Apparatus for Preparing Thermoplastic Composites

Abstract

The properties of high performance composites with semi-crystalline thermoplastic matrices are dependent upon the processing conditions during manufacturing. To study the relationship between processing and material properties, a low cost molding apparatus was developed and evaluated. This apparatus is capable of processing both thermoplastic composite and pure thermoplastic polymer test specimens at controlled combinations of cooling rate, molding temperature and consolidation pressure. It consists of a water cooled aluminum mold, a high flow rate water pump and a hydraulic molding press with heated platens. A description of the molding apparatus is presented along with a detailed descrip tion of the molding procedures used to fabricate and anneal both composite and pure polymer specimens. Using this apparatus specimens of carbon fiber/PEEK and PEEK polymer composites were molded at cooling rates ranging from 0.01 °F/min up to as high as 21,000°F/min. Differential Scanning Calorimetry (DSC) testing showed specimen crystallinities ranging from 0 to 45 percent crystallinity are readily obtainable.

Get full access to this article

View all access options for this article.

References

Talbott, M.F. , G.S. Springer , and L.A. Berglund. "The Effect of Crystallinity on the Mechanical Properties of PEEK and Graphite Fiber Reinforced PEEK," submitted for publication to the Journal of Composite Materials.

Seferis, J.C. "Polyetheretherketone (PEEK): Processing-Structure and Properties Studies for a Matrix in High Performance Composites," Polymer Composites, 7:158-169 (1986).

Lee, W.I. , M.F. Talbott , G.S. Springer , and L.A. Berglund. "Effects of Cooling Rate on the Crystallinity and Mechanical Properties of Thermoplastic Composites," Journal of Reinforced Plastics and Composites, 6(1) (1987).

Blundell, D.J. , J.M. Chalmers , M.W. Mackenzie , and W.F. Gaskin. "Crystalline Morphology of the Matrix of PEEK-Carbon Fiber Aromatic Polymer Composites I. Assessment of Crystallinity," SAMPE Quarterly, 16:22-30 (1985).

Blundell, D.J. , D.R. Beckett , and P.H. Wilcocks. "Routine Crystallinity Measurements of Polymers by D.S.C," Polymer, 22:704-707 (1981).

Hartness, J.T. "Polyphenylene Sulfide Matrix Composites," in The 1980's Payoff Decade for Advanced Materials. L. C. May and F. J. Riel, eds. 25th National SAMPE Symposium and Exhibition, 25:376-388 (1980).