In this study the fracture behavior of woven glass fiber reinforced epoxy composites with trough thickness crack oriented at different angles were investigated. The composite plates consisting of five layers have a thickness of 1.2 mm. The trough cracks were formed at the center of the specimens with lengths of 5 mm, 7 mm and 9 mm. The fracture behavior of the composites, subjected to tensile loading and kink formation, were investigated. The fracture toughness of the composite specimens was determined by using both initial notch depth and the compliance method. The experimental results were presented in graphical form.
Turon, A., Costa, J., Maimi, P., Trias, D. and Mayugo, J.A. (2005). A Progressive Damage Model for Unidirectional Fibre-Reinforced Composites Based on Fibre Fragmentation. Part I: Formulation, Composites Science and Technology, 65: 2039-2048.
2.
Mathews, M.J. and Swanson, S.R. (2007). Characterization of the Interlaminar Fracture Toughness of a Laminated Carbon/Epoxy Composite , Composites Science and Technology, 67: 1489-1498.
3.
O'Brien, T.K. (1984). Mixed-Mode Strain-Energy Release Rate Effects on Edge Delamination of Composites. Effects of Defects in Composite Materials, ASTM STP, American Society for Testing and Materials, Vol. 836, pp. 125-142.
4.
O'Brien, T.K. (1984). Characterization of Delamination Onset and Growth in a Composite Laminate. In: Damage in Composite Materials, Reifsnider K. L. (Ed.), ASTM STP, American Society for Testing and Materials , Vol. 775, pp. 140-167.
5.
Law, G.E. (1984). A Mixed-Mode Fracture Analysis of (±25/90 n)S Graphite/Epoxy Composite Laminates. Effects of Defects in Composite Materials, ASTM STP, American Society for Testing and Materials , Vol. 836, pp. 143-160.
6.
Lee, S.M. (1990). Failure Mechanisms of Edge Delaminations of Composites, Journal of Composite Materials24: 1200-1212.
7.
Parmigiani, J.P. and Thouless, M.D. (2006). The Roles of Toughness and Cohesive Strength on Crack Deflection at Interfaces, Journal of the Mechanics and Physics of Solids, 67: 266-287.
8.
Campbell, G.H. , Ruhle, M., Dalgleish , B.J. and Evans, A.G. (1990). Whisker Toughening: A Comparison Between Aluminium Oxide and Silicon Nitride Toughened with Silicon Carbide, J. American Ceramic Soc., 73(3): 521-530.
9.
Evans, A.G. and Marshall, D.B. (1989). The Mechanical Behavior of Ceramic Matrix Composites . Acta Metall., 37: 2567-2583.
10.
O'Brien, T.K. (1998). Composite Interlaminar Shear Fracture Toughness, GIIC: Shear Measurement or Sheer Myth. In: Composite Materials: Fatigue and Fracture - 7th volume, Bucinell, R. B. (Ed.), ASTM STP, American Society for Testing and Materials, Vol. 1330, pp. 3-18.
11.
Reeder, J.R. and Crews, Jr J.H. (1991). Nonlinear Analysis and Redesign of the Mixed-Mode Bending Delamination Test. NASA Technical Memorandum102777.
12.
Benzeggagh, M.L. and Kenane, M. (1996). Measurement of Mixed-Mode Delamination Fracture Toughness of Unidirectional Glass/Epoxy Composites with Mixed-Mode Bending Apparatus, Composites Science and Technology , 56: 439-449.
13.
Stevanovic, D., Jar, B., Lowe , A. and Kalyanasandaram , S. (2000 ). On Crack Initiations Conditions for Mode I and Mode II Delamination Testing of Composite Materials, Composites Science and Technology , 60: 1879-1887.
14.
Aveston, J. and Kelly, A. (1973). Theory of Multiple Fracture of Fibrous Composites, Journal of Materials Science, 8: 352-362.
Xiangiao, Y. (2006). Stress Intensives and Propagation of Mixed Mode Cracks, Engineering Failure Analysis , 13(6): 1022-1027.
18.
Nalla, R.K. , Campell, J.P. and Rtchie, R.O. (2002). Mixed-Mode High Cycle Fatigue Crack Growth Thresholds in Ti-6Al-4V Role of Small Cracks, International Journal of Fatigue, 24: 1047-1062.