This study investigated the effect of in-situ alloying of Ti6Al4V and TiB2 during laser metal deposition for microstructure, hardness and tensile properties enhancement. It was found that the addition of TiB2 at powder feed rates of range 0.1–0.3rpm resulted in the formation of TiB whiskers with columnar and equiaxed network morphologies, in a lamella α + β matrix. By increasing TiB2 at 0.4–0.5rpm, a complete dissolution of the equiaxed and columnar network morphologies were achieved. The dissolution led to a random distribution of formed TiB whiskers, resulting in enhanced hardness and ultimate tensile strength (UTS), with the 0.5rpm giving the highest hardness and UTS values of 511 ± 13 HV and 1745 MPa, respectively.
LekoadiPMTlotlengMMasinaBN. Effect of substrate heating on the microstructure and hardness of TiB/Ti6Al4V-ELI during laser in-situ metal deposition. In: Conference of the South African advanced material initiative. DOI: 10.3603/SATNT.2021cosaami.12.
2.
ZhangQSunWXuS, et al.Nano TiB whiskers reinforced Ti6Al4V matrix composite fabricated by direct laser deposition: microstructure and mechanical properties. J Alloys Compd2022; 922: 1–12.
3.
WangJLiLLinP,et al.Effect of TiC particle size on the microstructure and tensile properties of TiCp/Ti6Al4V composite fabricated by laser metal deposition. Opt Laser Technol2018; 105: 195–206.
4.
ShivakumarGAnanthiVRamanathanS. Production and mechanical properties of nano SiC particle reinforced Ti6Al4V matrix composite. Trans Nonferrous Met Soc China2017; 27: 82–90.
5.
FereiduniEGhasemiAElbestawiM. Unique opportunities for microstructure engineering via trace B4C addition to Ti6Al4V through laser powder bed fusion process: as-built and heat treated scenarios. Addit Manuf2022; 50: 1–19.
6.
GuDHongCMengG. Densification, microstructure and wear property of in-situ titanium nitride-reinforced titanium silicide matrix composites prepared by a novel selective laser melting process. Metall Mater Trans A2012; 43: 697–708.
ZhangWZhouSRenW, et al.Uniformly dispersing GNPs for fabricating graphene reinforced pure Ti matrix composite with enhanced strength and ductility. J Alloys Compd2021; 888: 161527.
9.
HayatDMSinghHHeZ,et al.Titanium metal matrix composites: an overview. Compos Part A Appl Sci Manuf2019; 121: 418–438.
10.
KondohK. Titanium metal matrix composites by powder metallurgy (PM) routes. Titanium Powder Metall2015: 277–297. DOI: 10.1016/B978-0-12-800054-0.00016-2.
11.
WeiSLHuangLJLiXT, et al.Interactive effects of cyclic oxidation and structural evolution of Ti6Al4V/(TiC + TiB) alloy composite at elevated temperatures. J Alloys Compd2013; 752: 69–175.
SighGRamamurtyU. Boron modified titanium alloys. Prog Mater Sci2020; 111: 1–54.
14.
XueALinXWangL, et al.Influence of traces of boron addition on microstructure, tensile properties, and their anisotropy of Ti6Al4V fabricated by laser directed energy deposition. Mater Des2019; 181: 1–15.
15.
HuangLAnQGengL. Multiscale architecture and superior high-temperature performance of discontinuously reinforced titanium matrix composites. Adv Mater2021; 33: 1–27.
16.
PanDLiSLiuL, et al.Enhanced strength and ductility of nano-TiBw-reinforced titanium matrix composites fabricated by electron beam powder bed fusion using Ti6Al4V–TiBw composite powder. Addit Manuf2022; 50: 1–15.
17.
WangZWFuLQWangSL, et al.Balance of strength and plasticity of additive manufactured Ti6Al4V alloys by forming TiB whiskers with cyclic gradient distribution. Addit Manuf2021; 39: 1–12.
18.
NiuJDaiGGuoY, et al.Microstructure and mechanical properties of B modified Ti-Fe alloy manufactured by casting, forging and laser melting deposition. Compos B: Eng2021; 261: 1–10.
19.
SousaBCCoteDL. Profilometry-based indentation plastometry brings speed and accuracy to metallurgical R&D. Adv Mater Process2022; 19: 19–24.
20.
VermaPKWarghaneSNichulU, et al.Effect of boron addition on microstructure, hardness and wear performance of Ti6Al4V alloy manufactured by laser powder bed fusion additive manufacturing. Mater Charact2021; 172: 1–11.
21.
DolgunEZemlyakovEShalnovaS, et al.The influence of heat treatment on the microstructure of products manufactured by direct laser deposition using titanium alloy Ti6Al4V. Mater Today2020; 30: 688–693.
22.
LekoadiPTlotlengMAnnanK, et al.Evaluation of heat treatment parameters on microstructure and hardness properties of high-speed selective laser melted Ti6Al4V. Metals2021; 255: 1–15.
23.
HuangLJGengLXueHY, et al.In situ TiC particles Ti6Al4V matrix composite reinforced with a network reinforcement architecture. Mater Sci Eng A2011; 528: 2859–2862.
24.
HuangLJGengLPengHX. Microstructurally inhomogeneous composites: is a homogeneous distribution optimal?Prog Mater Sci2015; 71: 93–168.
25.
GuptaAKhatirkarRKKumarA,et al.Investigation on the effects of heating temperature and cooling rate on evolution of microstructure in α+β titanium alloys. Mater Res Soc2018; 54: 1–12.
26.
FereiduniEGhasemiAElbestawiM. Tib reinforced Ti6Al4V matrix composites with improved short-term creep performance fabricated by laser powder bed fusion. J Manuf Proc2021; 70: 593–607.
27.
CaiCHeSLiL, et al.In situ TiB/Ti6Al4V composite with a tailored architecture produced by hot isostatic pressing: microstructure evolution, enhanced tensile properties and strengthening mechanism. Compos B: Eng2019; 164: 546–558.
28.
ZubackJSDebroyT. Hardness of additively manufactured alloys. Materials2018; 11: 2–41.
29.
KeistJSPalmerTA. Development of strength-hardness relationship in additively manufactured titanium alloys. Mater Sci Eng A2017; 693: 214–224.
AzarniyaAColeraXGMirzaaliMJ, et al.Additive manufacturing of Ti6Al4V parts through laser metal deposition (LMD): process, microstructure, and mechanical properties. J Alloys Compd2019; 804: 163–191.
32.
LiuSShinYC. Additive manufacturing of Ti6Al4V alloy: a review. Mater Des2019; 164: 107552.
33.
WhangSH. Rapidly solidified titanium alloys for high temperature applications. J Mater Sci1986; 21: 2224–2238.
34.
JeongHKimSHyunY,et al.Densification, and compressive strength of in-situ processed Ti/TiB composites by powder metallurgy. Met Mater Int2002; 8: 25–35.
Supplementary Material
Please find the following supplemental material available below.
For Open Access articles published under a Creative Commons License, all supplemental material carries the same license as the article it is associated with.
For non-Open Access articles published, all supplemental material carries a non-exclusive license, and permission requests for re-use of supplemental material or any part of supplemental material shall be sent directly to the copyright owner as specified in the copyright notice associated with the article.