A new kind of carborane-containing aromatic diamine, 1,2-bis (4-aminophenyl)-1,2-dicarba-closo-dodecaborane (HPPA), as a curing agent for epoxy resins was synthesized and confirmed by proton, carbon and boron nuclear magnetic resonance imaging, Fourier transform infrared spectroscopy and elemental analysis. The compatibility, thermal curing behaviour and thermal properties of HPPA/epoxy resin E51 system were investigated. HPPA exhibited good compatibility with E51. Compared with 4,4′-diaminodiphenylsulphone (DDS)/E51, HPPA/E51 system had higher reaction activity and lower curing temperature. When the ratio of amine protons versus epoxy groups was 1:1 in resin systems, the epoxy resin cured by HPPA exhibited the highest glass transition temperature of 207°C. The residual weight ratios of cured HPPA/E51 at 800°C under argon and in air atmospheres were 43.7% and 50.5%, respectively, which were 28.6% and 47.2% higher than that of DDS/E51, respectively, indicating that the HPPA/E51 system had good heat resistance.
YangGFuSYYangJP. Preparation and mechanical properties of modified epoxy resins with flexible diamines. Polymer2007; 48: 302–310.
2.
MustataFTudorachiNBicuI. Thermosetting resins obtained via sequential photo and thermal crosslinking of epoxy resins. Curing kinetics, thermal properties and morphology. Compos B: Eng2013; 55: 470–478.
3.
SemotoTTsujiYYoshizawaK. Molecular understanding of the adhesive force between a metal oxide surface and an epoxy resin. J Phys Chem C2011; 115: 11701–11708.
4.
LuXHuangYZhangC. Curing behavior and heat resistance of epoxy resin cured by diamine with heterocyclic ring. J Reinf Plast Compos2007; 26: 1713–1723.
5.
RenHTangSSyedJA. A naphthyl-imide-based epoxy resin: cure kinetics and application in carbon fiber reinforced composites. High Perform Polym2012; 24: 580–588.
6.
AkutsuFInokiMDaichoN. Curing behavior and properties of epoxy resins cured with the diamine having the quinoxaline or triazine structure. J Appl Polym Sci1998; 69: 1737–1741.
7.
InokiMKimuraSDaichoN. Curing behavior and properties of epoxy resins cured with the diamine having heterocyclic ring. J Macromol Sci A2002; 39: 321–331.
8.
QinJZhangGSunR. Synthesis of aromatic amine curing agent containing non-coplanar rigid moieties and its curing kinetics with epoxy resin. J Therm Anal Calorim2014; 117: 831–843.
9.
GhumaraRYAdrojaPPParsaniaP. Synthesis, characterization, and dynamic DSC curing kinetics of novel epoxy resin of 2,4,6-tris(4-hydroxyphenyl)-1-3-5-triazine. J Therm Anal Calorim2013; 114: 873–881.
10.
FengLWangYWangY. Study on reaction kinetics of epoxy resin cured by a modified dicyandiamide. J Appl Polym Sci2013; 127: 1895–1900.
11.
MartinJLazaJMorrasM. Study of the curing process of a vinyl ester resin by means of TSR and DMTA. Polymer2000; 41: 4203–4211.
12.
WangFLiSQWangJW. Effect of functionalized multi-walled carbon nanotubes on the curing behavior and thermal stability of epoxy resin. High Perform Polym2012; 24: 97–104.
13.
ValliantJFGuentherKJKingAS. The medicinal chemistry of carboranes. Coord Chem Rev2002; 232: 173–230.
14.
KokadoKChujoY. Emission via aggregation of alternating polymers with o-carborane and p-phenylene–ethynylene sequences. Macromolecules2009; 42: 1418–1420.
15.
PetersonJJWerreMSimonYC. Carborane-containing polyfluorene: o-carborane in the main chain. Macromolecules2009; 42: 8594–8598.
16.
