)s from hydroquinone and its derivatives. J Polym Sci Part A Polym Chem1999; 37: 665–675.
8.
ChungISKimSY. Soluble polyimides from unsymmetrical diamine with trifluoromethyl pendent group. Macromolecules2000; 33: 3190–3193.
9.
ChernYTShiueHC. Low dielectric constants of soluble polyimides derived from the novel4,9-bis[4-(4-aminophenoxy)phenyl] diamantane. Macromolecules1997; 30: 5766–5772.
LiQXFangXZWangZ. Polyimides from isomeric oxydiphthalic anhydrides. J Polym Sci Part A Polym Chem2003; 41: 3249–3260.
14.
FangXZWangZYangZH. Novel polyimides derived from 2,3,3′,4′-benzophenonetetracarboxylic dianhydride. Polymer2003; 44: 2641–2646.
15.
ZhangMWangZGaoLX. Polyimides from isomeric diphenylthioether dianhydrides. J Polym Sci Part A Polym Chem2006; 44: 959–967.
16.
YanJLWangZGaoLX. Synthesis and properties of polyimides from isomeric bis(dicarboxylphenylthio)diphenyl sulfone dianhydrides. Polymer2005; 46: 7678–7683.
17.
DingMXLiHYYangZH. Comparative study on polyimides from 3,3′- and 4,4′-linked diphthalic anhydride. J Appl Polym Sci1996; 59: 923–930.
18.
HergenrotherPMWatsonKASmithJGJr. Polyimides from 2,3,3′,4′-biphenyltetracarboxylic dianhydride and aromatic diamines. Polymer2002; 43: 5077–5093.
19.
ChenCHYokotaRHasegawaM. Isomeric biphenyl polyimides. (i) chemical structure-property relationships. High Perform Polym2005; 17: 317–333.
20.
ShiZMHasegawaMShindoY. Thermo-processable polyimides with high thermo-oxidative stability as derived from oxydiphthalic anhydride and bisphenol A type dianhydride. High Perform Polym2000; 12: 377–393.
21.
HasegawaMShiZMYokataR. Thermo-processable polyimides with high Tg and high thermo-oxidative stability as derived from 2,3,3′,4′-biphenyltetracarboxylic dianhydride. High Perform Polym2001; 13: 355–364.
22.
WeiHBPeiXLFangXZ. Comparative study on polyimides from isomeric 3,3′-, 3,4′-, and 4,4′-linked bis(thioether anhydride)s. J Polym Sci A Polym Chem2011; 49: 2484–2494.
23.
LiuJTChenGFFangXZ. Preparation, characterization, and properties of poly(thioether ether imide)s from isomeric bis(chlorophthalimide)s and 4,4′-thiobisbenzenethiol. Polym Adv Technol2014; 25: 329–337.
24.
LiuJTChenGFFangXZ. Preparation, characterization, and properties of poly(thioether ether imide)s from isomeric bis(chlorophthalimide)s and bis(4-mercaptophenyl) ether. High Perform Polym2014. 27: 112–121.
25.
WeiHBFangXZHanY. Synthesis and characterization of poly(thioether ether sulfone imide)s derived from isomeric bis(chlorophthalimide)s and bis(4-mercaptophenyl) sulfone. Eur Polym J2010; 46: 246–253.
26.
WeiHBWuXSHuBL. Preparation, characterization, and properties of poly(thioether ether ketone imide)s from isomeric bis(chlorophthalimide)s. Polym Adv Technol2011; 22: 2488–2495.
27.
GaoCLWuXELvGH. Syntheses and properties of soluble biphenyl-based polyimides from asymmetric bis(chlorophthalimide)s. Macromolecules2004; 37: 2754–2761.
28.
GaoCLZhangSBGaoLX. Syntheses of biphenyl polyimides via nickel-catalyzed coupling polymerization of bis(chlorophthalimide)s. Macromolecules2003; 36: 5559–5565.
29.
DingYBiksonBNelsonJK. Polyimide membranes derived from poly (amic acid) salt precursor polymers. 2. Composite membrane preparation. Macromolecules2002; 35: 912–916.
30.
FacinelliJVGardnerSLDongL. Controlled molecular weight polyimides from poly(amic acid) salt precursors. Macromolecules1996; 29: 7342–7350.
31.
YamanakaKJikeiMKakimotoM. Preparation and properties of hyperbranched aromatic polyimides via polyamic acid methyl ester precursors. Macromolecules2000; 33: 6937–6944.
32.
LeeHJWonJParkHC. Effect of poly (amic acid) imidization on solution characteristics and membrane morphology. J Membrane Sci2000; 178: 35–41.
33.
DingYHayAS. Synthesis and characterization of amorphous aromatic poly(thioether ketone)s and poly(thioether phenyl phosphine oxide)s. J Macromol Sci Pure Appl Chem A1997; 34: 405–415.
34.
OkutsuRSuzukiYAndoS. Poly(thioether sulfone) with High refractive index and high Abbe’s number. Macromolecules2008; 41: 6165–6168.
35.
MatsumuraSKiharaNTakataT. Synthesis and properties of novel aromatic poly(thioether-ketone)s as sulfur-containing high-performance polymers. Macromolecules2001; 34: 2848–2853.
36.
WilliamsFJDonahuePE. Reactions of phenoxides with nitro- and halo-substituted phthalimides. J Org Chem1977; 42: 3414–3419.
37.
WilliamsFJDonahuePE. Reaction of thiophenoxides with nitro-substituted and halo-substituted phthalimide derivatives. J Org Chem1978; 43: 250–254.
38.
WilliamsFJDonahuePE. Reaction of thiophenoxides with nitro- and halo-substituted phthalic anhydrides. J Org Chem1978; 43: 255–258.
39.
LiuJGShibasakiYAndoS. Synthesis and thermal properties of polythioetherimides derived from 4,4′-[p-thiobis(phenylenesulfanyl)]diphthalic anhydride and various aromatic diamines. High Perform Polym2007; 20: 221–237.
40.
LiXGHuangMRBaiH. High-resolution thermogravimetry of polyphenylene sulfide film under four atmospheres. J Appl Polym Sci2002; 83: 2053–2059.
41.
HanYFangXZZuoXX. Melt processable homo- and copolyimides with high thermo-oxidative stability as derived from mixed thioetherdiphthalic anhydride isomers. eXPRESS Polym Lett2010; 4: 712–722.
42.
KurokiT (Mitsui Chemicals, Inc.). Crystalline polyimide for melt molding with satisfactory thermal stability. Patent 6,458,912, USA, 2002.
43.
ZengHLPeiXLChenGF. Comparative studies on melt processable polyimides derived from 2,3,3′,4′-oxydiphthalic anhydride and 2,3,3′,4′-thioetherdiphthalic anhydride. High Perform Polym2013; 25: 454–463.
44.
SoccioMLottiNFinelliL. Thermal characterization of novel aliphatic polyesters with ether and thioether linkages. e-Polymers2011; 35: 1–12.