This investigation deals with the fatigue behaviour under low energy repeated impact (LERI) of quasi-isotropic graphite/epoxy composite plates. The damage growth during the test was monitored by ultrasonic C-scan imaging. The damage area plotted as function of the number of impacts displays a three stages pattern behaviour. Stage I corresponds to a matrix cracking of the region under the impactor, stage II corre sponds to a rapid delamination propagation and stage III to a slow delamination propaga tion. The relative extent and the damage growth rate in stage II increase with the impact energy E I. The number of impacts NIF corresponding to the transition between stage I and stage II is governed by an impact-fatigue curve in the form of EI = C log (NIF) + E 0 where E0 is the threshold impact energy that induces a delamination in one impact and C constant denoting the damage tolerance of the material.
Zukas, J.A., T. Nicholas, H.F. Swift, L.B. Greszczuk and D.R. Curran.1982. Impact Dynamics. New York, NY: John Wiley & Sons.
2.
Goldsmith, W.1960. Impact. London: Edward Arnold.
3.
Macaulay, M.A.1987. Introduction to Impact Engineering. London: Chapman and Hall.
4.
Kessler, S.L., G.C. Adams, S.B. Driscoll and D.R. Ireland.1987. "Instrumented Impact Testing of Plastics and Composite Materials," ASTM STP 936, American Society for Testing and Materials, Philadelphia.
5.
Rotem, A.1988. "The Strength of Laminated Composite Materials under Repeated Impact Loading," Journal of Composites Technology and Research , 10(2):74-79.
6.
Hertzberg, R.W. and J.A. Manson.1980. Fatigue of Engineering Plastics. New York, NY: Academic Press.
7.
Johnson, D.N., A.A. Johnson and D.J. Keller.1986. "Phenomenological Model of Impact Fatigue in Pearlitic Plain Carbon Steels," in Mechanism of Fracture , ASM, Metals Park, OH, pp. 451-454.
8.
Barr, B. and A. Bouamrata.1988. "Development of Repeated Drop Weight Impact Testing Apparatus for Studying Fiber Reinforced Concrete Materials ," Composites, 9(6):453-466.
9.
Barr, B. and A. Baghli.1988. "A Repeated Drop Weight Impact Testing Apparatus for Concrete," Magazine of Concrete Research, 40(144):167-176.
10.
Bhattacharya, A., T. Joseph and B. Kishor.1988. "Crack Formation and Fracture under Repeated Tension-Impact Loads," Theory and App. Fract. Mech., 9:39-44.
11.
Hsi, W.H. and K.Y. Lee.1989. "Repeated Impact Response of XT-75 mm Cannon Support," Theory and App. Fract. Mech., 12(1):33-43.
12.
Findley, W.N. and O.E. Hintz.1943. "The Relation between Results of Repeated Blow Impact Test and of Fatigue Tests," Amer. Soc. Test. Mat., Proc., 43:1226-1239.
13.
Bhateja, S.K. , J.K. Rieke and E.H. Andrews.1979. "Impact Fatigue Response of Ultra-High Molecular Weight Linear Polyethylene," J. of Mat. Sci., 14:2103-2109.
14.
Anonymous1988. " Durability Factor," Industrial Lubrication and Tribology, 40(2):14-15.
15.
Adams, C.C.1987. "Impact Fatigue of Polymers Using an Instrumented Drop Tower Device," in Reference [4], pp. 281-301.
16.
Lhymn, C.1985. "Impact Fatigue of PPS/Glass Composites," J. Mater. Sci., Letters4, pp. 1221-1224.
17.
Leach, D.C., D.C. Curtis and D.R. Tamblin.1987. "Delamination Behavior of Carbon Fiber/PEEK Composites," Toughened Composites, ASTM STP 937, ASTM, Philadelphia, pp. 358-380.
18.
Wyrick, D.A. and D.F. Adams.1988. "Residual Strength of a Carbon/Epoxy Composite Material Subjected to Repeated Impact," J. of Composite Materials, 22:749-765.
19.
Nayeb-Hashemi, H., M.D. Cohen, J. Zotos and R. Poormand.1988. "Ultrasonic Characteristics of Graphite/Epoxy Composite Material Subjected to Fatigue and Impacts," J. of Nondestructive Evaluation, Vol. 5, Nos. 3/4.
20.
Jang, B.P., C.T. Huang, C.Y. Hseih, W. Kowbel and B.Z. Jang.1991. "Repeated Impact Failure of Continuous Fiber Reinforced Thermoplastic and Thermoset Composites," Journal of Composite Materials, 25:1171-1203.
21.
Sun, C.T. and S. Chattopadhyay .1975. "Dynamic Response of Anisotropic Laminated Plates Under initial Stress to Impact of a Mass," Journal of Applied Mechanics, Transactions of the ASME, p. 693.
22.
Greszczuk, L.B.1982. "Damage in Composite Materials Due to Low Velocity Impact," in Reference [1], p. 55-94.
23.
Matthew, C.C. and M.M. Steven.1987. "Instrumented Impact Test Data Interpretation," in Reference [4], pp. 9-23.
24.
Pipes, R.B., R.A. Blake, J.W. Gillespie and L.A. Carlsson.1990. Test Methods, Lancaster, PA: Technomic Publishing, Co., Inc.
25.
Boukhili, R. , P. Hubert and R. Gauvin.1991. "Loading Rate Effect as a Function of the Span-to-Depth Ratio in Three-Point Bend Testing of Unidirectional Pultruded Composites," Composites, 22(1):39-45.
26.
Lakshminarayana, H.V., R. Boukhili and R. Gauvin.1993. "Finite Element Simulation of Impact Tests of Laminated Composites," Composites Structures , in press.
27.
Boukhili, R., C. Bojji and R. Gauvin.1992. "Effect of Repeated Impact on the Residual Shear Strength of Unidirectional Composites," in Composite Structures and Materials, S. V. Hoa and R. Gauvin, eds., London and New York: Elsevier Applied Science.
28.
Maikuma, H. , J.W. Gillespie and D.J. Wilkins.1990. " Mode II Interlaminar Fracture of the Center Notch Flexural Specimen Under Impact Loading," Journal of Composite Materials, Vol. 24.
29.
Russel, A.J. and K.N. Street.1985. "Moisture and Temperature Effect on the Mixed Mode Delamination Fracture of Unidirectional Graphite/Epoxy," ASTM STP 876, American Society for Testing and Materials, PA, pp. 349-370.
30.
Kim, C.G. and E.J. Jun.1991. "Impact Characteristics of Composite Laminated Sandwich Structures," Proc. of the International Conference on Composite Materials ICCM/VIII, Honolulu, Hawai, paper 32G.
31.
Hull, D. and Y.B. Shi.1993. "Damage Mechanism Characterization in Composite Damage Tolerance Investigations," Composites Structures , 23:99-120.
32.
Shivakumar, K.N. , W. Elbert and W. Illg.1985. "Prediction of Low-Velocity Impact Damage in Thin Circular Laminates," AIAA Journal, 23(3):442-449.