Influence of titanium surface roughness on a nanoscale on the zeta potential and platelet adhesion

Abstract

Thromboembolic complications still arise on blood contacting surfaces. Surface charge and topography influence the subsequent deposition of proteins and platelets, potentially leading to thrombi. Research showed a correlation of surface charge and nanoscale roughness, and a negative surface charge as well as a smooth surface finish are associated with lower thrombogenicity. The aim of this study was to compare the platelet adhesion on titanium with different nanoscale roughnesses and to examine if those roughness variations caused a change in surface charge. Titanium samples were polished and roughened to four different nanoscale roughness levels. Platelet adhesion (covered surface area (CSA), N = 8) was tested in flow chambers with human whole blood using fluorescence imaging. ζ-potential was measured over a broad range of pH-values and interpolated to obtain the ζ-potential for pH_Blood (7.4). Platelet adhesion tests were evaluated in terms of p-values and the Wilcoxon test effect size and the trend of the ζ-potential at pH_Blood and the CSA was compared. R_a-values ranged between 35 (polished) and 156 nm. Regarding platelet adhesion, the polished sample showed the lowest mean CSA with a medium or strong effect size compared to the roughened samples. The interpolated ζ-potentials for pH_Blood follow a similar trend as the CSA, with the lowest ζ-potential measured for the polished surface. These findings suggest that the decreasing ζ-potential due to lower nanoscale roughness might be an additional explanation for the improved hemocompatibility besides the smoother topography.

Keywords

Platelet adhesion hemocompatibility thrombogenicity titanium roughness zeta potential surface charge flow chamber ventricular assist devices

Get full access to this article

View all access options for this article.

References

Sin

Kei

Miao

. Surface coatings for ventricular assist devices. Expert Rev Med Devices 2012; 6: 264–283.

Zucker

Vroman

. Platelet adhesion induced by fibrinogen adsorbed onto glass. Proc Soc Exp Biol Med 1969; 131: 318–320.

Schuster

Vera

Laczeski

, et al. Adhesion of blood platelets in TiO₂ coatings. In: 144th Annual Meeting & Exhibition, 15th-19th March, 2015. Orlando, Florida: TMS, pp.653–660.

Jayaraman

Kang

Antaki

, et al. The roles of sub-micron and microscale roughness on shear-driven thrombosis on titanium alloy surfaces. Artif Organs 2023; 47: 490–501.

Linneweber

Dohmen

Kerzscher

, et al. The effect of surface roughness on activation of the coagulation system and platelet adhesion in rotary blood pumps. Artif Organs 2007; 31: 345–351.

Ferraris

Cazzola

Peretti

, et al. Zeta potential measurements on solid surfaces for in Vitro biomaterials testing: Surface charge, reactivity upon contact with fluids and protein absorption. Front Bioeng Biotechnol 2018; 6: 1–7.

Spriano

Sarath Chandra

Cochis

, et al. How do wettability, zeta potential and hydroxylation degree affect the biological response of biomaterials? Mater Sci Eng C 2017; 74: 542–555.

Srinivasan

Sawyer

. Role of surface charge of the blood vessel wall, blood cells, and prosthetic materials in intravascular thrombosis. J Colloid Interface Sci 1970; 32: 456–463.

Borghi

Vyas

Podestà

, et al. Nanoscale roughness and morphology affect the isoelectric point of titania surfaces. PLoS One 2013; 8: 1–14.

10.

Esslinger

Schulz

Bierewirtz

, et al. Visualization of platelet deposition in a flow chamber. Curr Dir Biomed Eng 2022; 8: 145–148.

11.

Wolberg

Meng

Monroe

, et al. A systematic evaluation of the effect of temperature on coagulation enzyme activity and platelet function. J Trauma Inj Infect Crit Care 2004; 56: 1221–1228.

12.

Zhang

Liao

Fok

, et al. Effect of crystalline phase changes in titania (TiO₂) nanotube coatings on platelet adhesion and activation. Mater Sci Eng C 2018; 82: 91–101.