Our developed accelerated testing methodology (ATM) based on matrix resin viscoelasticity for the long-term life prediction of carbon fiber reinforced plastics (CFRP) was applied to assess the statistical prediction of long-term creep failure time of a carbon fiber/polypropylene unidirectional (CF/PP) laminates under creep bending load. Results show that the statistical long-term creep failure times under an arbitrary constant bending load and temperature for the CF/PP laminates can be easily predicted from the statistical static strengths of the CF/PP laminates measured at several temperatures and the viscoelasticity of matrix PP.
ReifsniderKCaseSDuthoitJ. The mechanics of composite strength evolution. Composites Sci Technology2000; 60: 2539–2546.
3.
André LavoirJReifsniderKLRenshawAJ, et al.Prediction of stress-rupture life of glass/epoxy laminates. Int J Fatigue2000; 22: 467–480.
4.
PatelSCaseSW. Durability of a graphite/epoxy woven composite under combined hygrothermal conditions. Int J Fatigue2000; 22: 809–820.
5.
McBagonluriFGarciaKHayesM, et al.Characterization of fatigue and combined environment on durability performance of glass/vinyl ester composite for infrastructure applications. Int J Fatigue2000; 22: 53–64.
6.
CaprinoG. Predicting fatigue life of composite laminates subjected to tension-tension fatigue. J Compos Mater2000; 34: 1334–1355.
7.
SchaffJRDavidsonBD. Life prediction methodology for composite structures. Part I - constant amplitude and two-stress level fatigue. J Compos Mater1997; 31: 128–157.
8.
SchaffJRDavidsonBD. Life prediction methodology for composite structures. Part II - spectrum fatigue. J Compos Mater1997; 31: 158–181.
9.
BondIP. Fatigue life prediction for GRP subjected to variable amplitude loading. Compos Part A1999; 30: 961–970.
10.
BondIFarrowIR. Fatigue life prediction under complex loading for XAS/914 CFRP incorporating a mechanical fastener. Int J Fatigue2000; 22: 633–644.
11.
KlemencJFajdigaM. Description of statistical dependencies of parameters of random load states (dependency of random load parameters). Int J Fatigue2000; 22: 357–367.
12.
TovoR. A damage-based evaluation of probability density distribution for rain-flow ranges from random processes. Int J Fatigue2000; 22: 425–429.
13.
YaoWXHimmelN. A new cumulative fatigue damage model for fibre-reinforced plastics. Composites Sci Technol2000; 60: 59–64.
14.
CarmineRHimmelN. Life prediction for continuous fiber reinforced composites under stochastic fatigue loading based on the critical element concept. In: CardonAHFukudaHReifsniderK (eds). Progress in Durability Analysis of Composite Systems. Rotterdam, The Netherlands: Balkema; 1998, pp. 319–324.
15.
HimmelN. Fatigue life prediction of laminated polymer matrix composites. Int J Fatigue2002; 24: 349–360.
16.
PhilippidisTPVassilopoulosAP. Fatigue of composite laminates under off-axis loading. Int J Fatigue1999; 21: 253–262.
17.
PhilippidisTPVassilopoulosAP. Fatigue design allowables for GRP laminates based on stiffness degradation measurements. Compos Sci Technol2000; 60: 2819–2828.
18.
AgfajaniSHematiMTorabniaS. Life prediction of wind turbine blades using multi-scale damage model. J Reinforc Plastics Compos2021; 40: 644–653.
19.
ShokriehMMLessardLB. Progressive fatigue damage modeling of composite materials, part I: modeling. J Compos Mater2000; 34: 1056–1080.
20.
ShokriehMMLessardLB. Progressive fatigue damage modeling of composite materials, part II: material characterization and model verification. J Compos Mater2000; 34: 1081–1116.
21.
LeeC-HJenM-HR. Fatigue response and modelling of variable stress amplitude and frequency in AS-4/PEEK composite laminates, part 1: experiments. J Compos Mater2000; 34: 906–929.
22.
LeeC-HJenM-HR. Fatigue response and modelling of variable stress amplitude and frequency in AS-4/PEEK composite laminates, part 2: analysis and formulation. J Compos Mater2000; 34: 930–953.
23.
BeheshtyMHHarrisB. A constant-life model of fatigue behaviour for carbon-fiber composites: the effect of impact damage. Compos Sci Tech1998; 58: 9–18.
24.
BeheshtyMHHarrisBAdamT. An empirical fatigue-life model for high-performance fiber composites with and without impact damage. Compos Part A1999; 30: 971–987.
25.
RotemANelsonHG. Failure of a laminated composite under tension-compression fatigue loading. Compos Sci Tech1989; 36: 45–62.
26.
PetermannJPlumtreeA. A unified fatigue failure criterion for unidirectional laminates. Compos Part A2001; 32: 107–118.
27.
