To study the rate effect on the fracture properties of concrete, 700 mm × 150 mm × 100 mm specimens with a 60-mm notch were used for three-point bending test at the loading rate of 0.0005, 0.005, 0.05, and 0.5 mm/s, respectively. In the test, digital image correlation was used for monitoring the fracture process. The result shows that the fracture stress, unstable fracture toughness, and fracture energy have rate sensitivity. The numerical simulation was performed by extended finite-element model. The model calibration had a very good agreement with the experimental result under different loading rate. Meanwhile, fracture process zone length calculated by digital image correlation is similar to the result obtained by the extended finite-element model under different loading rate.
BischoffPHPerrySH.Compressive behaviour of concrete at high strain rates. Mater Struct1991; 24(6): 425–450.
2.
WuSChenXZhouJ.Influence of strain rate and water content on mechanical behavior of dam concrete. Constr Build Mater2012; 36(4): 448–457.
3.
SchulerHMayrhoferCThomaK.Spall experiments for the measurement of the tensile strength and fracture energy of concrete at high strain rates. Int J Impact Eng2006; 32(10): 1635–1650.
4.
YanDLinG.Dynamic properties of concrete in direct tension. Cement Concrete Res2006; 36(7): 1371–1378.
5.
BažantZPGettuR.Rate effects and load relaxation in static fracture of concrete. ACI Mater J1992; 89(5): 456–468.
6.
YuRCZhangXXRuizG, et al. Size of the fracture process zone in high-strength concrete at a wide range of loading rates. Applied Mech Mater2010; 24–25: 155–160.
7.
KaplanMF.Crack propagation and the fracture of concrete. J Proc1961; 58(11): 591–610.
8.
EvansRHMaratheMS.Microcracking and stress-strain curves for concrete in tension. Mater Struct1968; 1(1): 61–64.
9.
HillerborgA.Application of the fictitious crack model to different types of materials. Int J Fracture1991; 51(2): 95–102.
10.
BažantZPOhBH.Crack band theory for fracture of concrete. Matériaux Constr1983; 16(3): 155–177.
11.
BažantZPYuQ.Universal size effect law and effect of crack depth on quasi-brittle structure strength. ASCE J Eng Mech2009; 135(2): 78–84.
12.
BarbatGBCerveraMChiumentiM, et al. Structural size effect: experimental, theoretical and accurate computational assessment. Eng Struct2020; 213: 110555.
13.
XuSReinhardtHW.Determination of double-K criterion for crack propagation in quasi-brittle fracture, Part I: experimental investigation of crack propagation. Int J Fracture1999; 98(2): 111–149.
14.
XuSReinhardtHW.Determination of double-K criterion for crack propagation in quasi-brittle fracture, Part II: analytical evaluating and practical measuring methods for three-point bending notched beams. Int J Fracture1999; 98(2): 151–177.
15.
RamalhoLDCBelinhaJCampilhoRDSG.The numerical simulation of crack propagation using radial point interpolation meshless methods. Eng Anal Bound Elem2019; 109: 187–198.
16.
SaloustrosSCerveraMPelàL.Challenges, tools and applications of tracking algorithms in the numerical modelling of cracks in concrete and masonry structures. Arch Comput Method E2019; 26: 961–1005.
17.
KimJKKimYY. Fatigue crack growth of high-strength concrete in wedge-splitting test. Cement Concrete Res1999; 29(5): 705–712.
18.
MuralidharaSPrasadBKREskandariH, et al. Fracture process zone size and true fracture energy of concrete using acoustic emission. Constr Build Mater2010; 24(4): 479–486.
19.
BehniaAChaiHKRanjbarN, et al. Damage detection of SFRC concrete beams subjected to pure torsion by integrating acoustic emission and Weibull damage function. Struct Control Hlth2016; 23(1): 51–68.
20.
HanQYangGXuJ.Experimental study on the relationship between acoustic emission energy and fracture energy of crumb rubber concrete. Struct Control Hlth2018; 25: e2240.
21.
ZhangYKarnatiSPanT, et al. Determination of constitutive relation from miniature tensile test with digital image correlation. J Strain Anal Eng2020; 55: 99–108.
22.
CorrDAccardiMGraham-BradyL, et al. Digital image correlation analysis of interfacial debonding properties and fracture behavior in concrete. Eng Frac Mech2007; 74(1–2): 109–121.
23.
DongWWuZZhouX, et al. FPZ evolution of mixed mode fracture in concrete: experimental and numerical. Eng Fail Anal2017; 75: 54–70.
24.
RajaramSVanniamparambilPAKhanF, et al. Full-field deformation measurements during seismic loading of masonry buildings. Struct Control Hlth2017; 24: e1903.
25.
JGJ 52-2006. Standard for quality and inspection method of sand and stone for ordinary concrete.
26.
RILEM Technical Committee 50-FMC. Determination of the fracture energy of mortar and concrete by means of three-point bend tests on notched beams. Proposed RILEM Draft Recomm1985; 18(106): 285–296.
27.
SkarżyńskiŁTejchmanJ. Experimental investigations of fracture process using DIC in plain and reinforced concrete beams under bending. Strain2013; 49(6): 521–543.
28.
HillerborgAModéerMPeterssonPE.Analysis of crack formation and crack growth in concrete by means of fracture mechanics and finite elements. Cement Concrete Res1976; 6(6): 773–781.
29.
JenqYShahSP.Two parameter fracture model for concrete. ASCE J Eng Mech1985; 111(10): 1227–1241.
30.
YuKYuJLuZ, et al. Fracture properties of high-strength/high-performance concrete (HSC/HPC) exposed to high temperature. Mater Struct2016; 49(11): 4517–4532.
31.
HuSZhangXXuS.Effects of loading rates on concrete double-K fracture parameters. Eng Fract Mech2015; 149: 58–73.
32.
DasSAguayoMDeyV, et al. The fracture response of blended formulations containing limestone powder: evaluations using two-parameter fracture model and digital image correlation. Cement Concrete Comp2014; 53: 316–326.
33.
HuXWittmannF.Size effect on toughness induced by crack close to free surface. Eng Fract Mech2000; 65(2–3): 209–221.
34.
KarihalooBLMurthyARIyerNR.Determination of size-independent specific fracture energy of concrete mixes by the tri-linear model. Cement Concrete Res2013; 49: 82–88.
35.
KarihalooBLAbdallaHMImjaiT.A simple method for determining the true specific fracture energy of concrete. Mag Concrete Res2003; 55(5): 471–481.
36.
GuineaGVPlanasJElicesM.Measurement of the fracture energy using three-point bend tests: part 1—influence of experimental procedures. Mater Struct1992; 25(4): 212–218.
37.
PlanasJElicesMGuineaGV.Measurement of the fracture energy using three-point bend tests: part 2—influence of bulk energy dissipation. Mater Struct1992; 25(5): 305–312.
38.
ElicesMGuineaGVPlanasJ.Measurement of the fracture energy using three-point bend tests: part 3—influence of cutting the P- tail. Mater Struct1992; 25(6): 327–334.
39.
MurthyRAKarihalooBLIyerNR, et al. Bilinear tension softening diagrams of concrete mixes corresponding to their size-independent specific fracture energy. Constr Build Mater2013; 47: 1160–1166.
40.
ZhangXXRuizGYuRC, et al. Fracture behaviour of high-strength concrete at a wide range of loading rates. Int J Impact Eng2009; 36(10–11): 1204–1209.
41.
PeterssonPE.Crack growth and development of fracture zones in plain concrete and similar materials. Report TVBM 1006, December1981. Lund: Division of Building Materials, University of Lund.