Performance of a Filament Wound Graphite/Thermoplastic Composite Ring-Stiffened Pressure Hull Model

Abstract

The design, analysis, manufacture, and hydrostatic testing results of a 24- inchdiameter ringstiffened pressurehull model are presented. The AS-4 graphite/PEEK cylinder is manufactured using a nonautoclave insitu filament winding and tape laydown process. The cylinder incorporates 5 hoopwound rings and a shell (hoop/axial construction) that are integrally wound during manufacture. Ultrasonic inspection in conjunction with optical microscopy of end rings indicates that high quality is achieved with a void content of less than 1%. Translation of coupon data into the structure is quantified by subcomponent tests that measure insitu properties (A and Bbasis allowables) including shell axial compressive stiffness and strength and interlaminar shear strength. Analysis of the structure indicates that high interlaminar shear stress exists in the ring fillet areas. Subcomponent tests with supporting analysis to design the test method indicated that this failure mode was not critical. Design and analysis efforts focused on midbay and endbay performance. Axial compressive stress concentrations in the endbay were reduced by incorporating local increases in shell thickness and a steel insert ring that provided radial constraint of the shell to reduce the probability of an endbrooming failure mode. Steel hemispherical heads were designed and manufactured to further reduce axial compressive stress concentrations in the endbay. The test model was instrumented with strain gages and acoustic emission sensors and tested at Carderock Division, Naval Surface Warfare Center (CD-NSWC). Increments in pressure were followed by a 5-minute dwell time. Acoustic emission ceased for all pressures except the last two increments at 5250 and 5500 psi. The collapse pressure of 5500 psi was within 3% of our Bbasis prediction. The cylinder weight-to-displacement ratio, W/D, was 0.212 (unitless). Axial compression failure occurred in the cylinder midbay in agreement with our analysis.

References

1. Roberts, B. K. and M. A. Lamontia, et al. 1989. "Advanced Submarine Technology Thermoplastic Materials Program, Phase I, Final Report-Assessment of Current Technologies and Definition of Requirements for Use of Thermoplastics in Submarine Applications," prepared for DARPA Naval Technology office under Contract #MDA972-89-C-0043, August.

2. Roberts, B. K. and M. A. Lamontia, et al. 1991. "Advanced Submarine Technology Thermoplastic Materials Program, Phase I, Final Report-Design, Fabrication, and Testing of Thermoplastic Composite Pressure Hull Models," prepared for DARPA Naval Technology office under Contract #MDA972-89-C-0043, January.

3. Garala, H. J. 1989. Structural Evaluation of 8-Inch Diameter Graphite-Epoxy Composite Cylinders Subjected to External Hydrostatic Compressive Loading, DTRC-89/016, David Taylor Research Center, Bethesda, MD, September.

4. Pagano, N. J. 1974. "Exact Moduli of Anisotropic Laminates," Mechanics of Composite Materials, G. P. Sendeckyj , ed., Academic Press, 2:23-44.

5. Renzi, J. R. 1981. Axisymmnetric Stresses and Deflections, Interbay Buckling and General Instability of Orthotropic Hybrid Ring-Stiffened Cylindrical Shells under External Hydrostatic Pressure, Report NSWC TR 80-269, Naval Surface Warfare Center, Silver Spring, MD, April 19.

6. Gillespie, J. W., Jr. , T. A. Bogetti and M. A. Lamontia . 1991. "Influence of Ply Waviness and Residual Stress on Hydrostatic Collapse Pressure of Filament Wound Composite Cylinders," Proceedings of the 45th Meeting of the Mechanical Failures Prevention Group, Sponsored by: Office of Naval Research, David Taylor Research Center, Naval Civil Engineering Laboratory, and The Vibration Institute, April.

7. Garala, H. G. 1986. Structural Evaluation of Externally Pressurized, 4-Inch-Diameter, Graphite-Composite Cylinders, DTNSRDC-86/071, DTNSRDC, Bethesda, MD, December.

8. 1983. DOD/NASA Advanced Composites Design Guide, Wright-Patterson Air Force Base, OH: Volume IV, Materials, July.

9. BOSOR--!Buckling of Shells of Revolution," David Bushness, Dept. 93-30 Building 251, Lockheed Palo Alto Research Laboratory, 3251 Hanover St., Palo Alto, CA.