This study investigated the fire risk properties of cypress wood for the construction of interiors, especially focusing on heat and smoke hazard properties in fire scenarios. Fire risk characteristics were measured using a cone calorimeter (ISO 5660-1). The external heat flux was maintained at 50 kW/m2. The flame retardants used were metal oxide and metal silicate; they were mixed with a water glass solution. Flame retardants and the silicon compound were dispersed in a concentration of 20 wt% versus 80 wt%, respectively, during 24 h using a magnetic stirrer. The fire performance indexes of the specimens increased by 3–16 times, compared with uncoated specimen and the fire growth index of the specimens increased by 70%–92%. The smoke performance index of the specimens increased by 9–66 times, compared with uncoated specimens. The smoke risk as shown by the smoke performance index increased in the following order: SnO < mica < Co3O4 < ZrSiO4 < cypress. The smoke growth index decreased from 93% to 98%, compared with uncoated wood. The smoke risk due to smoke growth index increased in the following order: SnO < mica < ZrSiO4≈ Co3O4 < cypress. The smoke intensity decreased from a minimum of 85% to a maximum of 99%, compared with uncoated wood. The concentration of CO gas generated after combustion was decreased by 24%–67%. They increased in the following order: mica ≈ ZrSiO4 < SnO < Co3O4 < cypress. A comprehensive assessment of fire performance shows that flame retardants decreased heat hazards, smoke hazards, and CO toxicity.
XiaoZXieYMaiC. The fungal resistance of wood modified with glutaraldehyde. Holzforschung2012; 66: 237–243.
2.
XieYKrauseAMaiC, et al. Weathering of wood modified with the N-methylol compound 1,3-dimethylol-4,5-dihydroxyethyleneurea. Polym Degrad Stabil2005; 89: 189–199.
3.
OberleyWJ. Compositions for imparting fire retardance to wood. US4010296A patent, USA, 2011.
4.
HoracekHGrabnerR. Advantages of flame retardants based on nitrogen compounds. Polym Degrad Stabil1996; 54: 205–215.
5.
LeeCHLeeCWKimJW, et al. Organic phosphorus-nitrogen compounds, manufacturing method and compositions of flame retardants containing organic phosphorus nitrogen compounds. 2011-0034978, Korean Patent, 2011.
6.
GilmanJWKashiwagiTHarrisR, et al. Char enhancing approaches to flame retarding polymers. In: Al-MalaikaSGolovoyAWilkieCA (eds) Chemistry and technology of polymer additives. Malden, MA: Blackwell Science, 1999, p. 135.
TyanHLLeuCMWeiKH. Effect of reactivity of organics-modified montmorillonite on the thermal and mechanical properties of montmorillonite/polyimide nanocomposites. Chem Mater2001; 13: 222–226.
MahltigBHaufeHBottcherH. Functionalization of textiles by inorganic sol-gel coatings. J Mater Chem2005; 15: 4385–4398.
11.
SchmidtH. Considerations about the sol-gel process:from the classical sol-gel route to advanced chemical nanotechnologies. J Sol-Gel Sci Tech2006; 40:115–130.
12.
SharmaNVermaCChariarV, et al. Eco-friendly flame-retardant treatments for cellulosic green building materials. Indoor Built Environ2015; 24: 422–432.
13.
BaerDBurrowsPEl-AzabA. Enhancing coating functionality using nanoscience and nanotechnology. Prog Org Coatings2003; 47: 342–356.
14.
TshabalalaMAKingshottPVan LandinghamMR, et al. Surface chemistry and moisture sorption properties of wood coated with multifunctional alkoxysilanes by sol-gel process. J Appl Polym Sci2003; 88: 2828–2841.
15.
HshiehFY. Shielding effects of silica-ash layer on the combustion of silicones and their possible applications on the fire retardancy of organic polymers. Fire Mater1998; 22: 69–76.
16.
FergeTMaguhnJHafnerK, et al. On-line analysis of gas-phase composition in the combustion chamber and particle emission characteristics during combustion of wood and waste in a small batch reactor. Environ Sci Tech2005; 39: 1393–1402.
17.
