This paper induced a novel methodology for the characterization of creep behavior of weld heat-affected zone (HAZ) for boron-free P91 (PM) and boron modified P91B (B-PM) steels. Gleeble-3800 thermo-mechanical simulator replicated specimens, representing coarse-grain HAZ (CGHAZ), fine-grained HAZ (FGHAZ), and inter-critical HAZ (ICHAZ). Short-term impression creep tests were conducted at 625°C/270-410MPa on PM/B-PM and their simulated HAZs after being subjected to post-weld heat treatment (PWHT) of 760°C/3 h. Microstructural characterization and local strain analyses were accomplished by electron back-scattered diffraction. Simulated microstructures of P91B-FG/ICHAZ after PWHT exhibited lath martensitic structure and large prior-austenite grain size as regards P91-FG/ICHAZ, correspondingly. Average values of local microstructural strain from local average misorientation were relatively high in B-PM and P91B-ICHAZ than PM and P91-ICHAZ, respectively. Similar observations were found for P91-CG/FGHAZ with their counterparts. Stress dependent steady-state creep-rate (SSCR) followed power-law for all specimens except PM. The minimum and maximum ranges of SSCR for P91B specimens were observed to be in a narrower range than P91 specimens. The value of stress exponent for all specimens was evaluated, and corresponding mechanisms were discussed. The analyses of microstructures and corresponding impression creep behavior of P91/P91B samples suggested that modification of 100 ppm boron to P91 steel improved creep-rupture ductility that delayed type IV failure at outer HAZ of P91 steel weldments.
GoldenBJLiDFO’DowdNP, et al. Microstructural modeling of P91 martensitic steel under uniaxial loading conditions. J Press Vessel Technol2014; 136: 1–6.
2.
OgataTYaguchiM. Study on creep-fatigue damage evaluation for boiler weldment parts. J Press Vessel Technol2001; 123: 105–111.
3.
KhajuriaAKumarRBediR. Characterizing creep behaviour of modified 9Cr1Mo steel by using small punch impression technique for thermal powerplants. J Mech Mech Eng2018; 4: 47–61.
4.
FrancisJAMazurWBhadeshiaHKDH. Review type IV cracking in ferritic power plant steels. Mater Sci Technol2006; 22: 1387–1395.
5.
RothwellDJA, JS, Review of type IV cracking of weldments in 9–12%Cr creep strength enhanced ferritic steels. Int Mater Rev2013; 58: 437–473.
6.
TabuchiMHongoHLiY, et al. Evaluation of microstructures and creep damages in the HAZ of P91 steel weldment. J Press Vessel Technol2009; 131: 1–6.
7.
WatanabeTTabuchiMYamazakiM, et al. Creep damage evaluation of 9Cr–1Mo–V–Nb steel welded joints showing type IV fracture. Int J Press Vessel Piping2006; 83: 63–71.
8.
LahaKChandravathiKSParameswaranP, et al. Characterization of microstructures across the heat-affected zone of the modified 9Cr-1Mo weld joint to understand its role in promoting type IV cracking. Metallurgical Mater Trans A2007; 38: 58–68.
9.
LahaKChandravathiKSParameswaranP, et al. Type IV cracking susceptibility in weld joints of different grades of Cr-Mo ferritic steel. Metallurgical Mater Trans A2009; 40: 386–397.
10.
AkhtarM. Metallurgical characterisation of simulated heat affected zone in Boron modified P91 steel. Master Thesis, National Institute of Technology Warangal, Warangal, 2017.
11.
AkhtarMKhajuriaAKumarVSGuptaRK, et al. Evolution of microstructure during welding simulation of Boron modified P91 steel. Phys Met Metallography2019; 120: 672–685.
12.
AkhtarMKhajuriaA. Probing true creep-hardening interaction in weld simulated heat affected zone of P91 steels. J Manuf Process2019; 46: 345–356.
13.
FrancisJACantinGMDMazurW, et al. Effects of weld preheat temperature and heat input on type IV failure. Sci Technol Weld Joining2009; 14: 436–442.
14.
YuXBabuSSTerasakiH, et al. Correlation of precipitate stability to increased creep resistance of Cr–Mo steel welds. Acta Mater2013; 61: 2194–2206.
15.
KhajuriaAAkhtarMBediR, et al. Microstructural investigations on simulated intercritical heat-affected zone of boron modified P91-steel. Mater Sci Technol2020; 36: 1407–1418.
16.
KhajuriaAAkhtarMBediR, et al. Influence of boron on microstructure and mechanical properties of gleeble simulated heat-affected zone in P91 steel. Int J Press Vessel Piping2020; 188: 104246.
17.
AkhtarMKhajuriaA. Effects of prior austenite grain size on impression creep and microstructure in simulated heat affected zones of boron modified P91 steels. Mater Chem Phys2020; 249: 122847.
18.
