A new biomaterial has been developed by fixing native collagens with a polyepoxy compound (PC) fixative. Prior studies have shown that this biomaterial has comparable properties as compared to collagen fixed with glutaraldehyde (GA) and thus has a great promise for use as an implantable bioprosthesis. The purpose of this study was to understand the mechanism of the amino acids-PC reactions in the fixation process. Bovine arteries were fixed with PC under various pH, concentration and temperature conditions as a function of fixation time. Individual amino acid components in the fresh and the fixed arteries were assayed using a Beckman amino acid analyzer to determine the degree of tanning. The denaturation temperature (Td) was also measured on each sample. Since the denaturation temperature is a direct indication of cross-linking of individual amino acids with the fixative, the difference in the degree of tanning for the same increase in Td may be indicative of the quantity of the masked, non-cross-linked amino acids. The fixation reaction data indicated that not all amino acids were cross-linked upon contacting the PC fixative. Masking appeared to be more substantial with a fixation at higher pH values.
ImamuraE., SawataniO., KoyanagiH., NoishikiY., MiyataT.Anticalcification effects of epoxy compounds as cross-linking agent.Jpn J Artif Organs1988; 17: 1101–3.
8.
NoijiriC., NoishikiY., KoyanagiH.Aorta-coronary bypass grafting with heparinized vascular grafts in dogs.J Thorac Cardiovasc Surg1987; 93: 867–77.
9.
MasuokaM., NakamuraM.Effect of catalysts on epoxy tannage.Leather Chemistry1985; 30: 223–32.
10.
NoishikiY., KodairaK., FuruseM., MiyataT.Method of preparing antithrombogenic medical materials. US Patent 1989 Patent Number 4,806,595.
11.
TuR., McIntyreJ., HataC., LuC.L., QuijanoR.C.Dynamic internal compliance of a vascular prosthesis.Trans ASAIO1991; 37: M470–2.
12.
LeeJ.M., ThyagarajanK., PereiraC., McIntyreJ., TuR.Cross-linking of a prototype bovine artery xenograft: comparison of the effects of glutaraldehyde and four poly(glycidyl ether) compounds.Artificial Organs1991; 15(4): 303.
13.
McIntyreJ., TuR., WangE., HataC., DeJongeM., QuijanoR.C.Biomechanical properties of a new biomaterial - A polyepoxy tanned bovine artery.Transactions of the Society for Biomaterials1991: 14: 119.
14.
LohreJ., BacligL., SagartzJ., GuidaS., TuR.Evaluation of two diepoxy ether compounds for biocompatible potential (presented at the VIII World Congress of the ISAO, Montreal, Canada, August 19-22,1991).
15.
NioshikiY., MiyataT., KodairaK.Development of a small caliber vascular graft by a new cross-linking method incorporating slow heparin release collagen and natural tissue compliance.Trans ASAIO1986; 32: 114–9.
16.
SungH., WitzelT., HataC., TuR., QuijanoR.C.Noninvasive color doppler inspection of small diameter vascular grafts implanted in canine carotid and femoral arteries (in press).
17.
HataC., WangE., NoishikiY., TomozawaY., TuR., QuijanoR.C.Evaluation of polyepoxy compound fixed biological vascular prosthesis and an expanded polytetrafluoroethylene vascular graft.Artificial Organs1992; 16(3): 263–6.
18.
SungH., ShenS., TuR.Development of a polyepoxy compound preserved bioprosthetic heart valve (presented at 1992 ESAO meeting Rodos, Greece, October 14-17, 1992).
19.
HataC., TuR., ShenS.A pliable biological valved conduit with antithrombogenicity (presented at 1992 ESAO meeting, Rodos, Greece, October 14-17,1992).
SabatiniD., BenschK., BarrnettR.Cytochemistry and electron microscopy.J Cell Biol1963; 17: 19–58.
29.
TuR., LuC.L., ThyagarajanK., WangE., NguyenH.Quijano RC. Kinetics of fixation of bovine collagens with polyepoxy compounds (presented at 1991 ASAIO meeting, Chicago, Illinois, April 25-27, 1991).
30.
TuR., LuC.L., ThyagarajanK., WangE., NguyenH., QuijanoR.C.Kinetic study of collagen cross-linking using a new fixative - polyepoxy compounds (presented at 1991 Society for Biomaterials Meeting, Scottsdale, Arizona, May 1-5, 1991).
31.
TuR., LuC.L., ThyagarajanK.Kinetic study of collagen fixation with polyepoxy fixatives.J Biomedical Materials Research1993; 27: 3–9.
32.
NimniM.E., HarknessR.D.Molecular structure and functions of collagen. In: Nimni ME, ed. Collagen, Vol I. Boca Raton, Florida, USA.CRC Press, Inc.1988; 1: 1–78.
WaiteJ.H., TanzerM.L.Cross-linking of macromolecules. In: FloriniJ.R., ed. CRC handbook of biochemistry in aging.Boca Raton, Florida, USA.: CRC Press, Inc., 1981.
35.
EyreD.R., PazandM.A., GallopP.M.Cross-linking in collagen and elastin.Ann Rev Biochem1984; 53: 717.
36.
MurayamaY., SatohS., OkaT., ImanishiJ., NoishikiY.Reduction of the antigenicity and immunogenicity of xenografts by a new cross-linking reagent.Trans ASAIO1988; 34: 546–9.
37.
BaileyA.J., PeachC.M.Isolation and structural identification of a labile intermolecular cross-link in collagen.Biochem Biophys Res Commun1968; 33: 812.
38.
AllainJ.C., LeLousM., Cohen-SolaiL., BazinS., MaroteauxP.Isometric tensions developed during the hydrothermal swelling of rat skin.Connect Tissue Res1980; 7: 127.
39.
ShechterL., WynstraJ.Glycidyl ether reactions with alcohols, phenols, carboxylic acids, and acid anhydrides.Industrial and Engineering Chemistry1956; 48: 86–93.
40.
MarchJ.Advances organic chemistry - reactions, mechanisms, and structure.New York, Chester, Brisbane, Toronto, Singapore: John Wiley and Sons, 1985; 368–9.