The aim of the present research is to provide insights into the sorption behavior and degradation mechanisms of a unidirectional pultruded E-glass/vinylester composite subjected to synergistic hygrothermal exposure and sustained bending strain for exposure times of up to 2 years. Composite specimens were found to follow a Langmuir-type diffusion behavior in all environments, with departure from that behavior attributed either to material leaching-out, chemical breakdown, interfacial debonding, or central delamination. The composite tensile strength decreased with increasing immersion time and temperature, with high sustained strain levels having a more detrimental effect at elevated temperatures. The initial strength loss was associated with matrix plasticization, while later reductions were caused by the occurrence of mechanisms of fiber degradation and interfacial debonding. Changes in tensile strength were largely reversible as a result of immersion in deionized water at 22 °C, but the level of regain decreased substantially at higher immersion temperatures. Finally, failure by delamination was observed to occur in the most severe environments at strength retention levels dependent upon the amount of imposed bending strain.
Seible, F. and Karbhari, V.M. (1996). Advanced Composites for Civil Engineering Applications in the United States. In: Proceedings of the 1st International Conference on Composites in Infrastructure, Tucson, Arizona, January, pp. 21-37.
2.
Sridharan, S., Zureick, A.H. and Muzzy, J.D. (1998). Effect of Hot-Wet Environments on E-Glass/ Vinylester Composites. In: Proceedings of the 56th Annual Technical Conference of the Society of Plastics Engineers, Atlanta, Georgia, pp. 2255-2259.
3.
Phifer, S.P., Verghese, K.N.E. and Lesko, J.J. (2000). Remaining Strength of Hygrothermally Aged Pultruded Vinylester E-Glass Composites. In: Proceedings of the 3rd International Conference on Advanced Composite Materials in Bridges and Structures, Ottawa, Canada, August, pp. 29-36.
4.
Bradley, W.L. and Grant, T.S. (1995). The Effect of Moisture Absorption on the Interfacial Strength of Polymeric Matrix Composites, Journal of Materials Science, 30: 5537-5542.
5.
Apicella, A. , Migliaresi, C., Nicolais, L., Iaccarino L. and Roccotelli, S. (1983). The Water Ageing of Unsaturated Polyester-Based Composites: Influence of Resin Chemical Structure, Composites, 14(4): 387-392.
6.
Ghorbel, I. And Valentin, D. (1993). Hydrothermal Effects on the Physico-Chemical Properties of Pure and Glass Fiber Reinforced Polyester and Vinylester Resins, Polymer Composites, 14(4): 324-334.
7.
Chin, J.W., Aouadi, K., Haight, M.R., Hughes, W.L. and Nguyen, T. (2001). Effects of Water, Salt Solution and Simulated Concrete Pore Solution on the Properties of Composite Matrix Resins Used in Civil Engineering Applications, Polymer Composites, 22(2): 282-297.
8.
Prian, L. and Barkatt, A. (1999). Degradation Mechanisms of Fiber-Reinforced Plastics and Its Implication to Prediction of Long-Term Behavior, Journal of Materials Science, 34: 3977-3989.
9.
Mensitieri, G., Del Nobile, M.A., Apicella, A. and Nicolais, L. (1995). Moisture-Matrix Interactions In Polymer Based Composite Materials. Revue de l'Institut Francais du Petrole, 50(4): 551-571.
10.
Apicella, A. , Nicolais, L. and De Cataldis , C. (1985). Characterization of the Morphological Fine Structure of Commercial Thermosetting Resins Through Hygrothermal Experiments, Advances in Polymer Science, 66: 189-207.
11.
Kawagoe, M. , Hashimoto, S., Nomiya, M., Morita, M., Qiu, J., Mizumo, W. and Kitano, H. (1999). Effect of Water Absorption and Desorption on the Interfacial Degradation in a Model Composite of an Aramid Fibre and Unsaturated Polyester Evaluated by Raman and FT Infra-red Microspectroscopy , Journal of Raman Spectroscopy, 30: 913-918.
12.
Nogueira, P. , Ramirez, C., Torres, A., Abad, M.J., Cano, J., Lopez J., Lopez-Bueno, I. and Barral, L. (2001). Effect of Water Sorption on the Structure and Mechanical Properties of an Epoxy Resin System, Journal of Applied Polymer Science, 80: 71-80.
13.
Oosthuizen, J.F. and Stone, M.A. (1997). Residual Stresses in CSM/vinyl Ester Resin Laminates due to Post-cure Shrinkage, Composite Structures, 39(3-4): 303-307.
14.
Liao, K. and Tan, Y.M. (2001a). Influence of Moisture-induced Stress on in situ Fiber Strength Degradation of Unidirectional Polymer Composite, Composites: Part A, 32: 365-370.
15.
