In this report, poly(L-lactide-co-ε-caprolactone), poly(LLA-co-CL) and poly(L-lactide-co-1,5-dioxepan-2-one), poly(LLA-co-DXO) were evaluated and compared for potential use in bone tissue engineering constructs together with bone marrow stromal cells (BMSC). The copolymers were tailored to reduce the level of harmful tin residuals in the scaffolding. BMSC isolated from Sprague—Dawley rats were seeded onto the scaffolds and cultured in vitro for up to 21 days. Cell spreading and proliferation was analyzed after 72 h by scanning electron microscopy and thiazolyl blue tetrazolium bromide (MTT) conversion assay. Osteogenic differentiation of BMSC was evaluated by real-time PCR after 14 and 21 days of culture. Hydrophilicity was significantly different between poly(LLA-co-CL) and poly(LLA-co-DXO) with the latter being more hydrophilic. After 72 h, both scaffolds supported increased cell proliferation and the mRNA expression of osteocalcin and osteopontin was significantly increased after 21 days. Further investigation of these constructs, with lower levels of tin residuals, are being pursued.
Langer, R. and Vacanti, J.P. ( 1993). Tissue Engineering, Science, 260(5110): 920-926.
2.
Zhou, Y., Chen, F., Ho, S.T., Woodruff, M.A., Lim, T.M. and Hutmacher, D.W. ( 2007). Combined Marrow Stromal Cell-sheet Techniques and High-strength Biodegradable Composite Scaffolds for Engineered Functional Bone Grafts, Biomaterials, 28(5): 814-824.
3.
Hutmacher, D.W. , Schantz, J.T., Lam, C.X., Tan, K.C. and Lim, T.C. (2007). State of the Art and Future Directions of Scaffold-based Bone Engineering from a Biomaterials Perspective , J. Tissue Eng. Regen. Med., 1(4): 245-260.
4.
Pittenger, M.F. , Mackay, A.M., Beck, S.C., Jaiswal, R.K., Douglas, R., Mosca J.D. et al. (1999). Multilineage Potential of Adult Human Mesenchymal Stem Cells, Science, 284(5411): 143-147.
5.
Ishaug, S.L. , Crane, G.M., Miller, M.J., Yasko, A.W., Yaszemski, M.J. and Mikos, A.G. (1997). Bone Formation by Three-dimensional Stromal Osteoblast Culture in Biodegradable Polymer Scaffolds, J. Biomed. Mater. Res., 36(1): 17-28.
6.
Martin, I., Shastri, V.P., Padera, R.F., Yang, J., Mackay, A.J., Langer, R. et al. (2001). Selective Differentiation of Mammalian Bone Marrow Stromal Cells Cultured on Three-dimensional Polymer Foams, J. Biomed. Mater. Res., 55(2): 229-235.
7.
Lowry, K.J., Hamson, K.R., Bear, L., Peng, Y.B., Calaluce, R., Evans, M.L. et al. (1997). Polycaprolactone/Glass Bioabsorbable Implant in a Rabbit Humerus Fracture Model, J. Biomed. Mater. Res. , 36(4): 536-541.
8.
Matsusue, Y. , Yamamuro, T., Oka, M., Shikinami, Y., Hyon, S.H. and Ikada, Y. (1992). In Vitro and In Vivo Studies on Bioabsorbable Ultra-high-strength Poly(L-lactide) rods, J. Biomed. Mater. Res., 26(12): 1553-1567.
9.
Agrawal, C.M. and Ray, R.B. (2001). Biodegradable Polymeric Scaffolds for Musculoskeletal Tissue Engineering, J. Biomed. Mater. Res., 55(2): 141-150.
10.
Kyriakidou, K., Lucarini, G., Zizzi, A., Salvolini, E., Mattioli-Belmonte , M., Mollica, F. et al. (2008). Dynamic Co-seeding of Osteoblast and Endothelial Cells on 3D Polycaprolactone Scaffolds for Enhanced Bone Tissue Engineering, J. Bioact. Compat. Polym., 23(3): 227-243.
11.
