Pluronic® F127 is a biocompatible, injectable, and thermoresponsive polymer with promising biomedical applications. In this study, a chemically modified form, i.e., Pluronic ALA-L with tailored degradation rate, was tested as an encapsulation vehicle for osteoblastic cells. UV cross-linking of the modified polymer results in a stable hydrogel with a slower degradation rate. Toxicological screening showed no adverse effects of the modified Pluronic ALA-L on the cell viability. Moreover, high viability of embedded cells in the cross-linked Pluronic ALA-L was observed with life/death fluorescent staining during a 7-day-culture period. Cells were also cultured on macroporous, cross-linked gelatin microbeads, called CultiSpher-S® carriers, and encapsulated into the modified cross-linked hydrogel. Also, in this situation, good cell proliferation and migration could be observed in vitro. Preliminary in vivo tests have shown the formation of new bone starting from the injected pre-loaded CultiSpher-S® carriers.
WeinandCPomerantsevaINevilleCMGuptaRWeinbergEMadischI. Hydrogel-beta-TCP scaffolds and stem cells for tissue engineering bone. Bone2006; 38: 555–563.
2.
VertentenGLippensEGironèsJGorskiTDeclercqHSaundersJ. Evaluation of an injectable, photopolymerizable, and three-dimensional scaffold based on methacrylate-endcapped poly(D,L-lactide-co-epsilon-caprolactone) combined with autologous mesenchymal stem cells in a goat tibial unicortical defect model. Tissue Eng Part A2009; 15: 1501–1511.
3.
DeclercqHAGorskiTLTielensSPSchachtEHCornelissenMJ. Encapsulation of osteoblast seeded microcarriers into injectable, photopolymerizable three-dimensional scaffolds based on D,L-lactide and epsilon-caprolactone. Biomacromolecules2005; 6: 1608–1614.
Ruel-GariepyELerouxJC. In situ-forming hydrogels - review of temperature-sensitive systems. Eur J Pharm Biopharm2004; 58: 409–426.
10.
DumortierGGrossiordJLAgnelyFChaumeilJC. A review of poloxamer 407 pharmaceutical and pharmacological characteristics. Pharm Res2006; 23: 2709–2728.
11.
YeFBYaghmurAJensenHLarsenSWLarsenCOstergaardJ. Real-time UV imaging of drug diffusion and release from Pluronic F127 hydrogels. Eur J Pharm Sci2011; 43: 236–243.
12.
KhattakSFBhatiaSRRobertsSC. Pluronic F127 as a cell encapsulation material: utilization of membrane-stabilizing agents. Tissue Eng2005; 11: 974–983.
13.
Escobar-ChavezJJLopez-CervantesMNaikAKaliaYNQuintanar-GuerreroDGanem-QuintanarA. Applications of thermoreversible Pluronic F-127 gels in pharmaceutical formulations. J Pharm Pharm Sci2006; 9: 339–358.
14.
SahuAKasojuNGoswamiPBoraU. Encapsulation of curcumin in Pluronic block copolymer micelles for drug delivery applications. J Biomater Appl2011; 25: 619–639.
15.
SwennenIVermeerschVHornofMAdriaensERemonJ-PUrttiA. In-situ crosslinkable thermo-responsive hydrogels for drug delivery. J Controlled Rel2006; 116: e21–e24.
16.
ClokieCMLMoghadamHJacksonMTSandorGKB. Closure of critical sized defects with allogenic and alloplastic bone substitutes. J Craniofac Surg2002; 13: 111–121.
17.
FowlerEBCueninMFHokettSDPeacockMEMcPhersonJCIIIDirksenTR. Evaluation of Pluronic polyols as carriers for grafting materials: study in rat calvaria defects. J Periodontol2002; 73: 191–197.
18.
MylonasDVidalMDDe KokIJMoriarityJDCooperLF. Investigation of a thermoplastic polymeric carrier for bone tissue engineering using allogeneic mesenchymal stem cells in granular scaffolds. J Prosthodont2007; 16: 421–430.
19.
ZhouAJPeelSAClokieCM. An evaluation of hydroxyapatite and biphasic calcium phosphate in combination with Pluronic F127 and BMP on bone repair. J Craniofac Surg2007; 18: 1264–1275.
20.
Arevalo-SilvaCAEaveyRDCaoYVacantiMWengYVacantiCA. Internal support of tissue-engineered cartilage. Arch Otolaryngol Head Neck Surg2000; 126: 1448–1452.
21.
RuszymahBHChuaKLatifMAHusseinFNSaimAB. Formation of in vivo tissue engineered human hyaline cartilage in the shape of a trachea with internal support. Int J Pediatr Otorhinolaryngol2005; 69: 1489–1495.
22.
WengYCaoYSilvaCAVacantiMPVacantiCA. Tissue-engineered composites of bone and cartilage for mandible condylar reconstruction. J Oral Maxillofac Surg2001; 59: 185–190.
LeeSYTaeG. Formulation and in vitro characterization of an in situ gelable, photo-polymerizable Pluronic hydrogel suitable for injection. J Controlled Rel2007; 119: 313–319.
25.
CellesiFTirelliNHubbellJA. Materials for cell encapsulation via a new tandem approach combining reverse thermal gelation and covalent crosslinking. Macromol Chemis Phys2002; 203: 1466–1472.
26.
SosnikACohnD. Ethoxysilane-capped PEO-PPO-PEO triblocks: a new family of reverse thereto-responsive polymers. Biomaterials2004; 25: 2851–2858.
27.
LeeJBYoonJJLeeDSParkTG. Photo-crosslinkable, thermo-sensitive and biodegradable Pluronic hydrogels for sustained release of protein. J Biomater Sci, Polymer Ed2004; 15: 1571–1583.
28.
TielensSDeclercqHGorskiTLippensESchachtECornelissenM. Gelatin-based microcarriers as embryonic stem cell delivery system in bone tissue engineering: an in-vitro study. Biomacromolecules2007; 8: 825–832.
29.
HussFRMJunkerJPEJohnsonHKratzG. Macroporous gelatine spheres as culture substrate, transplantation vehicle, and biodegradable scaffold for guided regeneration of soft tissues. In vivo study in nude mice. J Plast Reconstr Aesthetic Surg2007; 60: 543–555.
30.
YangYRossiFMVPutninsEE. Ex vivo expansion of rat bone marrow mesenchymal stromal cells on microcarrier beads in spin culture. Biomaterials2007; 28: 3110–3120.