Stitching through-the-thickness (TTT) of composite materials produces a surface loop of yarn between successive penetrations. The surface loop is pressed into the surface layers of the composite material during the curing of the laminate, kinking the in plane fibers near the surface of the material. The compression strength and compression- after-impact (CAI) strengths of carbon-epoxy specimens were measured with and without the surface loop. Removal of the surface loop had no influence on failure mode or failure mechanism, but did significantly increase the compression and CAI strengths.
Get full access to this article
View all access options for this article.
References
1.
Dow, M.B. , D.L. Smith and S.J. Lubowinski1989. "An Evaluation of Stitching Concepts for Damage-Tolerant Composites," NASA CP 3038.
2.
Dexter, H.B. and J.G. Funk1986. "Impact Resistance and Interlaminar Fracture Toughness of Through-the-Thickness Reinforced Graphite/Epoxy," AIAA paper 86-1020-LP.
3.
Pelstring, R.M. and R.C. Madan.1989 "Stitching to Improve Damage Tolerance of Composites," presented at the 34th International SAMPE Symposium May 8-11, 1989, book 2 of 2
4.
Dow, M.B. and D.L. Smith1989 "Damage-Tolerant Composite Materials Produced by Stitching Carbon Fabrics," Proceedings of 21st International SAMPE Technical Conference, Atlantic City, NJ, Sept. 1989
5.
Farley, G.L.1991. "A Mechamsm Responsible for Reducing Compression Strength of Through-the-Thickness Reinforced Composite Material," submitted for publication to the Journal of Composite Materials, Winter 1991
6.
Evans, D.A. and J.S. Boyce.1989 "Transverse Reinforcement Methods for Improved Delamination Resistance," presented at the 34th International SAMPE Symposium, May 8-11, 1989, Vol. 34, book 1 of 2
7.
Farley, G.L., B.T. Smith and J. Maiden.1991. "Compression Response of Stitched and Integrally Woven Through-The-Thickness Reinforced Composite Materials," submitted to the Journal of Composite Materials for publication, Spring, 1991.
8.
1982. "Test of Fiber Content of Resin-Matrix Composites by Matrix Digestion," Annual Book of ASTM Standards, Part 36, D3171-76.