A fracture of a ceramic femoral head is reported in this study. Fractures of ceramic femoral heads are uncommon and reports on this complication are rare. After 3 million cycles, on a twelve station hip simulator that tested alumina femoral head against polyethylene acetabular cup, fracture of the ceramic ball was observed. The retrieved specimen consisted of three large ceramic fragments from the same ceramic femoral head, a polyethylene acetabular cup and a stainless steel jig. Careful and detailed examination of the removed components was made. The fracture of the ceramic ball resulted in damage to the metal taper of the jig component which was fixed into the simulator.
CigadaA., CabriniM., PedeferriP.. Increasing of the corrosion resistance of the Ti6AI-4V alloy by high thickness anodic oxidation.Int J Artif Organs1990; 13: 585.
2.
AmstutzH.C., SparlingE.A., GrigorisP., CampbellP.A., DoreyF.J.. Surface replacement: the hip replacement of the future?Hip International1998; 8(4): 187–207.
3.
OonishiH., MurataN., KushitaniS., ImotoK., IwakiY., KinN.. Wear behaviour of polyethylene cup against 28 mm Alumina ball in total hip prostheses. In: Sedel, ed. Bioceramics, 1997; 333–6.
4.
DowsonD., HardingR.T.. The wear characteristics of ultrahigh molecular weight polyethylene against a high density alumina ceramic under wet (distilled water) and dry conditions.Wear1982; 75: 313–31.
5.
BragdonC.R., JastyM., KawateK.. Wear of retrieved cemented polyethylene acetabula alumina femoral heads.The Journal of Arthroplasty1997; 12(2): 119–25.
6.
ZichnerI.P., WiIlertH.G.. Comparison of alumina-polyethylene and metal-polyethylene in clinical trails.Clinical orthopaedics and related research1992; 282: 86–94.
7.
AndrisanoA., DragoniE., StrozziA.. Asymmetric mechanical analysis of ceramic heads for total hip replacement.Proc Instn Mech Engrs1990; 204: 157–67.
8.
1636 AF 1995 Standard Specifications for Bores and Cones for Modular Femoral Heads. ASTM.
9.
CederL.. Hip fracture treatment: from local to multinational assessment.Hip International1998; 8(2): 99–101.
10.
De PedroJ.A., ReyJ., Lopez-CaseroR.. Peritrochanteric fractures of the femura: a comparison between the Ender nail, Gamma nail and Dyamic hip screw.Hip International1996; 6(1): 29–39.
11.
ParkerM.J., CurrieC.T., MountainJ.A., ThorngrenK.G.. Standardised audit of hip fracture in europe (SAHFE).Hip International1998; 8(1): 105–5.
12.
AffatatoS., TagliatiM., ToniA.. Hip prosthesis: an in vitro wear protocol based on a comparison between gravimetric and profilometric analysis.Int J Artif Organs1999; 22(4): 226–9.
13.
AffatatoS., TerziS., NardiD., ToniA.. Metal-UHMWPE wear: experimental testing.Chirurgia degli organi in movimento1997; 82: 393–9.
14.
AffatatoS., TestoniM., CacciariG.L., ToniA.. Mixed oxides prosthetic ceramic ball heads. Part 1: effect of the ZrO2 fraction on the wear of ceramic of polyethylene joints.Biomaterials1999; 20: 971–5.
15.
SaikkoV.O., PaavolainenP.O., SlatisP.. Wear of the polyethylene acetabular cup: metallic and ceramic heads comparaded in a hip simulator.Acta Orthop Scand1993; 64(4): 391–402.
16.
CallawayG.H., FlynnW., RanawatC.S., SculcoT.P.. Case report: fracture of the femoral head after ceramic-on-polyethylene total hip arthroplasty.The Journal of Arthroplasty1995; 10(6): 855–9.
17.
ZiebicA., LuberH., Bioceramic hip joint components-industrial production and testing procedures to ensure high functional reliability. In: VincenziniP., ed. Ceramics in surgery.Amsterdam: Elsevier1983; 267.
18.
WordsworthR.A., WeightmanB.. Laboratory development of a method of attaching cermic femoral heads to metal stems.Biomaterials1986; 7(3): 83–8.
19.
Dalla PriaP.. Why ceramic heads break. The ceramic-ceramic coupling in hip prosthesis.LIMA-Lto S.p.A., Udine,1997; 56.
20.
ErdemliB., GurkanI., GuzelB., CetinI.. Treatment of femoral fractures associated with stem loosening following total hip arthroplasty.Hip International1998; 8(3): 138–44.