Residual Strength Assessment of Low Velocity Impact Damage of Graphite-Epoxy Laminates

Abstract

This report contains the study of Low Velocity Transverse Impact Damage of graphite-epoxy T300/5208 composite laminates. The specimen, 100 mm diameter clamped plates, were impact damaged by a cantilever-type instrumented 1-inch diameter steel ball. Study was limited to impact velocity 6 m/sec. Rectangular strips, 50 mm x 125 mm, were cut from the impact-damage specimens so that the impact damage zone was in the center of the strips. These strips were tested in tension to ob tain their residual strength.

An energy dissipation model was developed to predict the residual strength from fracture mechanics concepts. Net energy absorbed I_a was evaluated from coefficient of restitution concepts based on shear dominated theory of fiber-reinforced materials, with the modification that during loading and unloading the shear deformation are respectively elastic-plastic and elastic. Delamination energy I_d was predicted by assum ing that the stiffness of the laminate dropped due to debonding. Fiber-breakage energy, assumed to be equal to the difference of I_a and I_d, was used to determine the residual strength. Predictions were compared with test results.

Get full access to this article

View all access options for this article.

References

Impact Tests at Fatigue and Fracture Laboratory, NASA-Langley Research Center, Hampton, Virginia 23665.

"Foreign Objects Damage to Composites,"

ASTM STP 586, 1976.

"Fracture of Engineering Brittle Materials," Jayatilaka, A. S., Applied Science Publishers Ltd., London, 1979, p. 268.

"Impact," Goldsmith, W., Edward Arnold, London, 1960.

Bostaph, G.M. and Elber, W. , "Static Indentation Tests of Composite Plates for Impact Suspectability Evaluation," A Research Report, NASA-Langley Research Center, Hampton, Virginia 23665.

Lal, K.M. , "Low Velocity Transverse Impact Behavior of Thin Graphite-Epoxy laminates," Submitted to Composites Technical Review.

"Theory of Plates and Shells," Timoshenko , S. and Woinowsky-Krieger, S. , McGraw-Hill Book Company, Inc., 1959, p. 396.

Shaw, L. and Spencer, A.J.M. , "Transverse Impact of Ideal Fiber-Reinforced Rigid-Plastic Plates," Proc. R. Soc. London, A361, 1978, p. 43.

Lal, K.M. , "Coefficient of Restitution for Low Velocity Transverse Impact of Thin Graphite-Epoxy Laminates," Submitted to Composites Technical Review.

10.

Johnson, W. , "Impact Strength of Material," Edward Arnold, London, 1972.

11.

Sih, G.C. , Paris, P.C. , and Irwin, G.R. , "On Cracks in Rectilinearly Anisotropic Bodies," Int. J. Frac. Mech., 1, 1965 , p. 189.

12.

Wu, E.M. , "Application of Fracture Mechanics to Anisotropic Plates," J. App. Mech., Trans. ASME, Series E, 34, 1967, p. 967.

13.

Husman, G.E. , Whitney, J.M. , and Halpin, J.C. , "Residual Strength Characterization of Laminated Composites Subjected to Impact Loading," Foreign Objects Damage to Composites, ASTM STP 586, 1974, p. 92.

14.

Lal, K.M. , "Prediction of Residual Tensile Strength of Transversely Impacted Composite Laminates," Structures and Solid Mechanics , NASA CP-2245, 1982, p. 97.