CCA removal from treated wood using a dual remediation process

Abstract

Novel approaches to remediate chromated-copper-arsenate (CCA)-treated waste wood are needed to divert this material from landfills. In this study, CCA-treated wood wafers were treated with a two-step remediation process to remove copper, chromium and arsenic. Process conditions, involving an acid extraction and bacterial culture with a metal-tolerant bacterium, were optimized. It was determined that 18 h of exposure to 1.0% oxalic acid was an optimal exposure time for the size of wood used in this study. Oxalic acid concentration was then varied to determine optimal concentration for metal removal. Increasing concentrations of oxalic acid removed increasing quantities of copper, chromium and arsenic. Acid extraction at 0.80% and bacterium exposure resulted in a total reduction of 78% copper, 97% chromium and 93% arsenic. An 0.8% of oxalic acid followed by bacterial culture with Bacillus licheniformis CC01 afforded the best conditions for maximum removal of copper, chromium, and arsenic from treated wood with minimal exposure of the wood fiber to acid conditions.

Keywords

Bacillus licheniformis CC01 bioremediation chromated copper arsenate (CCA)oxalic acid wood preservative

Get full access to this article

View all access options for this article.

References

AWPAA11-93 (1995) Standard method for the analysis of treated wood and treating solutions by atomic absorption spectroscopy. Woodstock, MD, USA: American Wood Preservers' Association.

Clausen, C.A. & Smith, R.L. (1998a) CCA removal from treated wood by chemical, mechanical and microbial processing. In: 4th International Symposium on Wood Preservation, IRG/WP 98-50101, Stockholm , Sweden, pp. 333-344.

Clausen, C.A. & Smith, R.L. (1998b) Removal of CCA from treated wood by oxalic acid extraction, steam explosion, and bacterial fermentation. Journal of Industrial Microbiology and Biotechnology 20, 251-257.

Cole, F.A. & Clausen, C.A. (1997) Bacterial Biodegradation of CCA Treated Waste Wood . In: Falk, R. H. (ed.) Proceedings Forest Products Society: the Use of Recycled Wood and Paper in Building Applications. Proceedings 7286, Madison, WI, USA: Forest Products Society, pp. 201-204.

Cooper, P.A. (1991) Leaching of CCA from treated wood: pH effects. Forest Products Journal 41, 30-32.

Cooper, P.A. (1993) Leaching of CCA: is it a problem? Disposal of treated wood removed from service: the issues. In: Proceedings, Environmental Considerations in Manufacture, Use, and Disposal of Preservative-Treated Wood Madison, WI, USA: Carolinas-Chesapeake Section, Forest Products Society, pp. 45-57, 85-90.

Kim, J. & Kim, G. (1993) Leaching of CCA components from treated wood under acidic conditions. International Research Group on Wood Preservation, IRG/WP/93-5004.

McQueen, J. , Stevens, J. & Kamdem, D.P. (1998) Recycling of CCA treated wood in the U.S In: 4th International Symposium on Wood Preservation, IRG/WP 98-50101, Stockholm, Sweden, pp. 77-93.

Micklewright, J.T. (1994) Wood preserving statistics. A Report to the Wood Preserving Industry in the United States. Granbury, TX , USA: American Wood Preservers' Association.

10.

Pasek, E. (1994) Treatment of CCA waste streams for recycling use . In: Proceedings, CITW Life Cycle Assessment Workshop . Ottawa, Ontario, Canada: Canada Institute of Treated Wood, pp. 76-104.

11.

Stephan, I. , Leithoff, H. & Peek, R.-D. (1996) Microbial conversion of wood treated with salt preservatives. Material und Organismen 30, 179-200.

12.

Stephan, I. , Mimz, H. & Peek, R.-D. (1993) Detoxification of salt-impregnated wood by organic acids in a pulping process. International Research Group on Wood Preservation, IRG/WP/93-50012.

13.

Warner, J. & Solomon, K. (1990) Acidity as a factor in leaching of copper, chromium and arsenic from CCA-treated dimension lumber. Environmental Toxicology and Chemistry 9, 1331-1337.