The main objective of this study was to investigate the relationship between consolidation quality and interlaminar fracture of CF/PEEK composites manufactured from commingled prepreg. A compression molding system using a hot press was applied to simulate the effect of processing conditions, such as holding time (10, 30 and 60 min) and processing temperature (400'C and 415'C). Consolidation quality was studied through void content and density measurement, while transverse flexural (TF) properties of consolidated CF/PEEK composites were measured and correlated with the processing conditions. Mode-I and mode-II interlaminar fracture behavior was studied using double cantilever beam (DCB) and end notch flexure (ENF) specimens. The results indicated that the consolidation quality of the composites is highly dependent on processing conditions, and it was clearly improved at 400'C when the holding time was increased from 10 to 60 min. Material degradation was observed for the composite produced at 415'C, especially when a long holding time was applied. Mode-I interlaminar fracture growth resistance had little correlation with consolidation quality, while apparent mode-II interlaminar fracture toughness decreased as the void content was reduced. Fracture mechanisms associated with material microstructure are discussed. The results indicate that consolidation quality is not the only aspect that controls interlaminar fracture properties.
1. Cattanach, J. B., G. Guff and F. N. Cogswell. 1986. "The Processing of Thermoplastics Containing High Loadings of Long and Continuous Reinforcing Fibres;' Journal of Polymer Engineering, 6(1-4). Proceedings of the 1st Meeting of the Polymer Processing Society, Akron, U.S.A., pp. 345-362.
2.
2. Moore, D. R. and J. C. Seferis, et al. 1991. "Intrinsic Characterization of Continuous Fibre Reinforced Thermoplastic Composites-1: Toughness Characterization of Carbon Fibre/Polyether Ether Ketone (CF/PEEK) Laminates,"Pure and Applied Chemistry, 24:1610-1625.
3.
3. Chang, I. Y. and J. K. Lees. 1988. "Recent Development in Thermoplastic Composites: A Review of Matrix Systems and Processing Methods,"Journal of Thermoplastic Composite Materials, 1:277-295.
4.
4. Leung, C.-L. and T. T. Liao. 1989. "Process Modeling of Thermoplastic Matrix Composites," in Advances in Thermoplastic Composite Materials, ASTM STh 1044, G. M. Newaz, ed., ASTM, pp. 5-13.
5.
5. Rigby, R. B.1985. "Polyetheretherketone," in Engineering Thermoplastics, Properties and Applications, J. M. Margolis, ed., Marcel Dekker, Inc., pp. 299-314.
7. Cogswell, F. N.1992. Thermoplastic Aromatic Polymer Composites, Butterworth-Heinemann Ltd.
8.
8. Ye, L., K. Friedrich, D. Cutolo and A. Savadori. 1994. "Manufacture of CF/PEEK Composites from Powder/Sheath Preforms,"Composites Manufacturing, 5:41-50.
9.
9. Olson, S. H.1990. "Manufacturing with Commingled Yarns, Fabrics and Powder Prepreg Thermoplastic Composite Materials,"SAMPE Journal, 26(5):31-36.
11. Klinkmuller, V. and K. Friedrich. "Pultrusion of GF/PBT Powder-Impregnated Fibre Bundles,"Advancing with Composite Materials, International Meeting on Composite Materials, Milan, Italy, May 4-6, 1994.
12.
12. Vautey, P.1990. "Cooling Rate Effects on the Mechanical Behaviour of a Semi-Crystalline Thermoplastic Composite,"SAMPE Quarterly, 10:23-28.
13.
13. Jar, P.-Y., W. J. Cantwell and H. H. Kausch. 1992. "Study of the Crystal Morphology and the Deformation Behaviour of Carbon Fibre Reinforced PEEK (APC-2),"Composites Science and Technology, 43:299-306.
14.
14. Blundell, D. J., R. A. Crick, B. Fife, J. Peacock, A. Keller and A. Waddon. 1989. "Spherulitic Morphology of the Matrix of Thermoplastic PEEK/Carbon Fibre Aromatic Polymer Composites,"Journal of Materials Science, 24:2057-2064.
15.
15. Barlow, C. Y., J. A. Peacock and A. H. Windle. 1990. "Relationships between Microstructures and Fracture Energies in Carbon Fibre/PEEK Composites,"Composites, 21:383-388.
16.
16. Buchman, A. and A. 1. Isayev. 1991. "Quality Assurance of Various Thermoplastic Composites,"SAMPE Journal, 27(4):19-27.
17.