Hakkarainen, M., Hoglund, A., Odelius, K. and Albertsson, A.C. (2007). Tuning the Release Rate of Acidic Degradation Products through Macromolecular Design of Caprolactone-based Copolymers, J. Am. Chem. Soc., 129(19): 6308-6312.
12.
Hoglund, A. , Odelius, K., Hakkarainen, M. and Albertsson, A.C. (2007). Controllable Degradation Product Migration from Cross-linked Biomedical Polyester-ethers through Predetermined Alterations in Copolymer Composition, Biomacromolecules, 8(6): 2025-2032.
13.
Kallrot, M., Edlund, U. and Albertsson, A.C. ( 2007). Covalent Grafting of Poly(L-lactide) to Tune the In Vitro Degradation Rate, Biomacromolecules, 8(8): 2492-2496.
14.
Odelius, K., Plikk, P. and Albertsson, A.C. ( 2005). Elastomeric Hydrolyzable Porous Scaffolds: Copolymers of Aliphatic Polyesters and a Polyether-ester, Biomacromolecules , 6(5): 2718-2725.
15.
Hu, K., Lv, Q., Cui, F.Z., Xu, L., Jiao, Y.P., Wang, Y. et al. (2007). A Novel Poly(L-lactide) (PLLA)/Fibroin Hybrid Scaffold to Promote Hepatocyte Viability and Decrease Macrophage Responses , J. Bioact. Compat. Polym., 22: 395-410.
16.
Middleton, J.C. and Tipton, A.J. (2000). Synthetic Biodegradable Polymers as Orthopedic Devices, Biomaterials, 21(23): 2335-2346.
17.
Albertsson, A.C. and Varma, I.K. (2003). Recent Developments in Ring Opening Polymerization of Lactones for Biomedical Applications, Biomacromolecules, 4(6): 1466-1486.
18.
Tanzi, M.C. , Verderio, P., Lampugnani, M.G., Resnati, M., Dejana, E. and Sturani, E. (1994). Cytotoxicity of Some Catalysts Commonly Used in the Synthesis of Copolymers for Biomedical Use , J. Mater. Sci.: Mater. Med., 5(6-7): 393-396.
19.
McLean, J.R., Blakey, D.H., Douglas, G.R. and Kaplan, J.G. (1983). The Effect of Stannous and Stannic (Tin) Chloride on DNA in Chinese Hamster Ovary Cells, Mutat. Res., 119(2): 195-201.
20.
Dantas, F.J. , de Mattos, J.C., Moraes, M.O., Viana, M.E., Lage, C.A., Cabral-Neto, J.B. et al. (2002). Genotoxic Effects of Stannous Chloride (SnCl2) in K562 Cell Line, Food Chem. Toxicol., 40(10): 1493-1498.
21.
Li, H., Zheng, Q., Xiao, Y., Feng, J., Shi, Z. and Pan, Z. ( 2009). Rat Cartilage Repair Using Nanophase PLGA/HA Composite and Mesenchymal Stem Cells, J. Bioact. Compat. Polym., 24: 83-99.
22.
Lee, J. , Cuddihy, M.J. and Kotov, N.A. (2008). Three-dimensional Cell Culture Matrices: State of the Art, Tissue Eng. Part B: Reviews , 14(1): 61-86.
23.
Karageorgiou, V. and Kaplan, D. (2005). Porosity of 3D Biomaterial Scaffolds and Osteogenesis, Biomaterials, 26(27): 5474-5491.
24.
Lu, L., Peter, S.J., Lyman, M.D., Lai, H.L., Leite, S.M., Tamada, J.A. et al. (2000). In Vitro and In Vivo Degradation of Porous Poly(DL-Lactic-co-Glycolic Acid) Foams, Biomaterials, 21(18): 1837-1845.
25.
Mikos, A.G. , Thorsen, A.J., Czerwonka, L.A., Bao, Y., Langer, R., Winslow, D.N. et al. (1994). Preparation and Characterization of Poly(L-Lactic Acid) Foams, Polymer , 35(5): 1068-1077.
26.