DelmanAKellyJSimmsB. Thermal stability of structurally related polymers containing carborane and phthalocyanine groups. J Polym Sci Polym Chem1970; 8: 111–123.
17.
HendersonLJKellerTM. Synthesis and characterization of poly(carborane-siloxane-acetylene). Macromolecules1994; 27: 1660–1661.
18.
LuSYHamertonI. Recent developments in the chemistry of halogen-free flame retardant polymers. Prog Polym Sci2002; 27: 1661–1712.
19.
EndoYSongkramCYamasakiR. Molecular construction based on icosahedral carboranes and aromatic N,N-dimethylurea groups. Aromatic layered molecules and a transition metal complex. J Organomet Chem2002; 657: 48–58.
20.
LiuYLHsiueGHChiuYS. Synthesis, characterization, thermal, and flame retardant properties of phosphate-based epoxy resins. J Polym Sci, A: Polym Chem1997; 35: 565–574.
21.
ShangCYZhaoXJYangX. Epoxy resin containing trifluoromethyl and pendant polyfluorinated phenyl groups: synthesis and properties. High Perform Polym. Epub ahead of print 29 November 2012. DOI: 10.1177/0954008312449844.
KissingerHE. Variation of peak temperature with heating rate in differential thermal analysis. J Res Nat Bur Stand1956; 57: 217–221.
24.
CraneLDynesPKaelbleD. Analysis of curing kinetics in polymer composites. J Polym Sci: Polym Lett Ed1973; 11: 533–540.
25.
HillDJGeorgeGARogersDG. A systematic study of the microwave and thermal cure kinetics of the DGEBA/DDS and DGEBA/DDM epoxy-amine resin systems. Polym Adv Technol2002; 13: 353–362.
26.
BarghamadiMBehmadiH. Influence of the epoxy functionalization of multiwall carbon nanotubes on the nonisothermal cure kinetics and thermal properties of epoxy/multiwall carbon nanotube nanocomposites. Polym Compos2012; 33: 1085–1093.
27.
LinHTLinCHHuYM. An approach to develop high-Tg epoxy resins for halogen-free copper clad laminates. Polymer2009; 50: 5685–5692.
28.
ZhuJWuYZhaoL. Study of thermal properties of curing of DGEBA epoxy resin with hexakis-(4-aminophenoxy)-cyclotriphosphazene. Adv Mater Res2011; 284: 365–368.
29.
BraunUBalabanovichAISchartelB. Influence of the oxidation state of phosphorus on the decomposition and fire behaviour of flame-retarded epoxy resin composites. Polymer2006; 47: 8495–8508.
30.
LevchikSVCaminoGLudaMP. Epoxy resins cured with aminophenylmethylphosphine oxide-II. Mechanism of thermal decomposition. Polym Degrad Stab1998; 60: 169–183.
31.
PaamaLPitkãnenIPerämäkiP. Analysis of archaeological samples and local clays using ICP-AES, TG-DTG and FTIR techniques. Talanta2000; 51: 349–357.
XuGRXuMJLiB. Synthesis and characterization of a novel epoxy resin based on cyclotriphosphazene and its thermal degradation and flammability performance. Polym Degrad Stab2014; 109: 240–248.
34.
VinogradovaSVValetskiiPMKabachiiYA. Polymers with arylenedicarbadodecaborane fragments in the chain. Russ Chem Rev1995; 64: 365–388.
35.
LyamenkovaYKZhuravlevaIAyupovaR. The thermal and thermal-oxidative degradation of the polyarylate from 1,2-bis-(4-hydroxyphenyl)carborane and 1,2-bis-(4-carboxyphenyl)carbonarane. Polym Sci USSR1975; 17: 801–809.
36.
SchwammDKuligJLittM. X-ray photoelectron spectroscopic depth profiling of an atomic oxygen resistant poly(carborane-siloxane) coating. Chem Mater1991; 3: 616–620.