In this article, the effects of ply thickness on the impact damage mechanisms in CFRP laminates are discussed based on the experimental observations. Quasi-isotropic CFRP laminates were manufactured using 38 µm thick thin-ply prepregs. Impact damage inside the laminates was evaluated by using ultrasonic scanning and sectional fractography. Compression after impact strength was also evaluated. Thin-ply laminates showed 23% higher strength than standard-ply laminates. Transverse cracks decreased drastically in thin-ply laminates, and localized delamination was largely extended. Based on the discussions in our previous study and the literature, the specific ply thickness without drastic crack propagation appears to be less than or equal to 40 µm. Therefore, the thin laminates showed few and localized transverse cracks and delamination was largely propagated in the midplane.
Guynn EG and Obrien TK. The influence of lay-up and thickness on composite impact damage and compression strength. In: Structures, Structural Dynamics, and Materials Conference, 26th, Orlando, FL, 1985, pp. 187–196.
2.
CantwellWMortonJ. The influence of varying projectile mass on the impact response of CFRP. Compos Struct1989; 13(2): 101–114.
3.
ClarkG. Modelling of impact damage in composite laminates. Composites1989; 20(3): 209–214.
ChoiH-YChangF-K. A model for predicting damage in graphite/epoxy laminated composites resulting from low-velocity point impact. J Compos Mater1992; 26(14): 2134–2169.
6.
KwonYSBhavaniVSankarB. Indentation-flexure and low-velocity impact damage in graphite epoxy laminates. J Compos Technol Res1993; 15(2): 101–111.
7.
IshikawaTSugimotoSMatsushimaMHayashiY. Some experimental findings in compression-after-impact (CAI) tests of CF/PEEK (APC-2) and conventional CF/epoxy flat plates. Compos Sci Technol1995; 55(4): 349–363.
8.
DaviesGAOZhangX. Impact damage prediction in carbon composite structures. Int J Impact Eng1995; 16(1): 149–170.
9.
HitchenSKempR. The effect of stacking sequence on impact damage in a carbon fibre/epoxy composite. Compos1995; 26(3): 207–214.
10.
BiboGAHoggJ. The role of reinforcement architecture on impact damage mechanisms and post-impact compression behaviour. J Mater Sci1996; 31(5): 1115–1137.
11.
ScarponiC. Ultrasonic technique for the evaluation of delaminations on CFRP, GFRP, KFRP composite materials. Compos Part B: Eng2000; 31(3): 237–243.
12.
HouJPetrinicNRuizCHallettSR. Prediction of impact damage in composite plates. Compos Sci Technol2000; 60(2): 273–281.
13.
JohnsonAFPickettAKRozycki. Computational methods for predicting impact damage in composite structures. Compos Sci Technol2001; 61(15): 2183–2192.
BouvetCCastaniéBBizeulMBarrauJ-J. Low velocity impact modelling in laminate composite panels with discrete interface elements. Int J Solids Struct2009; 46(14–15): 2809–2821.
16.
LalKM. Residual strength assessment of low velocity impact damage of graphite-epoxy laminates. J Reinfor Plast Compos1983; 2(4): 226–238.
17.
PavierMClarkeM. Experimental techniques for the investigation of the effects of impact damage on carbon-fibre composites. Compos Sci Technol1995; 55(2): 157–169.
18.
KimparaIKageyamaKSuzukiTOhsawaI. Simplified and unified approach to characterization of compressive residual strength of impact-damaged CFRP laminates. Key Eng Mater1997; 141–143: 19–34.
19.
HawyesVCurtisPSoutisC. Effect of impact damage on the compressive response of composite laminates. Compos Appl Sci Manuf2001; 32(9): 1263–1270.
20.
CartieDIrvingX. Effect of resin and fibre properties on impact and compression after impact performance of CFRP. Compos Appl Sci Manuf2002; 33(4): 483–493.
21.
SanchezsaezSBarberoEZaeraRNavarroC. Compression after impact of thin composite laminates. Compos Sci Technol2005; 65(13): 1911–1919.
22.
ParviziABaileyJE. On multiple transverse cracking in glass fibre epoxy cross-ply laminates. J Mater Sci1978; 13(10): 2131–2136.
23.
CrossmanFWWarrenWJWangASDLawGE. Initiation and growth of transverse cracks and edge delamination in composite laminates Part 2. Experimental correlation. J Compos Mater1980; 14(1): 88–108.
24.
KimRYSoniSR. Experimental and analytical studies on the onset of delamination in laminated composites. J Compos Mater1984; 18(1): 70–80.
25.
Kawabe K, Tomoda S and Matsuo T. A pneumatic process for spreading reinforcing fiber tow. In: The 42nd International SAMPE Symposium & Exhibition, Anaheim, CA, May 4–8, 1997, pp. 65–76.
26.
SasayamaHKawabeKTomodaSOhsawaIKageyamaKOgataN. Effect of lamina thickness on first ply failure in multidirectionally laminated composites. In: The 8th Japan International SAMPE Symposium & Exhibition (JISSE-8). Japan: Tokyo, 2003, pp. 18–21.
27.
Tsai SW, Sihn S and Kim RY. Thin ply composites. In: Collection of Technical Papers - AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics and Materials Conference, Vol. 4, AIAA/ASME/ASCE/AHS/ASC, Austin, TX, 2005, pp. 2555–2559.
KawabeKSasayamaHTomodaS. New carbon fiber tow-spread technology and applications to advanced composite materials. SAMPE J2009; 45(2): 6–17.
30.
NishikawaYOkuboKFujiiTKawabeK. Fatigue crack constraint in plain-woven CFRP using newly–developed spread tows. Int J Fatigue2006; 28(10): 1248–1253.
31.
YokozekiTAokiYOgasawaraT. Experimental characterization of strength and damage resistance properties of thin-ply carbon fiber/toughened epoxy laminates. Compos Struct2008; 82(3): 382–389.
32.
Morita M, Saito H, Tanaka M and Kimpara I. Clarification of impact damage morphology in Thin-Ply CFRP laminate. In: Proceedings of 11th Japan International SAMPE Symposium, November 25–27, Tokyo, Japan, AM-1 – 2, 2009.
33.
GaoSLKimJK. Three-dimensional characterization of impact damage in CFRPs. Key Eng Mater1998; 141–143: 35–54.
34.
ZhangXDaviesGAOHitchingsD. Impact damage with compressive preload and post-impact plates of carbon composite compression. Int J Impact Eng1999; 22(5): 485–509.
35.
Takeuchi H, Saito H and Kimpara I. Restraining effects of transverse cracking in 90° layer of Thin-ply CFRP cross-ply laminates. In: Proceedings of 7th Asian-Australasian Conference on Composite Material (ACCM-7), Taipei, Taiwan, WED-SE25-06 (CD-ROM), 2010.
36.
YokozekiTAokiTIshikawaT. Transverse crack propagation in the specimen width direction of CFRP laminates under static tensile loadings. J Compos Mater2002; 36(17): 2085–2099.