Thermally Induced Transverse Cracking in Graphite-Epoxy Cross-Ply Laminates

Abstract

Thermally induced transverse cracking in T300/5208 graphite-epoxy cross-ply laminates was investigated experimentally and theoretically. The six laminate configura tions studied were: [0/90₃]_s, [0₂/90₂]_s, [0₃/90]_s, [90/0₃]_s, [90₂/0₂]_s, and [90₃/0]_s. The thermal load required to initiate transverse cracking was determined experimentally and compared to theoretical prediction. Experimental results for the accumulation of transverse cracks, under cyclic thermal loading between —250°F and 250°F for up to 500 thermal cycles, are presented. The calculated in situ transverse lamina strength was deter mined to be at least 1.9 times the unidirectional lamina transverse tensile strength. All laminate configurations exhibited an increase in crack density with increasing thermal cycles.

Get full access to this article

View all access options for this article.

References

Adams, D.S. and Herakovich, C.T. , "Influence of Damage on the Thermal Response of GraphiteEpoxy Laminates," Journal of Thermal Stress, Vol. 7, pp. 91-103.

Bowles, D.E. , "Effects of Microcracks on the Thermal Expansion of Composite Laminates," Journal of Composite Materials, Vol. 18, No. 2, pp. 173-187 (March 1984).

Herakovich, C.T. , Davis, J.G. , Jr. and Mills, J.S. , "Thermal Microcracking in Celion 6000/PMR-15 Graphite Polyimide," Thermal Stresses in Severe Environments, D. P. H. Masselman , and R. A. Heller , Editors. Plenun Publishing Company, pp 649-664 (1980).

Adams, D.S. , Bowles, D.E. and Herakovich, C.T. , "Characteristics of Thermally-Induced Transverse Cracks in Graphite-Epoxy Composite Laminates," VPI-E-83-23, Virginia Polytechnic Institute and State University, Blacksburg, VA (June 1983).

Pagano, N.J. and Hahn, H.T. , "Evaluation of Composite Curing Stresses," Composite Materials: Testing and Design (Fourth Conference), ASTM STP 617, American Society for Testing and Materials, pp. 317-329 (1977).

Jones, R.M. , Mechanics of Composite Materials, Scripta Book Company , Washington, D.C. (1975 ).

Flaggs, D.L. and Kural, M.H. , "Experimental Determination of the In Situ Transverse Lamina Strength in Graphite/Epoxy Laminates," J. Composite Materials, Vol 16, pp. 103-116 (March 1982).

Nagarkar, A.P. and Herakovich, C.T. , "Nonlinear Temperature Dependent Failure Analysis of Finite Width Composite Laminates," VPI-E-79-36, Virginia Polytechnic Institute and State University, Blacksburg, VA (December 1979).