Wood plastic composite with high modulus and impact strength were manufactured by combining polyethylene (PE) or polypropylene (PP) with wood fiber (WF) using twin-screw extruder techniques. The advantage of using low melt viscosity polymer matrices is that it enhances the modulus and reduces the overall viscosity of the system. SEM analysis of the composites indicates that the polymer molecules penetrate into the vessels and cracks of the cellulose fiber, which decreases the number of voids and produces a higher density composite with improved mechanical performance. The addition of maleic anhydride-grafted polyolefin as a compatibilizer improves the level of adhesion between the wood fiber and the polyolefin matrix. The impact strength of the composites with compatibilizer is 60% higher than those without. Young's moduli of WF/PE and WF/PP with compatibilizer were 4.4 and 5.4 GPa, respectively, meanwhile the impact strengths of WF/PE and WF/PP were 44 and 24J/m, where the WF content was 50wt%.
Eichhorn, S.J. , Baillie, C.A., Zafeiropoulos , C.A., Mwaikambo, L.Y., Ansell, M.P., Dufresne, A., Entwistle, K.M., Herrera-France, P.J., Escamilla, G.C., Groom, L., Hughes, M., Hill, C., Rials, T.G. and Wild, P.M. (2001). Review: Current International Research Into Cellulosic Fibres and Composites, J. Mater. Sci., 36(9): 2107-2131.
2.
Li, Y., Mai, Y.-W. and Ye, L. (2000). Sisal Fibre and Its Composites: A Review of Recent Developments, Comp. Sci. Tech., 60(11): 2037-2055.
3.
Hornsby, P.R. , Hinrichsen, E. and Tarverdi, K. (1997). Preparation and Properties of Polyethylene Composites Reinforced With Wheat and Flax Straw Fibre: Part II Analysis of Composite Microstructure and Mechanical Properties, J. Mat. Sci., 32(4): 1009-1015.
4.
Karmaker, A.C. and Yooungquist, J.A. (1996). Injection Moulding of Polypropylene Reinforced With Short Jute Fibers, J. Appl. Polym. Sci., 62: 1147-1151.
5.
Gatenholm, P. , Kubat, J. and Mathiasson, A. (1992). Biodegradable Natural Composites: I - Processing and Properties, J. Appl. Polym. Sci., 45: 1667-1677.
6.
Coutinho, F.M.B. and Costa, T.H.S. (1999). Performance of Polypropylene-Wood Fiber Composites, Polymer Testing, 18(8): 581-587.
7.
Balasuriya, P.W., Ye, L. and Mai, Y.-W. (2001). Mechanical Properties of Wood Flake- Polyethylene Composite: Part I Effects of Processing Method and Matrix Melt Flow Behaviour, Composite Part A: Applied Science and Manufacturing, 32(5): 619-629.
8.
Li, T.Q. , Ng, C.N. and Li, R.K.Y. (2001). Impact Behavior of Sawdust/Recycled-PP Composites, Journal of Applied Polymer Science, 81(6): 1420-1428.
9.
Raj, R.G. , Kokta, B.V., Groleau, G. and Daneault, C. (1989). Use of Wood Fiber as a Filler in Polyethylene: Studies on Mechanical Properties, Plast., Rubb. Compos. Process. Appl., 11: 215-221.
10.
Razi, P.S., Raman, A. and Portier, R. (1997). Studies on Mechanical Properties of Wood-Polymer Composites, J. Compos. Mater., 31: 2391-2401.
11.
Maiti, S.N. and Singh, K. (1986). Influence of Wood Flour on the Mechanical Properties of Polyethylene, J. Appl. Polym. Sci., 32: 4285-4289.
12.
Stark, N.M. (1999). Wood Fiber Derived From Scrap Pallets Used in Polypropylene Composites, Forest Prod. J., 49: 39-46.
13.
Wu, J., Yu, D., Chan, C.-M., Kim, J. and Mai, Y.-W. (2000). Effect of Fiber Pretreatment Condition on the Interfacial Strength and Mechanical Properties of Wood Fiber/PP Composites , J. Appl. Polym. Sci., 76(7): 1000-1010.
14.
Balasuriya, P.W. , Ye, L., Mai, Y.-W. and Wu, J. (2002). Mechanical Properties of Wood Flake-Polyethylene Composites: II - Interface Modification, J. Appl. Polym. Sci., 83(12): 2505-2521.
15.
Liao, B., Huang, Y. and Cong, G. (1997). Influence of Modified Wood Fibers on the Mechanical Properties of Wood Fiber-Reinforced Polyethylene, J. Appl. Polym. Sci., 66(8): 1561-1568.
16.
Kazayawoko, M., Balatinecz, J.J. and Matuana, L.M. (1999). Surface Modification and Adhesion Mechanisms in Wood Fiber-Polypropylene Composites, J. Mater. Sci., 34: 6189-6199.
17.
Ichazo, M.N. , Albano, C., Gonzalez, J., Perera, R. and Candal, M.V. (2001). Polypropylene/Wood Flour Composites: Treatments and Properties, Compos. Struct. , 54(2-3): 207-214.
18.
Zhang, F., Endo, T., Qiu, W., Yang, L. and Hirotsu, T. (2002). Preparation and Mechanical Properties of Composite of Fibrous Cellulose and Maleated Polyethylene, J. Appl. Polym. Sci., 84(11): 1971-1980.
19.
Jakab, E., Varhegyi, G. and Faix, O. (2000). Thermal Decomposition of Polypropylene in the Presence of Wood-derived Materials, J. Anal. Appl. Pyrol. , 56: 273-285.
20.
Sawai, D., Nagai, K., Kubota, M., Ohama, T. and Kanamoto, T. (2006). Maximum Tensile Properties of Oriented Polyethylene, Achieved by Uniaxial Drawing of Solution-grown Crystal Mats: Effects of Molecular Weight and Molecular Weight Distribution, J. Polym. Sci. Part B: Polym. Phys.: 44(1): 2006, 153-161.
Lei, Y. , Wu, Q., Clemons, C.M., Yao, F. and Xu, Y. (2007). Influence of Nanoclay on Properties of HDPE/Wood Composites, J. Appl. Polym. Sci. , 106(6): 3958-3966.
23.
Pan, N. , Chen, H.C., Thompson, J., Inglesby, M.K., Khatua, S., Zhang, X.S. and Zeronian, S.H. (1997). The Size Effects on the Mechanical Behaviour of Fibres, J. Mater. Sci., 32(10): 2677-2685.