Simulation of failure of air plasma sprayed thermal barrier coating due to interfacial and bulk cracks using surface-based cohesive interaction and extended finite element method
Restricted accessResearch articleFirst published online February, 2016
Simulation of failure of air plasma sprayed thermal barrier coating due to interfacial and bulk cracks using surface-based cohesive interaction and extended finite element method
This article describes a method of predicting the failure of a thermal barrier coating system due to interfacial cracks and cracks within bulk coatings. The interfacial crack is modelled by applying cohesive interfaces where the thermally grown oxide is bonded to the ceramic thermal barrier coating. Initiation and propagation of arbitrary cracks within coatings are modelled using the extended finite element method. Two sets of parametric studies were carried out, concentrating on the effect of thickness of the oxide layer and that of initial cracks within the ceramic coating on the growth of coating cracks and the subsequent failures. These studies have shown that a thicker oxide layer creates higher tensile residual stresses during cooling from high temperature, leading to longer coating cracks. Initial cracks parallel to the oxide interface accelerate coating spallation, and simulation of this process is presented in this article. By contrast, segmented cracks prevent growth of parallel cracks which can lead to spallation.
SchlichtingKWPadtureNPJordanEH. Failure modes in plasma-sprayed thermal barrier coatings. Mat Sci Eng A: Struct2003; 342: 120–130.
2.
NaumenkoDShemetVSingheiserL. Failure mechanisms of thermal barrier coatings on MCrAlY-type bondcoats associated with the formation of the thermally grown oxide. J Mater Sci2009; 44: 1687–1703.
3.
BhatnagarHGhoshSWalterME. A parametric study of damage initiation and propagation in EB-PVD thermal barrier coatings. Mech Mater2010; 42: 96–107.
SoulignacRMaurelVRémyL. Cohesive zone modelling of thermal barrier coatings interfacial properties based on three-dimensional observations and mechanical testing. Surf Coat Tech2013; 237: 95–104.
6.
SeilerPBäkerMRösierJ. FEM simulation of oxidation induced stresses with a coupled crack propagation in a TBC model system. IOP C Ser Mater Sci Eng2010; 10: 012056.
7.
HilleTSNijdamTJSuikerASJ. Damage growth triggered by interface irregularities in thermal barrier coatings. Acta Mater2009; 57: 2624–2630.
8.
HilleTSSuikerASJTurteltaubS. Microcrack nucleation in thermal barrier coating systems. Eng Fract Mech2009; 76: 813–825.
9.
XieLChenDJordanEH. Formation of vertical cracks in solution-precursor plasma-sprayed thermal barrier coatings. Surf Coat Tech2006; 201: 1058–1064.
10.
HermosillaU. Mechanical modelling of thermal barrier coatings at high temperatures. PhD Thesis, The University of Nottingham, Nottingham, 2008.
11.
MaurelVBussoEPFrachonJ. Int J Solids Struct2014; 51(19): 3293–3330.
12.
Abaqus. User’s Manual version 6.11 Dassault Systemes Simulia Corporation, Providence, RI 02919, 2011.
13.
SharmaC. Displacement/mixed finite element formulation for beam and frame problems. Master’s Thesis, University of Pavia, Pavia, 2007.
14.
MartenaMBottoDFinoP. Modelling of TBC system failure: stress distribution as a function of TGO thickness and thermal expansion mismatch. Eng Fail Anal2006; 13: 409–426.
15.
RabieiAEvansAG. Failure mechanisms associated with the thermally grown oxide in plasma-sprayed thermal barrier coatings. Acta Mater2000; 48: 3963–3976.
16.
WrightPKEvansAG. Mechanisms governing the performance of thermal barrier coatings. Curr Opin Solid St M1999; 4: 255–265.
17.
BäkerMRöslerJHeinzeG. A parametric study of the stress state of thermal barrier coatings. Part II: cooling stresses. Acta Mater2005; 53: 469–476.
18.
BelytschkoTBlackT. Elastic crack growth in finite elements with minimal remeshing. Int J Numer Meth Eng1999; 45: 601–620.
19.
MelenkJMBabuskaI. Approximation with harmonic and generalized harmonic polynomials in the partition of unity method. Comput Assist Mech Eng Sci1997; 4: 607–632.
20.
BelytschkoTGracieRVenturaG. A review of extended/generalized finite element methods for material modeling. Model Simul Mater Sci2009; 17(4): 043001.
21.
AlfanoGCrisfieldMA. Finite element interface models for the delamination analysis of laminated composites: mechanical and computational issues. Int J Numer Meth Eng2001; 50: 1701–1736.
22.
