Heterophase polymerisation of styrene was carried out, and nanocomposite polystyrene microspheres with a controllable content of ZnO nanoparticles were synthesised. The colloid chemical properties of the obtained polymer suspensions were studied, and it was shown that the particles have a ‘core–shell’ structure with a ZnO content of up to 30%.
GritskovaI.A., The synthesis of polymer microspheres containing inorganic nanoparticles. Vestn. MITKhT, 6(5): 9–20 (2011).
3.
Van HerkA.M., Historical overview of (mini) emulsion polymerizations and preparation of hybrid latex particles. Adv. Polym. Sci., (233): 1–18 (2010).
4.
ZhachenkovS.V., The influence of the disperse composition of emulsions on the kinetic behaviour patterns governing the polymerisation of water-insoluble monomers. Doct. Chem. Sci. Dissertation, Moscow, 280 pp. (2013).
5.
LandfesterK., Preparation of polymerisable miniemulsions by ultrasonication. J. Coat. Technol., 1(1): 65–68 (2004).
6.
GoetzR.J., Investigation of the supramolecular structure of a dilute gel phase. J. Colloid Interface Sci., 137(2): 395–407 (1990).
7.
ProkopovN.I., The production of polymer composite microspheres with zinc oxide nanoparticles on their surface. Plast. Massy, (12): 27–32 (2013).
8.
SerkhachevaN.S., The polymerisation of styrene in highly disperse emulsions in the presence of sodium dodecyl sulphate, cetyl alcohol, and their mixture, and a study of the behaviour of the surfactants in monolayers at the air–water boundary. Plast. Massy, (9-10): 15–20 (2014).
9.
DazhiS., Purification and stabilization of colloidal ZnO nanoparticles in methanol. J. Sol–Gel Technol., 43: 237–243 (2007).
10.
MateiA., Synthesis and characterization of ZnO–polymer nanocomposites. Int. J. Mater. Form., 1: 767–770 (2008).