AkhtarMKhajuriaABediR. Effect of re-normalizing and re-tempering on inter-critical heat affected zone(S) of P91B steel. In: SharmaVDixitUSørbyK, et al. (eds) Manufacturing engineering. Singapore, Singapore: Springer, 2020, pp.255–270.
19.
AkhtarMKhajuriaA. Probing true microstructure-hardening relationship in simulated heat affected zone of P91B steels. Metallography Microstruct Anal2019; 8: 656–677.
20.
AkhtarMKhajuriaAPandeyMK, et al. Effects of boron modifications on phase nucleation and dissolution temperatures and mechanical properties in 9%Cr steels: alloy design. Mater Res Express2020; 6: 1265k3.
21.
AkhtarMKhajuriaAPandeyMK, et al. Effects of boron modifications on phase nucleation and dissolution temperatures and mechanical properties in 9%Cr steels: sensitivity and stability. Mater Res Express2020; 6: 1265k1.
22.
KhajuriaABediRKumarR. Investigation of impression creep deformation behavior of boron-modified P91 steel by high-end characterization techniques. In: SharmaVDixitUAlba-BaenaN (eds) Manufacturing engineering. Singapore, Singapore: Springer, 2019, pp.137–150.
23.
KhajuriaAKumarRBediR. Effect of boron addition on creep strain during impression creep of P91 steel. J Mater Eng Perform2019; 28: 4128–4142.
24.
KhajuriaAAkhtarMKumarR, et al. Effect of boron modified microstructure on impression creep behaviour of simulated multi-pass heat affected zone of P91 steel (eds DuttaSChakrabortySS). In: Proceedings of national conference on advanced materials, manufacturing and metrology, Durgapur, West Bengal, India, 16–17 February 2018, pp.150–157. CSIR-CMERI.
25.
AkhtarMKhajuriaAKumarR, et al. Metallurgical investigations on dual heat cycled boron alloyed P91 ferritic/martensitic steel. In: Young professionals conference of the international institute of welding, December 2017, Chennai, Tamil Nadu, India, IIW Chennai, pp.322–331.
26.
SchlacherCBéalCSommitschC, et al. Creep and damage investigation of advanced martensitic chromium steel weldments for high temperature applications in thermal power plants. Sci Technol Weld Joining2015; 20: 82–90.
27.
GibbsWSMatlockDKOlsonDL, et al. High temperature impression creep testing of weldments. Weld J1985; 64: 153s–158s.
28.
WangSH. Impression creep behavior in weldments. J Mar Sci Technol1994; 2: 17–24.
29.
HydeTHSunWWilliamsJA. Creep behaviour of parent, weld and HAZ materials of new, service-aged and repaired 1/2Cr1/2Mo1/4V: 2 1/4Cr1Mo pipe welds at 640°C. Mater High Temp1999; 16: 117–129.
30.
YangFLiJCM. Impression test—A review. Mater Sci Eng R Rep2013; 74: 233–253.
31.
ASTM A387 / A387M - 17a. Standard specification for pressure vessel plates, alloy steel, chromium-molybdenum, https://www.astm.org/Standards/A387.htm (2017, accessed 2 December 2020).
32.
KhajuriaAKumarRBediR, et al. Impression creep studies on simulated reheated haz of P91 and P91B steels. Int J Mod Manuf Technol2018; 10: 50–56.
33.
ChuSNGLiJCM. Impression creep; a new creep test. J Mater Sci1977; 12: 2200–2208.
34.
ChuSNLiJC. Impression creep of β-tin single crystals. Mater Sci Eng1979; 39: 1–10.
35.
CerriEEvangelistaESpigarelliS, et al. Evolution of microstructure in a modified 9Cr–1Mo steel during short term creep. Mater Sci Eng A1998; 245: 285–292.
36.
UleBNagodeA. A model based creep equation for 9Cr–1Mo–0·2V (P91 type) steel. Mater Sci Technol2007; 23(11): 1367–1374.
37.
AndersonPBellgardtTJonesFL. Creep deformation in a modified 9Cr-1 Mo steel. Mater Sci Technol2003; 19: 207–213.
38.
EvansRWWilshireB. Creep of metals and alloys. London: Institute of Metals, 1985.
39.
FedorovaIKostkaATkachevE, et al. Tempering behavior of a low nitrogen boron-added 9%Cr steel. Mater Sci Eng A2016; 662: 443–455.
40.
AkhtarMKhajuriaASahuJK, et al. Phase transformations and numerical modelling in simulated HAZ of nanostructured P91B steel for high temperature applications. Appl Nanosci2018; 8: 1669–1685.
41.
WrightSINowellMMFieldDP. A review of strain analysis using electron backscatter diffraction. Microsc Microanal2011; 17: 316–329.
42.
NaghdiFMahmudiR. Impression creep behavior of the extruded Mg–4Zn–0.5Ca and Mg–4Zn–0.5Ca–2RE alloys. Mater Sci Eng A2014; 616: 161–170.
43.
NabarroFRNDe VilliersHL. The physics of creep: creep and creep-resistant alloys. London: Taylor & Francis, 1995.