Epoxy resin was modified with polyurethane having different isocyanate index. Impact strength, tensile strength, elongation at break and flexural strength were estimated as functions of polyurethane content and isocyanate index. Hardness, linear expansion coefficient and the deflection temperature under load were estimated for selected compositions. Infrared spectroscopy was carried out for unmodified epoxy resin and compositions with improved mechanical properties. Maximum improvement in the fracture toughness was reached with polyurethane with highest content of isocyanate. Hardness was not affected but elastic modulus decreased, implying a softening of epoxy-based compositions. The infrared spectra indicated that an excess of isocyanate groups leads to a grafting process between the modifier and the matrix, explaining the toughening of the latter.
Lange, F.F. and Radford, K.C. ( 1971). Fracture Energy of an Epoxy Composite System, J. Mater. Sci., 6: 1197-1203.
2.
Spanoudakis, J. and Young, R.J. (1984). Crack Propagation in a Glass Particle-Filled Resin, J. Mater. Sci., 19: 487-496.
3.
Chikhi, N., Fellahi, S. and Bakar, M. ( 2002). Modification of Epoxy Resin with Kaolin, Eur. Polym. J., 38: 251-264.
4.
Kinloch, A.J. , Shaw, S.J., Tod , D.A. and Hunston, D.L. (1983). Deformation and Fracture Behaviour of a Rubber-Toughened Epoxy. I. Microstructure and Fracture Studies, Polymer, 24: 1341-1354.
5.
Sanjana, Z.N. and Kupchella, L. (1985). Dynamic Mechanical Analysis of Rubber Toughened Epoxy Resins, Polym. Eng. Sci. , 25: 1148-1154.
6.
Bartlet, P., Pascault, J.P. and Sautereau, H. ( 1985). Relationships Between Structure and Mechanical Properties of Rubber-Modified Epoxy Networks Cure with Dicyanodiamide Hardener , J. Appl. Polym. Sci., 30: 2955-2966.
7.
Kalfoglou, N.K. and Williams, H.L. (1973). Dynamic Mechanical Properties of Epoxy-Rubber Blends, J. Appl. Polym. Sci., 17: 1377-1386.
8.
Pearson, R.A. and Yee, A.F. (1991). Influence of Particle Size and Particle Size Distribution on Toughening Mechanisms in Rubber-Modified Epoxies, J. Mater. Sci., 26: 3828-3844.
9.
Kunz, S.C., Sayre, J.A. and Assink, R.A. ( 1982). Morphology and Toughness Characterization of Epoxy Resins Modified with Amine and Carboxyl Terminated Rubbers, Polymer , 23: 1897-1906.
10.
Levita, G., Marchetti, A. and Butta, E. ( 1985). Influence of the Temperature of Cure on the Mechanical Properties of ATBN/Epoxy Blends, Polymer, 26: 1110-1116.
11.
Chikhi, N., Fellahi, S. and Bakar, M. ( 2002). Modification of Epoxy Resin using Reactive Liquid (ATBN) Rubber, Eur. Polym. J., 38: 251-264.
12.
Sankaran, S. and Chanda, M. ( 1990). Chemical Toughening of Epoxies. II. Mechanical, Thermal and Microscopic Studies of Epoxies Toughened with Hydroxyl-Terminated Po(butadiene-co-acrylonitrile) , J. Appl. Polym. Sci., 39: 1635-1647.
13.
Verchere, D. , Pascault, J.P., Sautereau, H., Moschiar, S.M., Riccardi, C.C. and Williams, R.J.J. ( 1991). Rubber-Modified Epoxies. IV. Influence of Morphology on Mechanical Properties, J. Appl. Polym. Sci., 43: 293-304.
14.
Hwang, J.F. , Manson, J.A., Hertzberg, R.W., Miller, G.A. and Sperling, J.H. ( 1989). Structure-Property Relationships in Rubber Toughened Epoxies, Polym. Eng. Sci. , 29: 1466-1476.
15.
Hedrick, J.L. , Yilgor, I., Wilkes , G.L. and McGrath, J.E. (1985). Chemical Modification of Matrix Resin Networks with Engineering Thermoplastics, Polym. Bull., 13: 201-208.
16.
Bucknal, C.B. and Partridge, I.K. (1983). Phase Separation in Epoxy Resins Containing Polyethersulphone, Polymer, 24: 639-644.
17.
Hourston, D.J. , Lane, J.M. and MacBeath, N.A. (1991). Toughening of Epoxy Resins with Thermoplastics II. Tetrafunctional Epoxy-Polyetherimide Blends, Polym. Intern., 26: 17-21.
18.
Rong, M. and Zeng, H. ( 1997). Polycarbonate-Epoxy Semi-Interpenetrating Polymer Network 2. Phase Separation and Morphology, Polymer, 38: 269-277.
19.
Frisch, H.L. , Frisch, K.C. and Klempner, D. (1974). Glass Transitions of Topologically Interpenetrating Polymer Networks, Polym . Eng. Sci., 14: 646-650.
20.
Raymond, M.P. and Bui, V.T. (1998). Epoxy/Castor Oil Graft Interpenetrating Polymer Networks, J. Appl. Polym. Sci., 70: 1649-1659.
21.
Bussi, P. and Ishida, H. ( 1994). Partially Miscible Blends of Epoxy Resin and Epoxidized Rubber: Structure Characterization of the Epoxidized Rubber and Mechanical Properties of the Blends, J. Appl. Polym. Sci., 53: 441-454.
22.
Wang, H.H. and Chen, J.C. ( 1995). Modification and Compatibility of Epoxy Resin with Hydroxyl-Terminated or Amine-Terminated Polyurethanes, Polym. Eng. Sci., 35: 1468-1475.
23.
Hsieh, K.H. and Han, J.L. (1990). Graft Interpenetrating Polymer Networks of Polyurethane and Epoxy. I. Mechanical Behavior, J. Polym. Sci.: Part B: Polym. Phys., 28: 623-630.
24.
Hsieh, K.H. and Han, J.L. (1990). Graft Interpenetrating Polymer Networks of Polyurethane and Epoxy. II. Toughening Mechanism, J. Polym. Sci.: Part B: Polym. Phys., 28: 783-794.
25.
Stefani, P.M. , Moschiar, S.M. and Aranguren , M.I. (1998). Polyurethane-Ductilized Epoxy Resins, J. Appl. Polym. Sci. , 68: 1781-1789.
26.
Stefani, P.M. , Moschiar, S.M. and Aranguren , M.I. (2001). Epoxy-Urethane Copolymers: Relation Between Morphology and Properties , J. Appl. Polym. Sci., 82: 2544-2552.
27.
Harani, H., Fellahi, S. and Bakar, M. ( 1998). Toughening of Epoxy Resin using Synthesized Polyurethane Prepolymer Based on Hydroxyl-Terminated Polyesters, J Appl. Polym. Sci., 70: 2603-2618.
28.
Hsia, H.-C. , Ma, C.-C.M., Li , M.-S., Li , Y.-S. and Chen, D.-S. (1994). Glycidyl-Terminated Polyurethane Modified Epoxy Resins, Mechanical Properties, Adhesion Properties, and Morphology, J. Appl. Polym. Sci. , 52: 1137-1151.