Hot water extractives, solvent extractives and both hot water and solvent extractives were eliminated from different wood species via Soxhlet extraction. Different wood–linear low density polyethylene (LLDPE) composites were prepared using 10% wood and 7% poly(ethylene-co-vinyl alcohol) as a compatibilizer. A comparison of the mechanical properties, water absorption behaviour and resistance to UV radiation between composites filled with unextracted wood and composites filled with the same species but without the above extractives were carried out. The results illustrated that there are several distinct benefits and drawbacks when using wood without extractives as a filler. Unextracted wood produced composites with better mechanical properties and resistance to UV radiation, while extracted wood led to composites with lower water absorption rates. Using wood without both hot water and solvent extractives as a filler caused the largest reduction in mechanical properties, UV resistance and water absorption rate, compared to composites made with wood where only one extractive component was removed.
CaraschiJLeãoA. Woodflour as reinforcement of polypropylene. Mater Res2002; 5: 405–409.
2.
KimJPYoonTHMunSP. Wood–polyethylene composites using ethylene–vinyl alcohol copolymer as adhesion promoter. Bioresour Technol2006; 97: 494–499.
3.
NdiayeDFantonETheriasSM. Durability of wood polymer composites: influence of wood on the photochemical properties. Compos Sci Technol2008; 68: 2779–2784.
4.
AshoriABahreiniZ. Evaluation of Calotropis gigantea as a promising raw materials for fiber-reinforced composite. J Comp Mat2009; 34: 1297–1304.
WuRWangYXiaoQ. Green composite films prepared from cellulose, starch and lignin in room-temperature ionic liquid. Bioresour Technol2009; 100: 2569–2574.
7.
AshoriA. Wood plastic composites as promising green-composites for automotive industries. Bioresour Technol2008; 99: 4661–4667.
8.
PandeyKK. A note on the influence of extractives on the photo-discoloration and photo-degradation of wood. Polym Degrad Stabil2005; 87: 375–379.
9.
ZhangXNguyenDPaiceM. Degradation of wood extractives in thermo-mechanical pulp by soybean lipoxygenase. Enzyme Microb Tech2007; 40: 866–873.
10.
DoradoJClaassenFWVan BeekTA. Elimination and detoxification of softwood extractives by white-rot fungi. J Biotech2000; 80: 231–240.
11.
KallioinenAVaariARattoM. Effects of bacterial treatments on wood extractives. J Biotech2003; 103: 67–76.
12.
IshidaYGotoKYokoiH. Direct analysis of phenolic extractives in wood by thermochemolysis-gas chromatography in the presence of tetrabutylammonium hydroxide. J Anal Appl Pyrol2007; 78: 200–206.
13.
HillisWE. Formation and properties of some wood extractives. Phytochemistry1972; 11: 1207–1218.
14.
NachtigallSMCerveiraGSRosaSM. New polymeric-coupling agent for polypropylene/wood-flour composites. Polym Test2007; 26: 619–628.
15.
De MeijerMHaemersSCobbenW. Surface energy determinations of wood: comparison of methods and wood species. Langmuir2000; 16: 9352–9359.
16.
WangSZhangA. Chemical characterization of smoke from the production of wood-polymer composites. Forest Stud China2007; 9: 57–62.
17.
ShebaniANvan ReenenAJMeinckenM. The effect of wood extractives on the thermal stability of different wood species. Thermochim Acta2008; 471: 43–50.
18.
ShebaniANvan ReenenAJMeinckenM. The effect of wood extractives on the thermal stability of different wood-LLDPE composites. Thermochim Acta2009; 481: 52–56.
19.
TAPPI Test Methods. T 264 om-88 and T 222 om-88. Preparation of wood for chemical analysis. 1992–1993.
20.
ChoongETAchmadiSS. Effect of extractives on moisture sorption and shrinkage in tropical woods. Wood Fiber Sci1991; 23: 185–196.
21.
ShebaniANvan ReenenAJMeinckenM. The effect of wood species on the mechanical and thermal properties of wood-LLDPE composites. J Comp Mat2009; 43: 1305–1318.
22.
AshoriANourbakhshA. Reinforced polypropylene composites: effects of chemical compositions and particle size. Bioresour Technol2010; 101: 2515–2519.
23.
MarkHGaylordNBikalesN. Encyclopedia of polymer science and technology. Vol 15, 1st edn. New York, USA: John Wiley & Sons, 1970, pp. 22–30.
24.
RowellR. The chemistry of solid wood. 1st edn. Washington, USA: American Chemical Society, 1984, p. 73.
25.
PejicBKostiMSkundricP. The effects of hemicelluloses and lignin removal on water uptake behavior of hemp fibers. Bioresour Technol2008; 99: 7152–7159.
26.
WanJRWangXLiF. Effects of hemicellulose removal on cellulose fiber structure and recycling characteristics of eucalyptus pulp. Bioresour Technol2010; 101: 4577–4583.
27.
IwamotoSAbeKYanoH. The effect of hemicelluloses on wood pulp nanofibrillation and nanofiber network characteristics. Biomacromolecules2008; 9: 1022–1226.
28.
NaddeoCGuadagnLVittoriaV. Photooxidation of spherilene linear low-density polyethylene films subjected to environmental weathering: changes in mechanical properties. Polym Degrad Stabil2004; 85: 1009–1013.
29.
LiuMHorrocksAR. Effect of carbon black on UV stability of LLDPE films under artificial weathering conditions. Polym Degrad Stabil2002; 75: 485–499.
30.
AllenNSKatamiH. Comparison of various thermal and photoageing conditions on the oxidation of titanium dioxide pigmented linear low density polyethylene films. Polym Degrad Stabil1996; 52: 311–320.
31.
RoyPKTitusSSurekhaP. Degradation of abiotically aged LDPE films containing pro-oxidant by bacterial consortium. Polym Degrad Stabil2008; 93: 1917–1922.
32.
BasfarAAAliKM. Comparative study of photodegradation of wood by a UV laser and a xenon light source. Polym Degrad Stabil2006; 91: 437–443.
33.
PandeyKKVuorinenT. Comparative study of photodegradation of wood by a UV laser and a xenon light source. Polym Degrad Stabil2008; 93: 2138–2146.
34.
StarkNMMatuanaLM. Influence of photostabilizers on wood flour–HDPE composites exposed to xenon-arc radiation with and without water spray. Polym Degrad Stabil2006; 91: 3048–3056.