The effective flaw model is developed to describe the S-N curves of different materials and failure modes. By introducing the concepts of the “equivalent static loading” and the “equivalent number of cycles,” a new data fitting technique suggested by the present paper has some physical meaning. Using the simplified form of the present characterization, only a few tests are required to describe the sketch of unknown material S-N curve under the fatigue loading.
HahnH. T.1989. “Fatigue of Composites,” in ZwebenC.HahnH. T.ChouT.-W. (eds.), Mechanical Behavior and Properties of Composite Materials, Vol. 1, Lancaster: Technomic Publishing Co., Inc, pp. 73–130.
2.
YoungR. J.1984. “Fatigue of Non-Metallic Materials,” in SmithR. S. (ed.), Fatigue Crack Growth, 30 Years of Progress, Oxford: Pergamon Press, pp. 103–116.
3.
ReifsniderK. L. (ed.) 1990. Fatigue of Composite Materials, Amsterdam: Elsevier Sci. Publisher B.V.
4.
GaoZ. T.1986. Applied Statistics in Fatigue, Beijing: National Defence Industry Press.
5.
GaoZ. T.1980. Fatigue Property Test, Beijing: National Defence Industry Press.
6.
ReifsniderK. L.1982. “Damage Mechanics and NDE of Composite Laminates,” HashinZ.HerakovichC. T. (eds.), Mechanics of Composite Materials, Recent Advance, New York: Pergamon Press, pp. 399–420.
7.
WangA. S. D.1984. “Fracture Mechanics of Sublaminate Cracks in Composite Materials,” Composites Technology Review, 6(2):45–62.
8.
DanielI. M.CharewiczA.1986. “Fatigue Damage Mechanisms and Residual Properties of Graphite/Epoxy Laminates,” Engr. Fracture Mech., 35(5/6):793–808.
9.
O'BrienT. K.1988. “Fatigue Delamination Behaviour of PEEK Thermoplastic Composite Laminates,” J. Reinforced Plastics and Composites, 7(4):341–359.
10.
O'BrienT. K.RigamontiM.ZanottiC.1989. “Tension Fatigue Analysis and Life Prediction for Composite Laminates,” International J. Fatigue, 11(6):379–393.
11.
JessenS. M.PlumtreeA.1991. “Continuum Damage Mechanics Applied to Cyclic Behaviour of a Glass Fiber Composite Pultrusion,” Composites, 22(3):181–190.
12.
Henaff-GardinC.Lafarie-FrenotM. C.1992. “Fatigue Behaviour of Thermoset and Thermoplastic Cross-Ply Laminates,” Composites, 23(2):109–116.
13.
XuL. Y.1994. “Interaction between Matrix Cracking and Edge Delamination in Composite Laminates,” Composite Sci. and Tech., 50(4):469–478.
14.
GriffithA. A.1920. “The Phenomena of Rupture and Flaw in Solid,” Philosophical Transactions of the Royal Society, A-221:163.
15.
XuL. Y.1997. “Probabilistic Character of the Microcrack Growth in Brittle Layered Materials,” Theoretical and Applied Fracture Mechanics, 27:167–174.
16.
FlaggsD. L.1985. “Prediction of Tensile Matrix Failure in Composite Laminates,” J. of Composite Materials, 19(1):29–50.