DelichatsiosMA. Smoke yields from turbulent buoyant jet flames. Fire Safety J1993; 20: 299–311.
18.
NewmanJSSteciakJ. Characterization of particulates from diffusion flames. Combust Flame1987; 67: 54–67
19.
ISO 5660-1: 2015. Reaction-to-fire tests-heat release, smoke production and mass loss rate-part 1: heat release rate (cone calorimeter method) and smoke production rate (dynamic measurement).
20.
TawiahBYuBYuenRKK, et al. Highly efficient flame retardant and smoke suppression mechanism of boron modified graphene oxide/poly(lactic acid) nanocomposites. Carbon2019; 150: 8–20.
21.
YanLXuZDengN. Effects of polyethylene glycol borate on the flame retardancy and smoke suppression properties of transparent fire-retardant coatings applied on wood substrates. Prog Org Coatings2019; 135: 123–134.
22.
BabrauskasV. The cone calorimeter—a versatile bench-scale tool for the evaluation for fire properties. In: GraysonSJSmithDA (eds) New technology to reduce fire losses and costs. London: Elsevier, 1986, pp. 78–87.
23.
HirschlerMM. Fire performance of organic polymers, thermal decomposition and chemical composition. ACS Symp Series2001; 797: 293–306.
24.
ChungYJJinE. Smoke generation by burning test of cypress plates treated with boron compounds. Appl Chem Eng2018; 29: 670–676.
25.
SimpsonWT. Drying and control of moisture content and dimensional changes. In: BergmanR (ed.) Wood handbook-wood as an engineering material. Wisconsin, USA: US Department of Agriculture, Forest Products Laboratory, 2010, pp. 13.1–13.20.
26.
FangSHuYSongL, et al. Mechanical properties, fire performance and thermal stability of magnesium hydroxide sulfate hydrate whiskers flame retardant silicon rubber. J Mater Sci2008; 43: 1057–1062.
27.
HirschlerMM. Poly(vinyl chloride) and its fire properties. Fire Mater2017; 41: 993–1006.
28.
WangBTangQHongN, et al. Effect of cellulose acetate butyrate microencapsulated ammonium polyphosphate on the flame retardancy, mechanical, electrical, and thermal properties of intumescent flame-retardant ethylene-vinyl acetate copolymer/microencapsulated ammonium poly phosphate/polyamide-6 blends. ACS Appl Mater Interf2011; 3: 3754–3761.
29.
JiaoCChenXZhangJ. Synergistic effects of Fe2O3 with layered double hydroxides in EVA/LDH composites. J Fire Sci2009; 27: 465–479.
30.
SacristánMHullTRStecAA, et al. Cone calorimetry studies of fire retardant soybean-oil-based copolymers containing silicon or boron: comparison of additive and reactive approaches. Poly Degrad Stabil2010; 95: 1269–1274.
31.
BermejoJSRoviraLGFernandezR. Fire-retardant performance of intumescent coatings using halloysites as a novel fire-retardant additive. Jacobs J Nanomed Nanotechnol2015; 1: 1–9.
32.
PearceFMKhannaYPRaucherD. Chapter 8 Thermal analysis in polymer flammability. In: TuriEA (ed.) Thermal characterization of polymeric materials. Elsevier: New York, 1981, pp. 793–843.
WangQLiJWinadyJE. Chemical mechanism of fire retardance of boric acid on wood. Wood Sci Technol2004; 38: 375–389.
35.
SpearpointMJQuintiereGJ. Predicting the burning of wood using an integral model. Combust Flame2000; 123: 308–325.
36.
HagenMHereidJDelichtsiosMA, et al. Flammability assessment of fire-retarded nordic spruce wood using thermogravimetric analyses and cone calorimetry. Fire Safety J2009; 44: 1053–1069.
37.
MourituzAPMathysZGibsonAG. Heat release of polymer composites in fire. Compos Part A: Appl Sci Manuf2005; 37: 1040–1054.
38.
OSHA. Air contaminants; Fire rule. Federal Register1989; 54: 2331–2983.
39.
MSHA. Mine rescue team training metal and nonmetal. Virginia, USA: US Department Labor, Mine Safety and Health Administration, 2008, pp. 1–364.