Microstructure analysis of carbon-fiber-reinforced polymer laminates subjected to self-heating and fatigue strengthening under tension-tension fatigue loading
Restricted accessResearch articleFirst published online December, 2025
Microstructure analysis of carbon-fiber-reinforced polymer laminates subjected to self-heating and fatigue strengthening under tension-tension fatigue loading
In this study, tensile-tensile fatigue testing of unidirectional (UD) carbon-fiber-reinforced polymer (CFRP) prepreg laminates was performed. Two types of specimens (open-hole and unopened-hole ones) were examined at different stress levels to elucidate the impact of fatigue damage on their static strength at different numbers of cycles. The effect of internal heat generation during fatigue on the life of unopened-hole CFRP laminates was analyzed by observing the changes in the microstructure of specimens. The results revealed that the difference in fatigue life between unopened specimens with and without cooling at 70% ultimate tension stress (UTS) level was about 88 times. In the open-hole CFRP laminates, the residual tension strength (RTS) after increases and then decreases with the number of fatigue cycles, and the interface debonding was a significant cause of fatigue strengthening. Open-hole specimens were shown to withstand continuous cycling under severe loads at 5% above their ultimate stress levels. Therefore, the fatigue damage extension of the open-hole laminates can be slowed down under intensive cycling at high stress levels, ensuring good fatigue performance of the material.
ZhangXChenYHuJ. Recent advances in the development of aerospace materials. Prog Aerosp Sci2018; 97: 22–34.
2.
BarileCCasavolaCDe CillisF. Mechanical comparison of new composite materials for aerospace applications. Compos B Eng2019; 162: 122–128.
3.
SalifuSDesaiDOgunbiyiO, et al.Recent development in the additive manufacturing of polymer-based composites for automotive structures—a review. Int J Adv Manuf Technol2022; 119: 6877–6891.
4.
HarussaniMMSapuanSMNadeemG, et al.Recent applications of carbon-based composites in defence industry: a review. Defence Technol2022; 18: 1281–1300.
5.
LiJZhuZHuangY, et al.Ni3N: a multifunctional material for energy storage and electrocatalysis. Materials Today Energy2022; 26: 101001.
ZhangCLingYZhangX, et al.Ultra-thin carbon fiber reinforced carbon nanotubes modified epoxy composites with superior mechanical and electrical properties for the aerospace field. Compos - A: Appl Sci Manuf2022; 163: 107197.
9.
WangXGaoXZhangZ, et al.Advances in modifications and high-temperature applications of silicon carbide ceramic matrix composites in aerospace: a focused review. J Eur Ceram Soc2021; 41: 4671–4688.
10.
ZhangJLinGVaidyaU, et al.Past, present and future prospective of global carbon fibre composite developments and applications. Compos B Eng2023; 250: 110463.
11.
KambleMVashisthAYangH, et al.Reversing fatigue in carbon-fiber reinforced vitrimer composites. Carbon2022; 187: 108–114.
12.
GuoRLiCNiuY, et al.The fatigue performances of carbon fiber reinforced polymer composites – a review. J Mater Res Technol2022; 21: 4773–4789.
13.
ShokriehM. Multiaxial fatigue behaviour of unidirectional plies based on uniaxial fatigue experiments — I. Modelling. Int J Fatigue1997; 19: 201–207.
14.
ShokriehM. Multiaxial fatigue behaviour of unidirectional plies based on uniaxial fatigue experiments—II. Experimental evaluation. Int J Fatigue1997; 19: 209–217.
15.
KawaiM. A phenomenological model for off-axis fatigue behavior of unidirectional polymer matrix composites under different stress ratios. Compos - A: Appl Sci Manuf2004; 35: 955–963.
16.
FloreDWegenerK. Modelling the mean stress effect on fatigue life of fibre reinforced plastics. Int J Fatigue2016; 82: 689–699.
17.
ShiWHuWZhangM, et al.A damage mechanics model for fatigue life prediction of fiber reinforced polymer composite lamina. Acta Mechanica Solida Sinica2011; 24: 399–410.
D’AmoreAGiorgioMGrassiaL. Modeling the residual strength of carbon fiber reinforced composites subjected to cyclic loading. Int J Fatigue2015; 78: 31–37.
