The study of self-regulating α-TCP based composite by micro/nano scaled silk fibroin and α-CSH on physicochemical and biological properties of bone cement

Abstract

A novel self-hardening α-tricalcium phosphate (α-TCP) bone cement complexed with different content of α-calcium sulfate hemihydrate (α-CSH) and micrometer hydroxyapatite mineralized silk fibroin (HA-SF) using micro/SF as curing liquid has been investigated in this work, which was capable of tunable setting time, degradation, mechanical property and ability to anti-washout. After addition 0 ∼ 25% α-CSH to the α-TCP cement with SFFs as curing liquid, it shortened the setting time of the modified composite to 10 ∼ 30 min. Furthermore, the addition of SFFs improved the compressive strength of the composite from 5.41 MPa to 9.44 MPa. The composites with both Na₂HPO₄ and SFFs as curing liquid showed good anti-collapse performance. The weight loss ratio of bone cement was −0.18 ∼ 12.08% in 4 weeks when the content of α-CSH in α-TCP/α-CSH was between 0 ∼ 25 wt%. During the degradation of α-CSH, the amorphous α-TCP were deposited as hydroxyapatite to formed a plate-like products on the surface of composite. Compared to the composite with Na₂HPO₄ solution as the curing liquid, alkaline phosphatase (ALP) activity of the composites using SFFs as curing liquid were maintained at high levels on the 14th day especially when the Ca/P ratio was 1.7. This study provides a theoretical basis for the regeneration of bone defects guided by bone cement materials.

Graphical Abstract