Koç, A., Emin, N., Elçin, A.E. and Elçin , Y.M. (2008). In Vitro Osteogenic Differentiation of Rat Mesenchymal Stem Cells in a Microgravity Bioreactor, J. Bioact. Compat. Polym., 23(3): 244-261.
27.
Kokubo, S., Nozaki, K., Fukushima, S., Takahashi, K., Miyata, K. and Yokota, S. ( 2008). Recombinant Human Bone Morphogenetic Protein-2 as an Osteoinductive Biomaterial and a Biodegrdable Carrier in a Rabbit Ulnar Defect Model, J. Bioact. Compat. Polym., 23(4): 348-366.
28.
Idris, S., Arvidson, K., Plikk, P., Ibrahim, S., Finne-Wistrand, A., Albertsson, A.-C. et al. (2010). Polyester Copolymer Scaffolds Enhance Expression of Bone Markers in Osteoblast-like Cells, J. Biomed. Mat. Res., Part A (In press).
29.
Mathisen, T. and Albertsson, A.C. ( 1989). Polymerization of 1,5-Dioxepan-2-one. 1. Synthesis and Characterization of the Monomer 1,5-Dioxepan-2-one and Its Cyclic Dimer 1,5,8,12-Tetraoxacyclotertradecane-2,9-one , Macromolecules, 22(10): 3838-3842.
30.
Odelius, K., Plikk, P. and Albertsson, A.C. ( 2008). The Influence of Composition of Porous Copolyester Scaffolds on Reactions Induced by Irradiation Sterilization, Biomaterials , 29(2): 129-140.
31.
Plikk, P., Odelius, K., Hakkarainen, M. and Albertsson, A.C. ( 2006). Finalizing the Properties of Porous Scaffolds of Aliphatic Polyesters through Radiation Sterilization, Biomaterials, 27(31): 5335-5347.
32.
Maniatopoulos, C., Sodek, J. and Melcher, A.H. (1988). Bone Formation In Vitro by Stromal Cells Obtained from Bone Marrow of Young Adult Rats, Cell Tissue Res., 254(2): 317-330.
33.
Stjerndahl, A., Finne-Wistrand , A., Albertsson, A.C., Bäckesjö, C.M. and Lindgren, U. ( 2008). Minimization of Residual Tin in the Controlled Sn(II)Octoate-catalyzed Polymerization of Epsilon-caprolactone, J. Biomed. Mater. Res., Part A, 87(4): 1087-1091.
34.
Albertsson, A.C. and Löfgren , A. (1995). Synthesis and Characterization of Poly(1,5-Dioxpan-2-one-co-L-Lactic acid) and Poly(1,5-Dioxepan-2-one-co-D, L-Lactic acid), J. Macromol. Sci., Part A: Pure Appl. Chem., A32(1): 41-59.
35.
Kircheldorf, H.R., Jonté , J.M. and Berl, M. (1985). Polylactones 3 Copolymerization of Glycolide with L,L-Lactide and other Lactones , Macromol. Chem. Phys. Suppl., 12(S19851): 25-38.
36.
Curran, J.M. , Chen, R. and Hunt, J.A. (2006). The Guidance of Human Mesenchymal Stem Cell Differentiation In Vitro by Controlled Modifications to the Cell Substrate, Biomaterials, 27(27): 4783-4793.
37.
Aubin, J.E. , Liu, F., Malaval, L. and Gupta, A.K. (1995). Osteoblast and Chondroblast Differentiation, Bone, 17(2 Suppl): 77S-83S.
38.
Frank, O., Heim, M., Jakob, M., Barbero, A., Schafer, D., Bendik, I. et al. (2002). Real-time Quantitative RT-PCR Analysis of Human Bone Marrow Stromal Cells during Osteogenic Differentiation In Vitro , J. Cell. Biochem., 85(4): 737-746.
39.
Fu, H., Doll, B., McNelis, T. and Hollinger, J.O. ( 2007). Osteoblast Differentiation In Vitro and In Vivo Promoted by Osterix, J. Biomed. Mater. Res., Part A, 83(3): 770-778.