20.
HealeyRWangJWallbrinkC, et al.The application of cycle merging and an extension of a fatigue spectrum simplification methodology from unidirectional to woven composite materials. Compos C: Open Access2022; 8: 100283.
21.
SenthilnathanKHiremathCPNaikNK, et al.Microstructural damage dependent stiffness prediction of unidirectional CFRP composite under cyclic loading. Compos - A: Appl Sci Manu2017; 100: 118–127.
22.
BakerCMorscherGNPujarVV, et al.Transverse cracking in carbon fiber reinforced polymer composites: modal acoustic emission and peak frequency analysis. Compo Sci Technol2015; 116: 26–32.
23.
ÖzaslanEYetginAAcarB, et al.Damage mode identification of open hole composite laminates based on acoustic emission and digital image correlation methods. Compos Struct2021; 274: 114299.
24.
HanWHuKShiQ, et al.Damage evolution analysis of open-hole tensile laminated composites using a progress damage model verified by AE and DIC. Compos Struct2020; 247: 112452.
25.
CuadraJVanniamparambilPAHazeliK, et al.Damage quantification in polymer composites using a hybrid NDT approach. Compo Sci Technol2013; 83: 11–21.
26.
KoohborBMallonSKidaneA, et al.A DIC-based study of in-plane mechanical response and fracture of orthotropic carbon fiber reinforced composite. Compos B Eng2014; 66: 388–399.
27.
KhechaiATatiAGueriraB, et al.Strength degradation and stress analysis of composite plates with circular, square and rectangular notches using digital image correlation. Compos Struct2018; 185: 699–715.
28.
MontesanoJFawazZBougheraraH. Use of infrared thermography to investigate the fatigue behavior of a carbon fiber reinforced polymer composite. Compos Struct2013; 97: 76–83.
29.
GornetLWesphalOBurtinC, et al.Rapid determination of the high cycle fatigue limit curve of carbon fiber epoxy matrix composite laminates by thermography methodology: tests and finite element simulations. Procedia Eng2013; 66: 697–704.
30.
HuangJPastorMLGarnierC, et al.A new model for fatigue life prediction based on infrared thermography and degradation process for CFRP composite laminates. Int J Fatigue2019; 120: 87–95.
31.
SharbaMJ. Fatigue strength prediction of hybrid composites via IR-thermography and energy loss methods. J Ind Text2022; 51: 4184S–4199S.
32.
HariziWChakiSBourseG, et al.Mechanical damage characterization of glass fiber-reinforced polymer laminates by ultrasonic maps. Compos B Eng2015; 70: 131–137.
33.
GarceaSCMavrogordatoMNScottAE, et al.Fatigue micromechanism characterisation in carbon fibre reinforced polymers using synchrotron radiation computed tomography. Compo Sci Technol2014; 99: 23–30.
34.
GarceaSCSinclairISpearingSM. Fibre failure assessment in carbon fibre reinforced polymers under fatigue loading by synchrotron X-ray computed tomography. Compo Sci Technol2016; 133: 157–164.
35.
Nixon-PearsonOJHallettSR. An investigation into the damage development and residual strengths of open-hole specimens in fatigue. Compos - A: Appl Sci Manuf2015; 69: 266–278.
36.
DaiSCunninghamPRMarshallS, et al.Open hole quasi-static and fatigue characterisation of 3D woven composites. Compos Struct2015; 131: 765–774.
37.
YokozekiTAokiYOgasawaraT. Experimental characterization of strength and damage resistance properties of thin-ply carbon fiber/toughened epoxy laminates. Compos Struct2008; 82: 382–389.
38.
AokiRHiguchiRYokozekiT. Progressive damage and residual strength of open-hole thin-ply CFRP laminates under tensile fatigue loading. Compos Struct2023; 314: 116973.
39.
AmacherRCugnoniJBotsisJ, et al.Thin ply composites: experimental characterization and modeling of size-effects. Compo Sci Technol2014; 101: 121–132.
40.
YokozekiTKurodaAYoshimuraA, et al.Damage characterization in thin-ply composite laminates under out-of-plane transverse loadings. Compos Struct2010; 93: 49–57.
41.
