This paper discusses the matrix cracking sequence in a [02/90 2]s graphite epoxy laminate with double-side notches. Experiments were performed on specimens loaded in uniaxial, quasi-static tension. The specimens were inspected at ascending load increments by x-radiography for patterns of matrix cracks caused by stress concentration near the notched region.
Get full access to this article
View all access options for this article.
References
1.
Wang, A. S D. "Fracture Mechanics of Sublaminate Cracks in Composite Laminates," Composite Technology Review, 645-62 (1984).
2.
Crossman, F.W. and A. S D. Wang "The Dependence of Transverse Cracking and Delamination on Ply Thickness in Graphite-Epoxy Laminates," in Fatigue of Fibrous Composite Materials, ASTM STP-775, pp 118-139 (1982).
3.
Wang, A S. D. and F.W. Crossman "Initiation and Growth of Transverse Cracks and Edge Delamination in Composite Laminates, Part 1 An Energy Method ," Jour. Composite Materials, 1471-87 (1980)
4.
Crossman, F.W. , W.J. Warren, A. S D. Wang and G E Law "Initiation and Growth of Transverse Cracks and Edge Delamination in Composite Laminates, Part 2 Experimental Correlation," Jour. Composite Materials , 1488-108 (1980)
5.
Wang, A S D , N.N. Kishore and C.A. Li "On Crack Development in Graphite-Epoxy [0 2/902n]s Laminates under Uniaxial Tension," Composite Science and Technology, 24:1-31 (1985)
6.
Wang, A. S. D , W. Binienda and Y. Zhong. "Mixed Mode Fracture of Uniaxial Fiber Reinforced Composites," NADC Technical Report (1987)
7.
Wang, A S D., E.S. Reddy and N.N. Kishore "A Three Dimensional Finite Element Code and Users Manual for Analysis of Matrix Cracking in Laminates," Drexel University Technical Report (1987)
8.
Reifsnider, K.L. "Critical Element Concepts for Residual Strength and Life Prediction ," Proc. American Society for CompositesLancaster, PATechnomic Publishing Co., pp 387-403 (1986).