KyawSTJonesIAHydeTH. Predicting failure within TBC system: finite element simulation of stress within TBC system as affected by sintering of APS TBC, geometry of substrate and creep of TGO. Eng Fail Anal2013; 27150–164.
ZhuDMillerR. Thermal conductivity and elastic modulus evolution of thermal barrier coatings under high heat flux conditions. J Therm Spray Techn2000; 9: 175–180.
25.
MunroRG. Evaluated material properties for a sintered alpha-alumina. J Am Ceram Soc1997; 80: 1919–1928.
26.
BaiamonteLMarraFPulciG. High temperature mechanical characterization of plasma-sprayed zirconia-yttria from conventional and nanostructured powders. Surf Coat Tech2015; 277: 289–298.
27.
LughiVTolpygoVKClarkeDR. Microstructural aspects of the sintering of thermal barrier coatings. Mat Sci Eng A: Struc2004; 368: 212–221.
28.
ShinozakiMClyneTW. A methodology, based on sintering-induced stiffening, for prediction of the spallation lifetime of plasma-sprayed coatings. Acta Mater2013; 61: 579–588.
29.
ThompsonJAJiWKlockerT. Sintering of the top coat in thermal spray TBC systems under service conditions. In: PollockTMKissingerRDBowmanRR. (eds) Ninth international symposium on superalloys, Champion, PA, 17–21 September 2000. Seven Springs, PA: TMS, pp.685–692.
30.
CipitriaAGolosnoyIOClyneTW. Sintering kinetics of plasma-sprayed Zirconia TBCs. In: 2007 international thermal spray conference, Beijing, China, 14–16 May 2007, pp.434–439. Materials Park, OH: ASM International.
31.
BussoEPEvansHEQianZQ. Effects of breakaway oxidation on local stresses in thermal barrier coatings. Acta Mater2010; 58: 1242–1251.
32.
BussoEPLinJSakuraiS. A mechanistic study of oxidation-induced degradation in a plasma-sprayed thermal barrier coating system. Part I: model formulation. Acta Mater2001; 49: 1515–1528.
33.
BussoEP. Oxidation-induced stresses in ceramic-metal interfaces. J Phys IV France1999; 9: Pr9-287–Pr9-296.
34.
RöslerJBäkerMAufzugK. A parametric study of the stress state of thermal barrier coatings–Part I: creep relaxation. Acta Mater2004; 52: 4809–4817.
35.
BussoEPQianZQTaylorMP. The influence of bondcoat and topcoat mechanical properties on stress development in thermal barrier coating systems. Acta Mater2009; 57: 2349–2361.
36.
HermosillaUKarunaratneMSAJonesIA. Modelling the high temperature behaviour of TBCs using sequentially coupled microstructural-mechanical FE analyses. Mat Sci Eng A: Struct2009; 513–514: 302–310.
37.
MaharjanSZhangXCXuanFZ. Residual stresses within oxide layers due to lateral growth strain and creep strain: analytical modeling. J Appl Phys2011; 110: 063511.
38.
KondohJShiotaHKawachiK. Yttria concentration dependence of tensile strength in yttria-stabilized zirconia. J Alloy Compd2004; 365: 253–258.
39.
AdamsJWRuhRMazdiyasniKS. Young’s modulus, flexural strength, and fracture of yttria-stabilized zirconia versus temperature. J Am Ceram Soc1997; 80: 903–908.
40.
GellMEricJKrishnakumarV. Bond strength, bond stress and spallation mechanisms of thermal barrier coatings. Surf Coat Tech1999; 120–121: 53–60.
41.
OkazakiMYamazakiYNambaK. Collaborative research on adhesion strength of thermal barrier coatings in JSMS. J Solid Mech Mater Eng2010; 4(2): 252–263.
42.
BerndtC. Instrumented tensile adhesion tests on plasma sprayed thermal barrier coatings. J Mater Eng1989; 11: 275–282.
43.
SeraffonMSimmsNJNichollsJR. Performance of thermal barrier coatings in industrial gas turbine conditions. Mater High Temp2011; 28: 309–314.
44.
KrasuckiFLenciS. Analysis of interfaces of variable stiffness. Int J Solids Struct2000; 37: 3619–3632.
45.
StollbergDWHampikianJMRiesterL. Nanoindentation measurements of combustion CVD Al2O3 and YSZ films. Mat Sci Eng A: Struct2003; 359: 112–118.
46.
YamazakiYKugaSYoshidaT. valuation of interfacial strength by an instrumented indentation method and its application to an actual TBC vane. Acta Metall Sin2011; 24: 109–117.
47.
Ranjbar-FarMAbsiJMariauxG. Simulation of the effect of material properties and interface roughness on the stress distribution in thermal barrier coatings using finite element method. Mater Design2010; 31: 772–781.