Comparing Resilient Modulus and Dynamic Modulus of Hot-Mix Asphalt as Material Properties for Flexible Pavement Design

Abstract

With the current trend toward developing mechanistic flexible pavement design and the need for more reliable design procedures, accurate characterization of hot-mix asphalt (HMA) properties is needed. Resilient and dynamic modulus tests were performed at five temperatures on two typical mixes used in the Commonwealth of Virginia to compare the test results. The dynamic modulus was measured at six frequencies at each of the testing temperatures, and the resilient modulus test was performed at one loading time. The study found that the size of the specimen statistically affected the measured resilient modulus value. Resilient modulus values obtained in the 100-mm-diameter specimens were higher than those obtained in the 150-mm-diameter specimens at all testing temperatures. No statistical differences were observed in the resilient modulus of the two mixes. However, statistical differences were found in the dynamic modulus of the two mixes. A strong relation between the dynamic modulus test performed at 5 Hz and the resilient modulus was found. Three different pavement structures were analyzed to estimate the variation of their bottom-up fatigue life when different moduli were used for the HMA layer. It was found that the measured dynamic moduli resulted in the highest fatigue life estimates for the three considered pavements. It is concluded that the dynamic modulus test provides a better characterization of HMA than the resilient modulus test because it provides full characterization of the mix over temperature and loading frequencies.

Get full access to this article

View all access options for this article.

References

Guide for the Design of Pavement Structures. AASHTO, Washington, D.C., 1993.

Guide for Mechanistic-Empirical Design of New and Rehabilitated Pavement Structures. Final Report, NCHRP 1–37A. Transportation Research Board of the National Academies, Washington, D.C., 2004.

Loulizi

Al-Qadi

I. L.

Lahouar

and Freeman

T. E.

. Measurement of Vertical Compressive Stress Pulse in Flexible Pavements: Representation for Dynamic Loading Tests. In Transportation Research Record: Journal of the Transportation Research Board, No. 1816, Transportation Research Board of the National Academies, Washington, D.C., 2002, pp. 125–136.

Roque

and Buttlar

W. G.

. Development of a Measurement and Analysis Method to Accurately Determine Asphalt Concrete Properties Using the Indirect Tensile Mode. Proc., Association of Asphalt Paving Technologists, Vol. 61, 1992, pp. 304–332.

Clyne

T. R.

Marasteanu

M. O.

and Skok

E. L.

. Dynamic and Resilient Modulus of MNDOT Asphalt Mixtures. Report MN/RC-2003–09. Minnesota Department of Transportation, Minneapolis, 2003.

Pellinen

T. K.

and Witczak

M. W.

. Stress Dependent Master Curve Construction for Dynamic Modulus. Journal of the Association of Asphalt Paving Technologists, Vol. 71, 2002, pp. 281–309.

Huang

Y. H.

Pavement Analysis and Design, 2nd ed. Prentice Hall, Upper Saddle River, N.J., 2003.