Laboratory Aging and Annealing of Asphalt Binders by Microwave Radiation

Abstract

A household microwave oven with a frequency of 2.45 × 10³ ±13 MHz and an output power of 1000 W is used to simulate short- and long-term aging of asphalt, and for annealing, prior to sampling, to remove steric (isothermal) hardening. A quartz petri dish holds the asphalt during microwave treatment, at atmospheric pressure. To simulate thin film oven (TFO) aging, a 10-g sample is microwaved for a total of 33 min. For 11 asphalts, the average difference in G*/sin δ, at limiting high temperature, between TFO and microwave aging is ±0.68 kPa. Simulating rolling thin-film oven (RTFO) aging is possible by microwaving for a total of 63 min. For 18 asphalts, the average difference in G*/sin δ, at limiting high temperature, between RTFO and microwave aging is ± 1.19 kPa. Aging by RTFO + pressure aging vessel (PAV) and TFO + PAV is simulated by microwaving for a total of 158 min. Microwave aging marginally underestimates long-term aging. For 18 asphalts, the average difference in intermediate temperature obtained after RTFO + PAV versus microwave aging is −2.8°C; for TFO + PAV versus microwave aging, the average difference is −2.7°C. Annealing for 2 hr at 150°C in a convection oven (conductive heating) is simulated by microwaving for a total of 27 min. The average difference in G*/sin δ between the two methods is ±0.24 kPa. Molecular size index (MSI, the ratio of first to second fraction from size exclusion chromatography) correlates with stiffness at low temperature. At intermediate temperature, tan δ remains practically unchanged until MSI reaches a minimum, then increases sharply. At limiting high temperature, G^* does not correlate with MSI.

Get full access to this article

View all access options for this article.

References

Bishara

S. W.

, and McReynolds

R. L.

. Effect of Microwave Energy on the Properties of Asphalt and Its Use as an Aging Tool. In Transportation Research Record 1488, TRB, National Research Council, Washington, D.C., 1995, pp. 1–12.

Petersen

J. C.

, Robertson

R. E.

, Branthaver

J. F.

, Harnsberger

P. M.

, Duvall

J. J.

, Kim

S. S.

, Anderson

D. A.

, Christensen

D. W.

, and Bahia

H. U.

. Binder Characterization and Evaluation. Vol. 1, SHRP-A-367. Strategic Highway Research Program, National Research Council, Washington, D.C., 1994.

Neas

E. D.

, and Collins

M. J.

. In Introduction to Microwave Sample Preparation ( Kingston

H. M.

, and Jassie

L. B.

, eds.), American Chemical Society, Washington, D.C., 1993.

McKay

J. F.

, and Harnsberger

P. M.

. The Effects of Temperature on Reversible Hardening of Asphalts. In Annual Technical Report, Nov. 1, 1994–May 15, 1995, Western Research Institute, Laramie, Wyo., May 1995, pp. 109–133.

Billmeyer

F. W.

Jr. Textbook of Polymer Science (3rd ed.). John Wiley & Sons, New York, 1984.

Moore

D. S.

, and McCabe

G. P.

. Introduction to the Practice of Statistics. W. H. Freeman and Company, New York, 1989.

Bishara

S. W.

, McReynolds

R. L.

, and Lewis

E. R.

. Interrelationship Between Performance-Related Properties of Asphalt Cement and Their Correlation with Molecular Size Distribution. In Transportation Research Record 1323, TRB, National Research Council, Washington, D.C., 1991, pp. 1–9.

Anderson

R. L.

Practical Statistics for Analytical Chemists. Van Nostrand Reinhold Company, New York, 1987.

Branthaver

J. F.

, Duvall

J. J.

, Petersen

J. C.

, Plancher

, and Robertson

R. E.

. Preparative Size-Exclusion Chromatography Separation of SHRP Asphalts. Correlation with Viscoelastic Properties. Fuel Science and Technology International, Vol. 10, 1992, pp. 1003–1032.