CaoYZuoDZhaoY, et al.Experimental investigation on bearing behavior and failure mechanism of double-lap thin-ply composite bolted joints. Compos Struct2021; 261: 113565.
42.
SharifpourFMontesanoJ. A three-dimensional micromechanical model for simulating ply crack formation in laminates under in-plane tensile loading. Composites Part A: Applied Science and Manufacturing2022; 162: 107120.
43.
SaleemMToubalLZitouneR, et al.Investigating the effect of machining processes on the mechanical behavior of composite plates with circular holes. Compos - A: Appl Sci Manu2013; 55: 169–177.
44.
AlhazmiWHAbd-ElhadyAAMousaS, et al.Notch tensile strength of carbon fiber/epoxy composite plate with a center hole under static and cyclic loading. Procedia Struct Integr2019; 17: 292–299.
45.
MaYZhangYSugaharaT, et al.Off-axis tensile fatigue assessment based on residual strength for the unidirectional 45° carbon fiber-reinforced composite at room temperature. Compos - A: Appl Sci Manu2016; 90: 711–723.
46.
MandegarianSSamareh-MousaviSSTaheri-BehroozF. Experimental investigation on in-plane shear fatigue failure criteria of ± 45˚ angle-ply carbon epoxy composite. Int J Fatigue2022; 160: 106873.
47.
Serna MorenoMCHorta MuñozS. Pseudo-ductile effects in ±45° angle-ply CFRP laminates under uniaxial loading: compression and cyclic tensile test. Compos B Eng2022; 233: 109631.
48.
LiYMengJLuoJ, et al.Cryogenic mechanics and damage behaviors of carbon fiber reinforced polymer composites. Compos - A: Appl Sci Manu2023; 169: 107484.
49.
YangMSunWLiW. On transverse strength prediction of unidirectional carbon fiber reinforced polymer composites at elevated temperatures. Compos Commun2023; 40: 101598.
50.
MahmoudiAMohammadiB. Theoretical-experimental investigation of temperature evolution in laminated composites due to fatigue loading. Compos Struct2019; 225: 110972.
51.
FangGGaoXZhangS, et al.A residual strength model for the fatigue strengthening behavior of 2D needled CMCs. Int J Fatigue2015; 80: 298–305.
52.
FangGGaoXYuG, et al.Effect of the stress level on the fatigue strengthening behavior of 2D needled C/SiC CMCs at room temperature. Mater Des2016; 89: 432–438.
53.
LiYXiaoPLiZ, et al.Tensile fatigue behavior of plain-weave reinforced C f/C–SiC composites. Ceram Int2016; 42: 6850–6857.
54.
LiYXiaoPLiZ, et al.Strength evolution of cyclic loaded LSI-based C/C-SiC composites. Ceram Int2016; 42: 14505–14510.
55.
LiYXiaoPLuoH, et al.Fatigue behavior and residual strength evolution of 2.5D C/C-SiC composites. J Eur Ceram Soc2016; 36: 3977–3985.
56.
EftekhariMFatemiA. On the strengthening effect of increasing cycling frequency on fatigue behavior of some polymers and their composites: experiments and modeling. Int J Fatigue2016; 87: 153–166.
57.
PegorinFPingkarawatKMouritzAP. Mixed-mode I/II delamination fatigue strengthening of polymer composites using z-pins. Compos B Eng2017; 123: 219–226.
58.
ShabaniPTaheri-BehroozFSamareh-MousaviSS, et al.Very high cycle and gigacycle fatigue of fiber-reinforced composites: a review on experimental approaches and fatigue damage mechanisms. Prog Mater Sci2021; 118: 100762.
59.
BrunbauerJPinterG. On the strain measurement and stiffness calculation of carbon fibre reinforced composites under quasi-static tensile and tension-tension fatigue loads. Polym Test2014; 40: 256–264.
60.
SarkaniSMichaelovGKihlDP, et al.Comparative study of nonlinear damage accumulation models in stochastic fatigue of FRP laminates. J Struct Eng2001; 127: 314–322.
61.
ReifsniderKStinchcombWO’BrienT. Frequency effects on a stiffness-based fatigue failure criterion in flawed composite specimens. Fatigue Filamentary Compos Mat. 1977; 636: 171–184.