To evaluate the hot deformation behavior of Al0.6CoCrFeNi high entropy alloy, the elevated temperature compression tests were performed. The flow stress decreased as the temperature increased and the strain rate decreased. The shape of the flow curves exhibits that the alloy was undergone the dynamic restoration behavior. The constitutive relationships and processing maps were established, and the optimal hot working condition of 950 °C and 10 s−1 was confirmed through the correlation of temperature-strain rate-strain rate. Deformed microstructure through EBSD analysis revealed that the discontinuous dynamic recrystallization acts as the main dynamic restoration mechanism of the alloy.
KaoYFChenTJ. Microstructure and mechanical property of as-cast, homogenized, and deformed AlxCoCrFeNi (0 ≤ x≤2) high-entropy alloys. J Alloy Compd2009; 488: 57.
4.
LiZZhaoSDiaoH, et al.High-velocity deformation of Al0.3CoCrFeNi high-entropy alloy: remarkable resistance to shear failure. Sci Rep2017; 7: 42742.
5.
ZhangJDiHWangH, et al.Hot deformation behavior of Ti-15-3 titanium alloy: a study using processing maps, activation energy map, and Zener-Hollomon parameter map. J Mater Sci2012; 47: 4000.
6.
SellarsCMcTegartW. On the mechanism of hot deformation. Acta Metall1966; 14: 1136.
7.
MalasJ.Methodology for design and control of thermomechanical processes. Ph.D dissertation, Ohio University.
8.
ShiCMaoWChenX. Evolution of activation energy during hot deformation of AA7150 aluminum alloy. Mater Sci Eng A2013; 571: 83.
9.
AsgharzadehHSimchiAKimH. Microstructure, strengthening mechanisms and hot deformation behavior of an oxide-dispersion strengthened UFG Al6063 alloy. Mater. Charact2013; 75: 08.
10.
GavgaliMAksakalB. Effects of various homogenization treatments on the hot workability of ingot aluminum alloy AA2014. Mater Sci Eng A2002; 254: 15.
11.
PrasadYVRK. Author’s reply: dynamic materials model: basis and principles. Metall Mater Trans A1996; 27: 35.
12.
PrasadYVRKSasidharaS. Hot working guide: a compendium on processing maps. Novelty, OH: ASM International, 1997, 1.
13.
ShuXLuSWangK, et al.Optimization of hot working parameters of as-forged Nitinol 60 shape memory alloy using processing maps. Met Mater Int2015; 21: 26.
14.
KilTDHanSWMoonYH. Studies on quantitative estimation of hot forgeability by using deformation processing map. Korean J Met Mater2014; 52: 31.
15.
GongMBolongLHongmeiL, et al.Hot deformation and processing maps of an Al–5.7 wt.% Mg alloy with erbium. Mater Sci Eng A2009; 517: 32.
16.
SonHWJungTKLeeJW, et al.Hot deformation characteristics of CaO-added AZ31 based on kinetic models and processing maps. Mater Sci Eng A2017; 695: 79.
17.
McQueenHEvangelistaEJinN, et al.Energy dissipation efficiency in aluminum dependent on monotonic flow curves and dynamic recovery. Metall Mater Trans A1995; 26: 1757.
18.
HumphreysF. J.HatherlyM. Recrystallization and related annealing phenomena. 2nd edn. Oxford: Elsevier, 2004, 415–466.
19.
JonasJJ. Dynamic recrystallization—scientific curiosity or industrial tool?Mater Sci Eng A1994; 184: 55.
20.
McQueenHJBlumW. Dynamic recovery: sufficient mechanism in the hot deformation of Al (<99.99). Mater Sci Eng A2000; 290: 95.
GjestlandHLohneORyumN. The effect of quenching on recrystallization after hot working. Metall Trans A1978; 9: 1892.
23.
CerriEEvangelistaEForcelleseA, et al.Comparative hot workability of 7012 and 7075 alloys after different pretreatments. Mater Sci Eng A1995; 197: 81.
24.
Avramovic-CingaraGMcQueenHJPerovicDD. Comparison of torsion and compression constitutive analyses for elevated temperature deformation of Al–Li–Cu–Mn alloy. Mater Sci Technol2003; 19: 11.
25.
LeeJWJungTKYoonYO, et al.Continuous dynamic recrystallization behavior and kinetics of Al–Mg–Si alloy modified with CaO-added Mg. Mater Sci Eng A2016; 673: 48.
26.
VerlindenBDriverJSamajdarI, et al.Thermo-mechanical processing of metallic materials. Amsterdam/Netherlands: Elsevier, 2007, 83.