On the Increase in Fracture Energy with Thickness in Delamination of Unidirectional Glass Fibre-Epoxy with Cut Central Plies

Abstract

The effect of thickness on delamination is investigated by means of static tension tests on unidirectional glass fibre-epoxy specimens with cut central plies. It is found that the delamination stress decreases with increasing thickness, but by significantly less than predicted on the basis of classical fracture mechanics. This indicates that the fracture energy is not constant and therefore cannot be considered to be a material prop erty. Tests on specimens with 8 cut and 32 continuous plies showed an increase of 69% in the fracture energy compared with specimens with 1 cut and 4 continuous plies. Tests on specimens with different ratios of cut to continuous plies suggest that it is the number of cut plies and the magnitude of the applied stress which influence the fracture energy. It is postulated that the fracture energy is a function of the size of a plastic zone which is dependent on the specimen geometry and applied stress. Caution therefore needs to be exercised in using values of fracture energy in situations different from the ones under which they were measured.

Get full access to this article

View all access options for this article.

References

O'Brien, T.K. 1982. "Characterisation of Delamination Onset and Growth in a Composite Laminate" in Damage in Composite Materials , ASTM STP 775, pp. 140-167

Wang, A.S.D. and F.W. Crossman. 1980. "Initiation and Growth of Transverse Cracks and Edge Delamination in Composite Laminates Part 1, An Energy Method," J. Composite Materials, (Supp. 14):71-87.

Law, G.E. 1984. "A Mixed Mode Fracture Analysis of (±25/90 n) s Graphite/Epoxy Composite Laminates," in Effects and Defects in Composite Materials, ASTM, STP 836, pp. 143-160.

Salpekar, S.A. , I.S. Raju and T.K. O'Brien. 1988. "Stram Energy Release Rate Analysis of Delamination in a Tapered Laminate Subjected to Tension Load," Proc. American Soc. for Composites 3rd Tech. Conf., Seattle, pp. 642-654.

Brewer, J.C. and P.A. Lagace. 1988. "Quadratic Stress Criterion for Initiation of Delamination," J. Composite Materials , 22 1141-1155.

Wisnom, M.R. 1991. "Delamination in Tapered Unidirectional Glass Fibre-Epoxy Under Static Tension Loading," Proc. AIAA Structures, Structural Dynamics and Materials Conf., Baltimore, pp. 1162-1172.

Darby, M.I. , J.M. Richards and B. Yates. 1985. "Effect of Discontinuous Plies on the Tensile Strength of CFRP Laminates," J. Material Science Letters, 4:203-206

Prinz, R. and Li Ye. 1990. "Interlaminar Mode II Energy Release Rate for Delamination Growth of Graphite/Epoxy Composites," in Selected Papers in Scientific and Technical International Cooperation Program (2) Chinese Aeronautics and Astronautics Establishment , pp. 83-116.

Wang, S.S. 1979 "Delamination Crack Growth in Unidirectional Fiber-Reinforced Composites Under Static and Cyclic Loading," in Composite Materials: Testing and Design (Fifth Conference, ASTM STP 674, pp. 642-663.

10.

Partridge, I.K. , J. A M. Jaussaud and P.E.L. Corberand. 1991. "Toughness Transfer from Matrix to Composite under Static and Dynamic Loadings," Proc. 1st Int Conf. on Deformation and Fracture of Composites, Manchester, Paper no. 4, pp. 1-7.

11.

Sinclair, G.B. and A.E. Chambers. 1987. "Strength Size Effects and Fracture Mechanics: What Does the Physical Evidence Say?" Engineering Fracture Mechanics, 26(2):279-310