Liao, K. and Tan, Y.M. (2001b). Influence of Moisture-induced Stress on in situ Fiber Strength Degradation of Unidirectional Polymer Composite, Composites: Part B, 32: 365-370.
16.
Bascom, W.D. (1974). The Surface Chemistry of Moisture-induced Composite Failure, In: Plueddemann, E.P. (ed.), Interfaces in Polymer Matrix Composites, pp. 79-108.
17.
Hodzic, A., Kim, J.K. and Stachurski, Z.H. (2001). Nano-indentation and Nano-scratch of Polymer/Glass Interfaces. II: Model of Interphases in Water Aged Composite Materials, Polymer, 42: 5701-5710.
18.
Charles, R.J. (1958). Static Fatigue of Glass, Part I, Journal of Applied Physics, 2(11): 1549-1560.
19.
Schmitz, G.K. and Metcalfe, A.G. (1966). Stress Corrosion of E-Glass Fibers, Industrial and Engineering Chemistry Product Research and Development, 5(1): 1-8.
20.
Mould, R.E. (1959). Strength and Static Fatigue of Glass, Glastechnische Berichte-Sonderband, 32(3): 18-28.
21.
Kasturiarachchi, K.A. and Pritchard , G. (1983). Water Absorption of Glass/Epoxy Laminates Under Bending Stresses, Composites, 14(3): 244-250.
22.
Harper, J.F. and Naeem, M. (1989). The Moisture Absorption of Glass Fibre Reinforced Vinylester and Polyester Composites, Materials & Design , 10(6): 297-300.
23.
Chateauminois, A., Chabert, B., Soulier, J.P. and Vincent, L. (1993). Effects of Hygrothermal Aging on the Durability of Glass/epoxy Composites, Physico-chemical Analysis and Damage Mapping in Static Fatigue, Proceedings of the 9th International Conference on Composite Materials, Madrid, Spain, pp. 593-600.
24.
Helbling, C. and Karbhari, V.M. (2002). Environmental Durability of E-Glass/Vinylester Composites Under the Combined Effect of Moisture, Temperature and Stress. In: Proceedings of the 2nd International Conference on Durability of Fibre Reinforced Polymer (FRP) Composites for Construction, Montreal, Canada, June, pp. 247-258.
25.
Carter, H.G. and Kibler, K.G. (1978). Langmuir - Type Model for Anomalous Moisture Diffusion in Composite Resins, Journal of Composite Materials, 12: 118-131.
26.
Morii, T., Ikuta, N., Kiyosumi, K. and Hamada H. (1997). Weight-Change Analysis of the Interphase in Hygrothermally Aged FRP: Consideration of Debonding, Composites Science and Technology, 57: 85-990.
27.
Marshall, J.M. , Marshall, G.P. and Pinzelli, R.F. (1982). The Diffusion of Liquids into Resins and Composites, Polymer Composites, 3(3): 131-137.
28.
Chin, J.W., Nguyen, T. and Aouadi, K. (1999). Sorption and Diffusion of Water, Salt Water, and Concrete Pore Solution in Composite Matrices, Journal of Applied Polymer Science, 71: 483-492.
29.
Neumann, S. and Marom, G. (1987) Prediction of Moisture Diffusion Parameters in Composite Materials under Stress, Journal of Composite Materials, 21: 68-80.
30.
Rogers, C.E. (1965). Solubility and Diffusivity. In: Physics and Chemistry of the Organic Solid State, Vol. 2, pp. 509-635, Interscience Publishers, New York.
31.
Weitsman, Y.J. (1998). Effects of Fluids on Polymeric Composites - A Review. Mechanical and Aerospace Engineering and Engineering Science, The University of Tennessee Report MA ES98-5.0-CM, August.
32.
Fahmy, A.A. and Hurt, J.C. (1980). Stress Dependence of Water Diffusion in Epoxy Resin, Polymer Composites, 1(2): 77-80.
33.
Lagrange, A., Melennec, C. and Jacquemet, R. (1991). Influence of Various Stress Conditions of the Moisture Diffusion of Composites in Distilled Water and in Natural Sea-Water , In: Cardon, A. H. and Verchery, G. (eds), Durability of Polymer Based Composite Systems for Structural Applications, pp. 385-392, Elsevier Applied Sciences.
34.
Kaelble, D.H. , Dynes, P.J. and Maus, L. (1974). Surface Energy Analysis of Treated Graphite Fibers, Journal of Adhesion, 6(3): 239-258.
35.
Chin, J.W., Hughes, W.L. and Signor, A. (2001). Elevated Temperature Aging of Glass Fiber Reinforced Vinyl Ester and Isophthalic Polyester Composites in Water, Salt Water and Concrete Pore Solution, In: Proceedings of the 16th Technical Conference of the American Society for Composites, September 9-12, Blacksburg, VA, pp. 1-12.