An injectable chelate-setting hydroxyapatite cement (IP6-HAp), formed by chelate-bonding capability of inositol phosphate (IP6), was developed. The effects of ball-milling duration of starting HAp powder and IP6 concentration on the material properties such as injectability and mechanical strength of the cement were examined. The cement powder was prepared by ball-milling the as-synthesized HAp powder for 5 min using ZrO₂ beads with a diameter of 10 mm, followed by another 60 min with ZrO₂ beads with a diameter of 2 mm, and thereafter surface-modified with 5000 ppm of IP6 solution. Injectable cement was then fabricated with this HAp powder and 2.5 mass% chitosan as a mixing solution, with a setting time of 36.3 ± 4.7 min and a compressive strength of 19.0 ± 2.1 MPa. The IP6-HAp cements prepared with chitosan showed favorable biocompatibility in vitro using an osteoblast cell model, and osteoconductivity in vivo using a pig tibia model.

Keywords

Calcium-phosphate cement hydroxyapatite chitosan biocompatibility osteoconductivity

Get full access to this article

View all access options for this article.

References

LeGeros RZ and LeGeros JP. Dense hydroxyapatite. In: Hench LL, Wilson J (eds) An introduction to bioceramics. Singapore: World Scientific, 1993, pp.139–180.

Akao

Aoki

Kato

. Mechanical properties of sintered hydroxyapatite for prosthetic applications. J Mater Sci 1981; 16: 809–812.

Tamai

Myoui

Tomita

. Novel hydroxyapatite ceramics with an interconnective porous structure exhibit superior osteoconduction in vivo. J Biomed Mater Res 2002; 59: 110–117.

Oonishi

Hench

Wilson

. Comparative bone growth behavior in granules of bioceramic materials of various sizes. J Biomed Mater Res 1999; 44: 31–43.

Chow

. Development of self-setting calcium phosphate cements. J Ceram Soc Jpn 1991; 99: 954–964.

Miyamoto

Ishikawa

Takechi

. Histological and compositional evaluations of three types of calcium phosphate cements when implanted in subcutaneous tissue immediately after mixing. J Biomed Mater Res 1999; 48: 36–42.

Hirabayashi

Hirasawa

Kohno

. Studies on primers combined chelating agent with metallic ion for tooth-bonding I. Effects of primer combined phytic acid and tin(II) fluoride. J Jpn Soc Dent Mater Dev 1993; 12: 435–444.

Jackson

Jones

Linskens

. Phytic acid in pollen. Phytochemistry 1982; 21: 1255–1258.

Martin

Evans

. Phytic acid-metal ion interactions. II. The effect of pH on Ca(II) binding. J Inorg Biochem 1986; 27: 17–30.

10.

Aizawa

Haruta

Okada

. Development of novel cement processing using hydroxyapatite particles modified with inositol phosphate. Arch BioCeram Res 2003; 3: 134–138.

11.

Horiguchi

Yoshikawa

Oribe

. Fabrication of chelate-setting hydroxyapatite cements from four kinds of commercially-available powder with various shape and crystallinity and their mechanical property. J Ceram Soc Jpn 2008; 116: 50–55.

12.

Konishi

Horiguchi

Mizumoto

. Novel chelate-setting calcium-phosphate cements fabricated with wet-synthesized hydroxyapatite powder. J Mater Sci Mater Med 2013; 24: 611–621.

13.

Jensen

Evans

Mathis

. Percutaneous polymethylmethacrylate vertebroplasty in the treatment of osteoporotic vertebral body compression fractures: technical aspects. AJNR Am J Neuroradiol 1997; 18: 1897–1904.

14.

Mosekilde

. Normal vertebral body size and compressive strength: relations to age and to vertebral and iliac trabecular bone compressive strength. Bone 1986; 7: 207–212.

15.

Takechi

Miyamoto

Ishikawa

. Non-decay type fast-setting calcium phosphate cement using chitosan. J Mater Sci Mater Med 1996; 7: 317–322.

16.

Cherng

Takagi

Chow

. Effects of hydroxypropyl methylcellulose and other gelling agents on the handling properties of calcium phosphate cement. J Biomed Mater Res 1997; 35: 273–277.

17.

Konishi

Takahashi

Zhuang

. Biodegradable β-tricalcium phosphate cement with anti-washout property based on chelate-setting mechanism of inositol phosphate. J Mater Sci Mater Med 2013; 24: 1383–1394.

18.

Konishi

Takahashi

Mizumoto

. Effect of the addition of various polysaccharides on the material properties and cytotoxicity of chelate-setting β-tricalcium phosphate cement. Phosphorus Res Bull 2012; 26: 59–64.

19.

Yuasa

Miyamoto

Ishikawa

. In vitro resorption of three apatite cements with osteoclasts. J Biomed Mater Res 2001; 54: 344–350.

20.

Frankenburg

Goldstein

Bauer

. Biomechanical and histological evaluation of a calcium phosphate cement. J Bone Joint Surg Am 1998; 80: 1112–1124.

21.

Yuan

de Bruijn

. Tissue responses of calcium phosphate cement: a study in dogs. Biomaterials 2000; 21: 1283–1290.

22.

Ooms

Wolke

van der Waerden

. Trabecular bone response to injectable calcium phosphate (Ca-P) cement. J Biomed Mater Res 2002; 61: 9–18.

23.

Ishikawa

Asaoka

. Estimation of ideal mechanical strength and critical porosity of calcium phosphate cement. J Biomed Mater Res 1995; 29: 1537–1543.

Supplementary Material

Please find the following supplemental material available below.

For Open Access articles published under a Creative Commons License, all supplemental material carries the same license as the article it is associated with.

For non-Open Access articles published, all supplemental material carries a non-exclusive license, and permission requests for re-use of supplemental material or any part of supplemental material shall be sent directly to the copyright owner as specified in the copyright notice associated with the article.

0.00 MB

0.24 MB

Injectable chelate-setting hydroxyapatite cement prepared by using chitosan solution: Fabrication,material properties,biocompatibility,and osteoconductivity

Abstract

Keywords

Get full access to this article

References

Supplementary Material