Flammability and Thermal Properties of a Novel Intumescent Flame Retardant Polypropylene

Abstract

A novel intumescent flame retardant system (IFRs) combines Tri (1-oxo-2,6,7-trioxa-1-phosphabicyclo [2. 2. 2] octane-methyl) phosphate (TPMP) with melamine pyrophosphate (MPOP) and its application in polypropylene (PP) has been investigated. The thermal stability, flammability, and water resistance were studied by thermogravimetric analysis (TGA), UL-94 test, and cone calorimetry. TGA shows that pure PP degrades at about 4008C, while sample PP-6 degrades at about 270°C under nitrogen atmosphere. With 30wt% total loading of the IFRs, sample PP-6 passes the UL-94 V-0 test. It can still pass the UL-94 V-0 test after the water treatment. The introduction of TPMP and MPOP strongly decreases the peak heat release rate (PHRR) value of the flame retardant (FR) PP composite. The morphologies of the char residues obtained after cone calorimetry were investigated by means of scanning electron microscopy (SEM). The char residue of sample PP-6 has better structure, which prevents the underlying materials from further decomposing. X-ray photoelectron spectroscopy (XPS) was used to further explore the char residues of the FR PP composites. The results show that sample PP-6 has the best char residue, which enhances the oxidation resistance of the char layer.

Keywords

intumescent flame retardant thermal degradation cone calorimetry water resistance.

Get full access to this article

View all access options for this article.

References

Balabanovich, A.I. (2005). Thermal Decomposition Study of Intumescent Additives: Pentaerythritol Phosphate and its Blend with Melamine Phosphate , Thermochimica Acta, 435: 188-196.

Camino, G. and Delobel, R. (2000). In: Grand, A.F. and Wilkie, C.A. (eds), Fire Retardancy of Polymeric Materials, pp. 217-243, Marcel Dekker , New York.

Almeras, X. , Le Bras, M. , Poutch, F. , Bourbigot, S. , Marosi, G. and Anna, P. (2003). Effect of Fillers on Fire Retardancy of Intumescent Polypropylene Blends , Macromolecular Symposia, 198: 435-447.

Almeras, X. , Le Bras, M. , Hornsby, P. , Bourbigot, S. , Marosi, G. , Keszei, S. and Poutch, F. (2003). Effect of Fillers on the Fire Retardancy of Intumescent Polypropylene Compounds , Polymer Degradation and Stability , 82: 325-331.

Wu, K. , Wang, Z. and Liang, H. (2008). Microencapsulation of Ammonium Polyphosphate: Preparation, Characterization, and Its Flame Retardance in Polypropylene , Polymer Composites, 29: 860-866.

Le Bras, M. , Bourbigot, S. , Delporate, C. , Siat, C. and Le Tallec1, Y. (1996). New Intumescent Formulations of Fire-retardant Polypropylene- Discussion of the Free Radical Mechanism of the Formation of Carbonaceous Protective Material During the Thermooxidative Treatment of the Additives , Fire and materials, 20: 191-203.

Bourbigot, S. , Le Bras, M. , Duquesne, S. and Rochery, M. (2004). Recent Advances for Intumescent Polymers , Macromolecular Materials and Engineering, 289: 499-511.

Halpern, Y. , Mott, D.M. and Niswarder, R.H. (1984). Fire Retardancy of Thermoplastic Materials by Intumescence , Industrial & Engineering Chemistry Product Research and Development, 23: 233-238.

Le Bras, M. , Bugajny, M. , Lefebvre, J.M. and S. Bourbigot (2000). Use of Polyurethanes as Char-forming Agents in Polypropylene Intumescent Formulations , Polymer International, 49(10): 1115-1124.

10.

Metin, D. , Tihminlioglu, F. , Balkose, D. and Ulku, S. (2004). The Effect of Interfacial Interactions on the Mechanical Properties of Natural Zeolite-PP Composites , Composites: Part A, Applied Science and Manufacturing, 35: 23-32.

11.

Wu, Q. , Lv, J.P. and Qu, B.J. (2003). Preparation and Characterization of Microcapsulated Red Phosphorus and Its Flame-retardant Mechanism in Halogen-free Flame Retardant Polyolefins , Polymer International, 52(8): 1326-1331.

12.

Li, X. , Ou, Y.X. , Zhang, Y.H. and Lian, D.J. (2000). Synthesis and Structure of A Novel Caged Bicyclic Phosphate Flame Retaradant , Chinese Chemical Letters, 11(10): 887-890.

13.

Schartel1, B. and Hull, T.R. (2007). Development of Fire-retarded Materials - Interpretation of Cone Calorimeter Data , Fire and Materials, 31: 327-354.

14.

Wang, J.Q. (1992). Theory of X-ray Photoelectron Spectroscopy, Industry of National Defence Press, Beijing.

15.

Nakayama, Y. , Soeda, F. and Ishitani, A. (1990). XPS Study of the Carbon Fiber Matrix Interface , Carbon, 28(1): 21-26.

16.

Delpeux, S. , Beguin, F. , Benoit, R. , Erre, R. , Manolova, N. and Rashkov, I. (1998). Fullerene Core Star-like Polymers-1. Preparation from Fullerenes and Monoazidopolyethers , European Polymer Journal, 34(7): 905-915.

17.

Brown, N.M.D. , Hewitt, J.A. and Meenan, B.J. (1992). X-ray-Induced Beam Damage Observed during X-ray Photoelectron Spectroscopy (XPS) Studies of Palladium Electrode Ink Materials , Surface and Interface Analysis, 18(3): 187-198.

18.

Shih, P.Y. , Yung, S.W. and Chin, T.S. (1998). Thermal and Corrosion Behavior of P2O5-Na2O-CuO Glasses , Journal of Non-Crystalline Solids, 224(2): 143-152.

19.

Clark, D.T. , Fok, T. , Roberts, G.G. and Sykes, R.W. (1980). An Investigation by Electron Spectroscopy for Chemical Analysis of Chemical Treatments of the (100) Surface of n-type InP Epitaxial Layers for Langmuir Film Deposition , Thin Solid Films, 70(2): 261-283.

20.

Bourbigot, S. , Lebras, M. and Delobel, R. (1993). Carbonization Mechanisms Resulting from Intumescence Association with the Ammonium Polyphosphateepentaerythritol Fire Retardant System , Carbon, 31(8): 1219-1230.

21.

Beamson, G. and Briggs, D. (1992). High Resolution XPS of Organic Polymers, John Wiley & Sons, Chichester.

22.

Chen, X.L. , Hu, Y. , Jiao, C.M. and Song, L. (2007). Preparation and Thermal Properties of a Novel Flame-retardant Coating , Polymer Degradation and Stability , 92: 1141-1150.

23.

Wang, Z.Y. , Han, E.H. and Ke, W. (2006). Effect of Acrylic Polymer and Nanocomposite with nano-SiO2 on Thermal Degradation and Fire Resistance of APP-DPER-MEL Coating , Polymer Degradation and Stability, 91: 1937-1947.

24.

Qu, B.J. and Xie, R.C. (2003). Intumescent Char Structures and Flame-retardant Mechanism of Expandable Graphite-based Halogen-free Flame-retardant Linear Low Density Polyethylene Blends , Polymer International , 52: 1415-1422.

25.

Carpentier, F. , Bourbigot, S. and Le Bras , M. (2000). Charring of Fire Retarded Ethylene Vinyl Acetate Copolymer - Magnesium Hydroxide/Zinc Borate Formulations , Polymer Degradation and Stability, 69: 83-92.