In this study, the corrosion behaviour of X65MS/ N08825 composite pipe welded joints during immersion was investigated using an electrochemical workstation and scanning electrochemical microscopy techniques. When the immersion time was more than 24 h, significant corrosion craters appeared in the weld area, with a maximum depth of 7.05 μm, and the corresponding self-corrosion potentials and self-corrosion current densities were −781 mV and 11.82 μA/cm². When the immersion time was extended to 48 h, the depth of the corrosion crater further increased to 15.23 μm, and the self-corrosion potential and self-corrosion current density were −816 mV and 23.73 μA/cm², respectively.
MehtaSJhaSLiangH. Corrosion of nickel-based alloys fabricated through additive manufacturing: a review. Progr Add Manufactur2022; 7: 1257–1273.
2.
WangYLiJQuC, et al.Research progress on corrosion of oil and gas field gathering pipeline in H2S-CO2-cl−system. IOP Confere Ser: Earth Environ Sci2020; 555: 012046.
3.
Song P, Wang W and Jia X. Corrosion study of 80S steel under the coexistence of CO2 and H2S. Metals 2022; 12: 1923.
4.
LazarevaAOwenJVargasS, et al.Investigation of the evolution of an iron carbonate layer and its effect on localized corrosion of X65 carbon steel in CO2 corrosion environments. Corros Sci2021; 192: 109849.
5.
ShuxinZFaqinXXianmingL, et al.Failure analysis of the leakage in girth weld of bimetal composite pipe. Eng Failure Anal2023; 143: 106917.
6.
LeiXFengYZhangJ, et al.Impact of reversed austenite on the pitting corrosion behavior of super 13Cr martensitic stainless steel. Electr Acta2016; 191: 640–650.
7.
XuLYJingHYHanYD. Effect of welding on the corrosion behavior of X65/inconel 625 in simulated solution. Weld World2018; 62: 363–375.
8.
AbioyeTEFarayibiPKMccartneyDG, et al.Effect of carbide dissolution on the corrosion performance of tungsten carbide reinforced inconel 625 wire laser coating. J Mater Process Technol2016; 231: 89–99.
9.
WangBLanHLeiB. Effect of welding method on microstructure and mechanical properties of L360QS/N08825 composite pipe welded joint. Trans Indian Inst Metals2020; 73: 629–643.
10.
WangBLeiB-BWangW, et al.Investigations on the crack formation and propagation in the dissimilar pipe welds involving L360QS and N08825. Eng Failure Anal2015; 58: 56–63.
11.
WangFWangEZhangL, et al.Influence of electromagnetic stirring (EMS) on the microstructure and mechanical property of Incoloy825 superalloy. J Manufactu Process2017; 26: 364–371.
12.
LiuSFengJLuoX, et al.Effect of special grain boundary on hot corrosion path in Incoloy825 alloy. J Mater Sci2022; 57: 15560–15580.
13.
SayyarNShamanianMNiroumandB, et al.EBSD Observations of microstructural features and mechanical assessment of INCOLOY 825 alloy/AISI 321 stainless steel dissimilar welds. J Manufactur Process2020; 60: 86–95.
14.
KangazianJShamanianM. Micro-texture and corrosion behavior of dissimilar joints of UNS S32750 stainless steel/UNS N08825 Ni-based superalloy. Mater Character2019; 155: 109802.
15.
XuLZhangJHanY, et al.Insights into the intergranular corrosion of overlay welded joints of X65-Inconel 625 clad pipe and its relationship to damage penetration. Corros Sci2019; 160. DOI:https://doi.org/10.1016/j.corsci.2019.108169.
16.
WangBZhangTLiuY, et al.Corrosion damage behavior of X65/incoloy 825 welded bimetallic composite pipe in H2S environment. Front Mater Sci 2021; 8. DOI: https://doi.org/10.3389/fmats.2021.709101
17.
ZhangNZengD. Research on TIG welding gap corrosion resistance of X52/825 metallurgical clad pipein H2S/CO2 environment. Anti-Corros Method Mater2019; 66: 412–417.
18.
LiYZXuNLiuGR, et al.Crevice corrosion of N80 carbon steel in CO2−saturated environment containing acetic acid. Corros Sci2016; 112: 426–437.
19.
RihanRZafarMNAl-HadhramiL. A novel emulsion flow loop for investigating the corrosion of X65 steel in emulsions with H2S/CO2. J Mater Eng Perform2016; 25: 3065–3073.
20.
CieslakMJHeadleyTJRomigAD, et al.A melting and solidification study of alloy 625, metall. Trans A1988; 19: 2319–2331.
21.
GaoDY-TBinMYuan-junM, et al.Research progress in evolution of precipitated phases in inconel 625 superalloy. J Mater Eng2020; 48: 13–22.
22.
LiQJiaWYangK, et al.CO2 Corrosion behavior of X70 steel under typical gas–liquid intermittent flow. Metals2023; 13: 1239.
23.
BarkerRBurkleDCharpentierT, et al.A review of iron carbonate (FeCO3) formation in the oil and gas industry. Corros Sci2018; 142: 312–341.
24.
ShehzadAArslanARehmanF, et al.Corrosion behavior of copper, aluminium, and stainless steel 316L in chicken fat oil based biodiesel-diesel blends. Sustain Energy Technol Assess2023; 56: 103089.
25.
GongQWuHYangF, et al.Corrosion of pipeline steel weld metals containing alloying elements in CO2/H2S environment. Gas Sci Eng2023; 109: 104846.
26.
ColeISCorriganPSimS,et al.Corrosion of pipelines used for CO2 transport in CCS: is it a real problem?Int J Greenh Gas Control2011; 5: 749–756.
27.
ZhangNZengDXiaoG, et al.Effect of cl− accumulation on corrosion behavior of steels in H2S/CO2 methyldiethanolamine (MDEA) gas sweetening aqueous solution. J Nat Gas Sci Eng2016; 30: 444–454.
28.
RyanMPWilliamsDEChaterRJ, et al.Why stainless steel corrodes. Nature2002; 415: 770–774.
29.
KimSJHongSGOhM-s. Effect of metallurgical factors on the pitting corrosion behavior of super austenitic stainless steel weld in an acidic chloride environment. J Mater Res2017; 32: 1343–1350.