Hygrothermal Influence on the Flexural Properties of Kevlar-Graphite/Epoxy Hybrid Composites

Abstract

The hygrothermal influence on the flexural properties of unidirectional Kevlar 49-graphite/epoxy hybrid composite was investigated in the temperature range -50°C to 150°C. Moisture was introduced into the specimen by immersion in distilled water. Two material lay-ups were used in this investigation. In Kev 49/T-300/Kev 49, Kevlar 49 and graphite prepreg are used as outer and center layer, respectively and in T-300/Kev 49/T-300, it was vice-versa. In both cases the tapes were alternated until the total thickness was achieved. Data for the determination of flexural strength and modulus were generated at various temperatures for both dry and saturated specimens. The results show that both flexural strength and modulus change with the ply sequence of hybrid lami nates. The flexural strength and modulus of Kev 49/T-300/Kev 49 are relatively higher than those of T-300/Kev 49/T-300. The apparent flexural strength decrease with the in crease of temperature in the range 23°C to 150°C. The addition of moisture further degrades the flexural strength in the same temperature range. At low temperature (-50°C) the addition of moisture resulted in an increase in the flexural strength of Kev 49/T-300/Kev 49. Both tensile and compressive failures take place in flexural test and the failure mode changes with the aging condition.

Get full access to this article

View all access options for this article.

References

Chamis, C.C. and R.F. Lark. "Hybrid Composites State-of-the-Art Review Analysis, Design, Application and Fabrication," NASA TM X-73545

Zweben, C. and M.W. Wardle. 1979 "Flexural Fatigue of Marine Laminate Reinforced of E-Glass and Kevlar 49 Aramid," Proceedings of 34th Annual Conference Reinforced Plastics/Composite Institute, Society of Plastic Industry, New Orleans, LA, Section 4c, pp 1-6

Riewald, P.G. and C. Zweben. 1975 "Kevlar 49 Hybrid Composites for Commercial and Aerospace Applications," Presented 30th Annual Conference of Reinforced Plastics/Composites Institute, February 6

Fogg, L.D. 1974. "Hybrid Composite Design for Damage Tolerance," 2nd Conference on Fibrous Composites in Flight Vehicle Design , Daytona, Ohio, May

1981 "DuPont" Technical Information, Kevlar Aramid, Bulletin K-5, September

Fisher, S. and G. Marom 1987 "The Flexural Behavior of Aramid Fiber Hybrid Composite Materials," Composite Science & Technology, 28:291-314.

Guerini, E. and P. Lissae 1978 "Contribution to the Study of Hybrid Laminates Fabricated from Graphite, Kevlar 49 and Glass," Verre Text. Plast Reinf ., No , (July-August) 5-16

Abbott, N.J. , J.G. Donovan , M.M. Schoppee and J. Skelton. 1975 "Some Mechanical Properties and Other Heat Resistant, Nonflammable Fibers, Yarns, and Fabrics," Fabric Research Laboratories Report AFML-TR-74-65, Part III, Dedham, MA (March)

Springer, G S , ed. 1981 Environmental Effects on Composite Materials, Vol. I Lancaster, PA: Technomic Publishing Company

10.

Springer, G S , ed 1984 Environmental Effects on Composite Matenals, Vol. 2 Lancaster, PA

Technomic Publishing Company

11.

Tsai, S. W. , ed 1988. Composite Design, 4th ed Think Composite Publication, pp 17-3