17. Leach, D. C., D. C. Curtis and D. R. Tamblin. 1987. "Delamination Behaviour of Carbon Fibre/Poly(Etheretherketone) (PEEK) Composites," in Toughened Composites, ASTM STP 937, N. J. Johnston, ed., ASTM, pp. 358-380.
18.
18. Hashemi, S., A. J. Kinloch and J. G. Williams. "The Effects of Geometry, Rate and Temperature on the Mode I, Mode II and Mixed-Mode I/II Interlaminar Fracture of Carbon Fibre/Poly(Ether-Ether Ketone) Composites,"Journal of Composite Materials, 24:918-956.
19.
19. Hashemi, S., A. J. Kinloch and J. G. Williams. 1989. "Corrections Needed in Double Cantilever Beam Tests for Assessing the Interlaminar Failure of Fibre Composites,"J. Materials Science Letters, 8:125-129.
20.
20. Williams, J. G.1989. "End Corrections for Orthotropic DCB Specimens,"Composites Science and Technology, 35:357-376.
21.
21. 1988. European Group on Fracture, Polymer & Composites Task Group, A Protocol for Interlaminar Fracture Testing of Composites.
22.
22. ASTM E790M-Standard Test Methods for Flexural Properties of Unreinforced and Reinforced Plastics and Electrical Insulating Materials.
23.
23. Ye, L., K. Friedrich, J. Kastle and Y.-W. Mai. 1994. "Manufacturing of CF/PEEK Composites from Commingled Yarn Preforms,"Composites Science and Technology, in press, 1995.
24.
24. Van West, B. P., R. B. Pipes and S. G. Advani. 1991. "The Consolidation of Thermoplastic Fabrics,"Polymer Composites, 12:417-427.
25.
25. WeiB, R.1990. "Influence of Production Parameters on the Mechanical Behaviour of CF/PEEK," in Proceedings of 4th European Conference on Composite Materials, J. Fuller, ed., Elsevier Applied Science, pp. 1007-1011.
26.
26. Jar, P.-Y. B., R. Mulone, P. Davies and H.-H. Kausch. 1993. 'A Study of the Effect of Forming Temperature on the Mechanical Behaviour of Carbon-Fibre/PEEK Composites,"Composites Science and Technology, 46:7-19.
27.
27. Hine, P. J., B. Brew, R. A. Duckett and I. M. Ward. 1988. "The Fracture Behaviour of Carbon Fibre Reinforced Poly(Ether Etherketone),"Composites Science and Technology, 33:35-71.
28.
28. Friedrich, K., L. A. Carlsson, J. W. Gillespie, Jr. and J. Karger-Kocsis. 1991. "Fracture of Thermoplastic Composites," in Thermoplastic Composite Materials, L. A. Carlsson, ed., R. B. Pipes, series ed., Elsevier Science Publishers, pp. 233-294.
29.
29. Johnson, W. S. and P. D. Mangalgiri. 1987. "Investigation of Fiber Bridging in Double Cantilever Beam Specimens,"Journal of Composites Technology and Research, 9(1):10-13.
30.
30. Ye, L. and K. Friedrich. 1993. "Mode I Interlaminar Fracture of Co-Mingled Yarn Based Glass/Polypropylene Composites,"Composites Science and Technology, 46:187-198.
31.
31. Davies, P. and M. L. Benzeggagh. 1989. "Interlaminar Mode-I Fracture Testing," in Application of Fracture Mechanics to Composite Materials, K. Friedrich, ed., R. B. Pipes, series ed., Elsevier Science Publications, pp. 81-112.
32.
32. ASTM D5528-94a-Standard Test Method for Mode I Interlaminar Fracture Toughness of Unidirectional Fiber-Reinforced Polymer Matrix Composites.
33.
33. Davies, P., W. J. Cantwell and H. H. Kausch. 1990. "Delamination from Thin Starter Films in Carbon Fibre/PEEK Composites,"Journal of Materials Science Letters, 9:1349-1350.
34.
34. Davies, P. et al. 1992. "Round-Robin Interlaminar Fracture Testing of Carbon-Fibre-Reinforced Epoxy and PEEK Composites,"Composites Science and Technology, 43:129-136.
35.
35. Carlsson, L. A. and J. W. Gillespie, Jr.1989. "Mode-II Interlaminar Fracture of Composites," in Application of Fracture Mechanics to Composite Materials, K. Friedrich, ed., R. B. Pipes, series ed., Elsevier Science Publishers, pp. 113-157.