SchönJ. Model for predicting the load ratio for the shortest fatigue life. Compos Sci Technol2001; 61: 1143–1149.
28.
KawaiMYajimaSHachinoheA, et al.High-temperature off-axis fatigue behaviour of unidirectional carbon-fiber-reinforced composites with different resin matrices. Compos Sci Tech2001; 61: 1285–1302.
29.
KawaiMYajimaSHachinoheA, et al.Off-axis fatigue behavior of unidirectional carbon fiber-reinforced composites at room and high temperatures. J Compos Mater2001; 35: 545–576.
SullivanJL. Creep and physical aging of composites. Compos Sci Tech1990; 39: 207–232.
32.
GatesTS. Experimental characterization of nonlinear, rate dependent behavior in advanced polymer matrix composites. Exp Mech1992; 32: 68–73.
33.
KawaiMYagihashiYHoshiH, et al.Anisomorphic constant fatigue life diagrams for quasi-isotropic woven fabric carbon/epoxy laminates under different hygro-thermal environments. Adv Compos Mater2013; 22: 79–98.
34.
Rojas-SanchezJFSchmackTBoeslB, et al.Strain rate-dependent characterization of carbon fibre-reinforced composite laminates using four-point bending tests. J Reinforc Plastics Compos2020; 39: 165–174.
35.
AlamPMamalisDRobertC, et al.The fatigue of carbon fibre reinforced plastics – A review. Compos Part B2019; 166: 555–579.
36.
MouradAHIIdrisiAHIWrageMC, et al.Long-term durability of thermoset composites in seawater environment. Compos Part B2019; 168: 243–253.
37.
LiHZhangKFanX, et al.Effect of seawater ageing with different temperatures and concentrations on static/dynamic mechanical properties of carbon fiber reinforced polymer composites. Compos Part B2019; 173: 106910.
38.
NashNHPortelaABachour-SirerolCI, et al.Effect of environmental conditioning on the properties of thermosetting- and thermoplastic-matrix composite materials by resin infusion for marine applications. Compos Part B2019; 177: 107271.
39.
AlmudaiheshFHolfordKPullinR, et al.The influence of water absorption on unidirectional and 2D woven CFRP composites and their mechanical performance. Compos Part B2020; 182: 107626.
40.
MiyanoYNakadaMCaiH. Formulation of long-term creep and fatigue strengths of polymer composites based on accelerated testing methodology. J Compos Mater2008; 42: 1897–1919.
41.
NakadaMMiyanoY. Formulation of time- and temperature-dependent strength of unidirectional carbon fiber reinforced plastics. J Compos Mater2013; 47: 1897–1906.
42.
NakadaMMiyanoY. Advanced accelerated testing methodology for long-term life prediction of CFRP laminates. J Compos Mater2015; 49: 163–175.
43.
ChristensenRMiyanoY. Stress intensity controlled kinetic crack growth and stress history dependent life prediction with statistical variability. Int J Fracture2006; 137: 77–87.
44.
ChristensenRMMiyanoY. Deterministic and probabilistic lifetime from kinetic crack growth-generalized forms. Int J Fracture2007; 143: 35–39.
45.
MiyanoYNakadaM. Durability of fiber-reinforced polymers. Weinheim, Germany: Wiley-VCH, 2018.
46.
NakadaMMiyanoYKagetaS, et al.Prediction of statistical life time for unidirectional CFRTP under cyclic loading. J Reinforc Plastics Compos2021; 40: 749–758.
47.
NakadaMMiyanoYKagetaS, et al.Prediction of statistical life time for unidirectional CFRTP under water absorption. J Reinforc Plastics Compos2021; 38(19–20): 073168441985421. DOI: 10.1177/07316844211051735
48.
NakadaMMiyanoYMorisawaY, et al.Statistical life prediction of unidirectional carbon fiber/polypropylene tape under creep tension load. J Reinforc Plastics Compos2020; 39: 278–284.
49.
MiyanoYNakadaMYoshikoshiY. Statistical creep failure time of unidirectional CFRP under bending load. J Compos Mater2016; 56: 653–658.
50.
International and National Patent Collections. JP WO2016/114352 Reinforcing Fiber Bundle and Carbon Fiber-Reinforced Thermoplastic Resin Molded Article, and Method for Manufacturing Reinforcing Fiber Bundle. Minato, Japan: Mitsui Chemicals Inc.
51.
MiyanoYNakadaMKagetaS, et al.Determination of long-term viscoelastic coefficient of epoxy resin. Mater Syst2021; 38: 7–10.
52.
ChristensenRM. Theory of Viscoelasticity. 2nd ed.Mineola, NY: Dover Publications, Inc., 1982.
53.
NakadaMMiyanoYCaiH, et al.Prediction of long-term viscoelastic behavior of amorphous resin based on the time-temperature superposition principle. Mech Time-Depend Mater2011; 15: 309–316.