A two-component polyurea elastomer is evaluated for fire retardancy using the cone calorimeter and thermal analysis. The content of the fire retardant, aluminum diethylphosphinate, the thickness, and heat flux were varied. Thicker samples (12 mm) containing about 3% phosphorus (~15% aluminum diethylphosphinate) seem to be the best.
CostacheMCKanughEMWilkieCA. Fire retardancy of polyureas. J Fire Sci2006; 24: 433.
2.
AwadWHNyamboCKimS. Development of polyurea nanocomposites with improved fire retardancy. In: ACS symposium series 1013 (eds WilkieCAMorganABNelsonGL), 2009, p. 102. chapter 8
3.
AwadWHWilkieCA. Investigation of the thermal degradation of polyurea: The effect of ammonium polyphosphate and expandable graphite. Polymer2010; 51: 2277.
4.
BabrauskasVPracockRD. Heat release rate: The single most important variables in fire hazard. Fire Safety J1992; 18: 255.
5.
ASTM E 1354-04a. Standard test method for heat and visible smoke release rates for materials and products using an oxygen consumption calorimeter, Philadelphia, PA.
6.
GrandAFWilkieCA. Fire retardancy of polymeric materials. New York: Marcel Dekker, 2000.
7.
SchartelBBartholmaiMKnollU. Some comments on the use of cone calorimeter data. Polym Degrad Stabil2005; 88: 540.
8.
AwadWHWilkieCA. Further study on the flammability of polyurea: The effect of intumescent coating and additive flame retardants. Polym Adv Technol2011; 22: 1297.