A novel superhydrophilic hybrid scaffold was created by electrospinning a mixture of poly(l-lactic acid-co-ε-caprolactone) and formulated fibrinogen. The hybrid scaffolds possess the combined benefits of each individual component, such as moderate mechanical strength and excellent biocompatibility. In vitro studies also revealed that endothelial cells seeded on the hybrid scaffolds achieved a relatively high level of cell attachment after three days of culture and a significant increase in the proliferation rate after seven days of culture, compared with pure fibrinogen or poly(l-lactic acid-co-ε-caprolactone) scaffolds. A comparative study of hybrid and pure poly(l-lactic acid-co-ε-caprolactone) patches was performed in an abdominal wall defect model in rats. In both groups, implants degraded by six months, but muscle reconstruction was only observed in the hybrid patch group.
FortelnyRHPetter-PuchnerAHGlaserKS. Adverse effects of polyvinylidene fluoride-coated polypropylene mesh used for laparoscopic intraaperitoneal onlay repair of incisional hernia. Br J Surg2010; 97: 1140–1145.
3.
BraccoPBrunellaVTrossarelliL. Comparison of polypropylene and polyethylene terephthalate (Dacro) meshes for abdominal wall hernia repair: a chemical and morphological study. Hernia2005; 9: 51–55.
4.
OhDSManningMMEmmanuelJ. Repair of full-thickness defects in alimentary tract wall with patches of expanded polyterafluoroethylene. Ann Surg2002; 235: 708–711.
5.
CandageRJonesKLuchetteFA. Use of human acellular dermal matrix for hernia repair. Friend or foe?Surgery2008; 144: 703–709.
6.
SriussadapornSkritayakiranaKPak-artR. Operative management of small bowel fistulae associated with open abdomen. Asian J Surg2006; 29: 1–7.
7.
O'DwyerPJKingsnorthANMolloyRG. Randomized clinical trial assessing impact of a lightweight or heavyweight mesh on chronic pain after inguinal hernia repair. Br J Surg2005; 92: 166–170.
8.
JerniganTWFabianTCCroceMA. Staged management of giant abdominal wall defects: acute and long-term results. Ann Surg2003; 238: 349–355.
9.
WyheDSchmitzIBelyaevO. Experimental comparison of monofile light and heavy polypropylene meshes: less weight does not mean less biological response. World J Surg2006; 30: 1586–1591.
10.
EberliDRodriguezSAtalaA. In vivo evaluation of acellular human dermis for abdominal wall repair. J Biomed Mater Res A2010; 93: 1527–1538.
KarpelowskyJSThomasGShunA. Definitive abdominal wall closure using a porcine intestinal submucosa biodegradable membrane in pediatric transplantation. Pediatr Transplant2009; 13: 285–289.
14.
MoXMXuCYKotakiM. Electrospun P(LLA-CL) nanofiber: a biomimetic extracellular matrix for smooth muscle cell and endothelial cell proliferation. Biomaterials2004; 25: 1883–1890.
15.
NotteletBPektokEMandracchiaD. Factorial design optimization and in vivo feasibility of poly(ε-caprolactone)-micro- and nanofiber-based small diameter vascular grafts. J Biomed Mater Res2009; 89: 865–875.
16.
VaquetteCKahnCFrochotC. Aligned poly(L-lactic-co-e-caprolactone) electrospun microfibers and knitted structure: a novel composite scaffold for ligament tissue engineering. J Biomed Mater Res2010; 94: 1270–1282.
17.
PrabhakaranMPVenugopalJRRamakrishnaS. Mesenchymal stem cell differentiation to neuronal cells on electrospun nanofibrous substrates for nerve tissue engineering. Biomaterials2009; 30: 4996–5003.
18.
HeWMaZTeoWE. Tubular nanofiber scaffolds for tissue engineered small-diameter vascular grafts. J Biomed Mater Res2009; 90: 205–216.
19.
LimJIYuBLeeYK. Fabrication of collagen hybridized elastic PL-CL for tissue engineering. Biotechnol Lett2008; 30: 2085–2090.
20.
HeWMaZWYongT. Fabrication of collagen-coated biodegradable polymer nanofiber mesh and its potential for endothelial cells growth. Biomaterials2005; 26: 7606–7615.
21.
ZhangKHWangHSHuangC. Fabrication of silk fibroin blended P(LLA-CL) nanofibrous scaffolds for tissue engineering. J Biomed Mater Res2010; 93A: 984–993.
22.
LeeJTaeGKimYH. The effect of gelatin incorporation into electrospun poly(L-lactide-co-ε-caprolactone) fibers on mechanical properties and cytocompatibility. Biomaterials2008; 29: 1872–1879.
23.
AnantaMAulinCEHilbornJ. A poly(lactic acid-co-caprolactone)-collagen hybrid for tissue engineering applications. Tissue Eng Part A2009; 15: 1667–1675.
HeWYongTTeoWE. Fabrication and endothelialization of collagen-blended biodegradable polymer nanofibers: potential vascular graft for blood vessel tissue engineering. Tissue Eng2005; 11: 1574–1588.
26.
HeCXuXZhangF. Fabrication of fibrinogen/P(LLA-Cl) hybrid nanofibrous scaffold for potential soft tissue engineering applications. J Biomed Mat Res2011; 97: 339–347.
27.
SpotnitzWDBurksS. Hemostats, sealants, and adhesives: components of the surgical toolbox. Transfusion2008; 48: 1502–1516.
28.
AchneckHESileshiBJamiolkowskiRM. A comprehensive review of topical hemostatic agents: efficacy and recommendations for use. Ann Surg2010; 251: 217–228.
29.
ElvinCMBrownleeAGHusonMG. The development of photochemically crosslinked native fibrinogen as a rapidly formed and mechanically strong surgical tissue sealant. Biomaterials2009; 30: 2059–2065.
30.
LinnesMPRatnerBDGiachelliCM. A fibrinogen-based precision microporous scaffold for tissue engineering. Biomaterials2007; 28: 5298–5306.
31.
DainiakMBAllanIUSavinaIN. Gelatin–fibrinogen cryogel dermal matrices for wound repair: preparation, optimisation and in vitro study. Biomaterials2010; 31: 67–76.
32.
LaiPHChangYLiangHC. Peritoneal regeneration induced by an acellular bovine pericardial patch in the repair of abdominal wall defects. J Surg Res2005; 127: 85–92.
33.
Turner N and Badylak S. Biologic scaffolds for musculotendinous tissue repair. Eur Cell Mater 2013; 25: 130–143.
34.
SwartzDDRussellJAAndreadisST. Engineering of fibrin-based functional and implantable small-diameter blood vessels. Am J Physiol Heart Circ Physiol2005; 288: 1451–1460.