Effects of temperature,seawater and impact on the strength,stiffness,and life of sandwich composites

Abstract

A study was conducted to determine the effects of subzero temperatures, seawater saturation, and low velocity impact on the flexural strength, stiffness, and life of sandwich composites. Specimens were tested statically and in fatigue using a four-point bending arrangement that included a combined metal and rubber load pad that spanned the inner loading heads and which prevented any local crushing damage. Both undamaged and impact damaged specimens were tested in room temperature (RT) dry, RT seawater saturated, -20°C dry, and -20°C seawater saturated environments. The impact energy level was chosen to produce damage that was observable, yet did not produce excessive permanent deformation. The primary results were that reducing the temperature tended to increase stiffness, strength, and fatigue life. Seawater saturation had minimal effects on strength, stiffness, or life, but influenced the static failure mode. Impact damage had little effect on the static results, but caused a significant loss in fatigue life. These results demonstrate that static test results cannot be used to infer fatigue behaviors, and indicate the need for the accurate determination of material and structural responses across the full range of expected usage environments.

Keywords

sandwich composite temperature moisture seawater impact fatigue

Get full access to this article

View all access options for this article.

References

Vinson JR Sandwich structures. Appl Mech Rev 2001; 54(3): 201 214.

Sharma N. , Gibson RF and Ayorinde EO Fatigue of foam and honeycomb core composite sandwich structures: a tutorial . J Sandwich Struct Mater 2006; 8(4): 263 319.

Miyano Y. and Nakada M. Accelerated testing for long-term durability of various FRP laminates for marine use. In: Daniel IM , Gdoutos EE and Rajapakse YDS (eds) Major accomplishments in composite materials and sandwich structures - an anthology of ONR sponsored research. New York: Springer, 2010, pp.3 25.

Soni MS , Gibson RF and Ayorinde EA Characterization of fatigue behavior of composite sandwich structures as sub-zero temperatures. In: Daniel IM , Gdoutos EE and Rajapakse YDS (eds) Major accomplishments in composite materials and sandwich structures - an anthology of ONR sponsored research. New York: Springer, 2010, pp.605 624.

Burman M. and Zenkert D. Fatigue of foam core sandwich beams, Part I: undamaged specimens. Int J Fatig 1997; 19(7): 551 561.

Burman M. and Zenkert D. Fatigue of foam core sandwich beams, Part II: effect of initial damages. Int J Fatig 1997; 19(7): 563 578.

Kulkarni N. , Mahfuz H. , Jeelani S. and Carlsson L. Fatigue crack growth and life prediction of foam core sandwich composites under flexural loading. Compos Struct 2003 ; 59: 499 505.

Bing Q. and Davidson BD An improved methodology for measuring the interfacial toughness of sandwich beams. In: Daniel IM , Gdoutos EE and Rajapakse YDS (eds) Major accomplishments in composite materials and sandwich structures - an anthology of ONR sponsored research. New York: Springer, 2010, pp.365 380.

Shipsha A. and Zenkert D. Fatigue behaviour of foam core sandwich beams with sub-interface impact damage . J Sandwich Struct Mater 2003; 5(1): 147 160.

10.

Smith SA , Emmanwori LL , Sadler RL and Shivakumar KN Evaluation of composite sandwich panels fabricated using vacuum assisted resin transfer molding. In: Proceedings of SAMPE 2000 , Long Beach, CA, 21 25 May, 2000.

11.

Kanny K. , Mahfuz H. , Thomas T. and Jeelani S. Temperature effects on the fatigue behavior of foam core sandwich structures . Polym Polym Compos 2004; 12(7): 551 559.