Aerogel: a potential three-dimensional nanoporous filler for resins

Abstract

Considering its special microstructure and unique properties, silica aerogel was chosen as three-dimensional (3D) nanoporous filler for epoxy resin in this paper. Pure epoxy resin (0 wt%), 0.1 wt%, 1 wt%, 5 wt%, 10 wt%, and 100 wt% (pure silica aerogel) aerogel/epoxy composites were fabricated and then characterized by dynamic mechanical analyzer (DMA) and field emission scanning electron microscope. The results showed that small amount of filler efficiently increased the stiffness of the composites, but the stiffness decreased with the increase of the mass fraction of the aerogel in the composites (composites ratio); the glass transition temperature of the composites substantially increased, compared to pure epoxy resin. Also, the compressive modulus of the composites at glassy state, rubbery state, and hardening state were studied, respectively. At last, the effects which presumably affect the properties of aerogel/epoxy composites were discussed. Anchoring effect and interfacial effect were suggested to explain the thermal—mechanical behaviors of the composites with different composite ratio.

Keywords

aerogel filler epoxy thermomechanical nanoporous three-dimensional

Get full access to this article

View all access options for this article.

References

Pierre AC and Pajonk GM Chemistry of aerogels and their applications. Chem Rev 2002; 102: 4243-4266.

Schaefer DW and Keefer KD Structure of random porous materials: silica aerogel. Phys Rev Lett 1986; 56: 2199-2202.

Hüsing N. and Schubert U. Aerogel-airy materials: chemistry, structure, and properties. Adv Mater 2007; 37: 22-45.

Du A. , Zhou B. , Shen J. , Xiao S. , Zhang Z. , Liu C. and Zhang M. Monolithic copper oxide aerogel via dispersed inorganic sol-gel method . J Non-Cryst Solids 2009; 355: 175-181.

Du A. , Zhou B. , Zhong Y. , Zhu X. , Gao G. , Wu G. , Zhang Z. and Shen J. Hierarchical microstructure and formative mechanism of low-density molybdena-based aerogel derived from MoCl5. J Sol-Gel Sci Technol 2011; 58: 225-231. Doi: 10.1007/s10971-010-2381-8.

Ren H. , Zhang L. , Shang C. , Wang X. and Bi Y. Synthesis of a low-density tantalum oxide tile-like aerogel monolithic . J Sol-Gel Sci Technol 2010; 53: 307-311.

Du A. , Zhou B. , Shen J. , Gui J. , Zhong Y. , Liu C. , Zhang Z. and Wu G. A versatile sol-gel route to monolithic oxidic gels via polyacrylic acid template . New J Chem 2011; 35: 1096-1102. Doi: 10.1039/c0nj00909a.

Bag S. , Trikalitis PN , Chupas PJ , Armatas GS and Kanatzidis MG Porous semiconducting gels and aerogels from chalcogenide clusters . Science 2007; 317: 490-493.

Shen J. , Hou J. , Guo Y. , Xue H. , Wu G. and Zhou B. Microstructure control of RF and carbon aerogels prepared by sol-gel process . J Sol-Gel Sci Technol 2005; 36: 131-136.

10.

Leventis N. , Sadekar A. , Chandrasekaran N. and Sotiriou-Leventis C. Click synthesis of monolithic silicon carbide aerogels from polyacrylonitrile-coated 3 d silica networks. Chem Mater 2010; 22: 2790-2803.

11.

Aliev AE , Oh J. , Kozlov ME , Kuznetsov AA , Fang S. , Fonseca AF , et al. Giant-stroke, superelastic carbon nanotube aerogel muscles. Science 2009; 323: 1575-1578.

12.

Worsley MA , Pauzauskie PJ , Olson TY , Biener J. , Satcher JH and Baumann TF Synthesis of graphene aerogel with high electrical conductivity. J Am Chem Soc 2010; 132: 14067-14069.

13.

Hassan S. , Hector AL , Hyde JR , Kalaji A. and Smith DC A non-oxide sol-gel route to synthesise silicon imidonitride monolithic gels and high surface area aerogel. Chem Commun 2008; 42: 5304-5306.

14.

Wagh PB , Begag R. , Pajonk GM , Rao AV and Haranath D. Comparison of some physical properties of silica aerogel monoliths synthesized by different precursors. Mater Chem Phys 1999 ; 57: 214-218.

15.

Deng Z. , Wang J. , Wu A. , Shen J. and Zhou B. High strength SiO2 aerogel insulation. J Non-Cryst Solids 1998; 225: 101-104.

16.

Meador MAB , Weber AS , Hindi A. , Naumenko M. , McCorkle L. , Quade D. , et al. Structure-property relationships in porous 3 d nanostructures: epoxy-cross-linked silica aerogels produced using ethanol as the solvent. ACS Appl Mater Interfaces 2009; 1: 894-906.

17.

Kanamori K. , Aizawa M. , Nakanishi K. and Hanada T. New transparent methylsilsesquioxane aerogels and xerogels with improved mechanical properties . Adv Mater 2007; 19: 1589-1593.

18.

Russo RE and Hunt AJ Comparison of ethyl versus methyl sol-gels for silica aerogels using polar nephelometry. J Non-Cryst Solids 1986 ; 86: 219-230.

19.

Sun Y. , Zhang Z. , Moon KS and Wong CP Glass transition and relaxation behavior of epoxy nanocomposites. J Polym Sci B 2004; 42: 3849-3858.

20.

Park JH and Jana SC The relationship between nanoand micro-structures and mechanical properties in PMMA-epoxy-nanoclay composites. Polymer 2003; 44: 2091-2100.

21.

Kinloch AJ , Mohammed RD , Taylor AC , Eger C. , Sprenger S. and Egan D. The effect of silica nano particles and rubber particles on the toughness of multiphase thermosetting epoxy polymers. J Mater Sci 2005; 40: 5083-5086.

22.

Zhang H. , Tang LC , Zhang Z. , Friedrich K. and Sprenger S. Fracture behaviours of in situ silica nanoparticle-filled epoxy at different temperatures. Polymer 2008; 49: 3816-3825.