Elastic Recovery of Rubber Vulcanizates at Very Short Times

Abstract

Elastic recovery is a measure of the extent to which a rubber specimen regains its original dimensions after release of an imposed strain. A recoverable strain and rate of recovery after prolonged aging under compression in the environment of intended use are important factors in characterizing rubber performance characteristics. So far the recoverable strain and its rate at very short time intervals have not been studied. Therefore, the present study describes an instrument and reliable method for measuring elastic recovery after release of compressive strain within time periods from 0.007 to 0.1 s. Significant differences are observed in both recoverable strains and their rates measured within these short time periods for the different rubber vulcanizates after aging. Data obtained for various rubbers aged in different environments are fitted to power law and Williams-Watts equations relating elastic strain with time after release of stress. The intercept in the power law equation and characteristic time in Williams-Watts equation are found to be very sensitive to changes in the elastic recovery of various rubbers during aging. The designed testing procedures will make possible the ability to discriminate different rubber materials intended for use in sealing applications, especially those used in dynamic seals. A comparison between novel and traditional measurements is also given.

Keywords

elastic recovery aging seals compression set stress relaxation characteristic time

Get full access to this article

View all access options for this article.

References

1. Gent, A. N. Ed. 1992. Engineering with Rubber Hanger, Munich.

2. Treloar, L. R. G. . 1974. The Physics of Rubber Elasticity, 2nd Ed., Oxford, London.

3. Tobolsky, A. V. 1960. Properties and Structure of Polymers, Wiley, New York.

4. White, J. L. and I. Soos . 1993. Rubber Chem. Tech., 66:435.

5. Thomas, D. K. 1966. Polymer, 7:125.

6. Kalfayan, S. H. , R. H. Silver , and A. A. Mazzeo . 1975. Rubber Chem. Tech., 48:944.

7. Qgunnyi, D. S. 1987. Europ. Polym. J., 23:557.

8. Stenberg, B. and J. F. Jansson . 1977. Rubber Chem., Tech., 50:906.

9. ATSM D 1390-76. 1987. Rubber Property—Stress Relaxation, Vol. 9.01, p. 316.

10.

10. BS 903, Part A42. 1983. "Determination of Stress Relaxation in Compression," British Standards Institution.

11.

11. DIN 53 517. 1977. "Testing of Elastomers: Determination of Stress Relaxation in Compression," Deutschen Normenausschuss.

12.

12. ISO 3384-1975. 1979. "Rubber Vulcanized-Determination of Stress Relaxation in Compression at Normal and Elevated Temperatures," International Standards Organization.

13.

13. Burton, T. , J. L. Delanaye , and C. P. Rader . 1988. Paper #28, presented at the Intern. Rubber Conf., Sydney, Australia, October.

14.

18(11):16.

15.

15. Bunting, W. , G. H. Slocum , and W. D. Russell . 1992. Paper #93, presented at the 142nd ACS Rubber Division Meeting, Nashville, Tennessee.

16.

16. Armah, J. C. , A. W. Birley , K. P. Fernando , C. Hepburn , and M. Tahir . 1986. Rubber Chem. Tech., 59:765.

17.

17. McKenna, G. B. . and R. J. Gaylord . 1988. Polymer, 29:2027.

18.

18. Nagdi, K. 1989. Kautschuk Gummi Kunststoffe, 42:236.

19.

19. Birley, A. W. , K. P. Fernando , and M. Tahir . 1986. Polymer Testing, 6:85.

20.

20. Zhang, Y. and A. W. Birley . 1992. Progress in Rubber and Plastics Technol., 8:318.

21.

21. Fernando, K. P. , A. W. Birley , C. Hepburn , and N. Wright . 1983. Polymer Testing, 3:209.

22.

22. Ellul, M. D. and F. Southern . 1985. Plastics Rubber Processing Applications, 5:61.

23.

23. Dunn, J. R. , G. C. Blackshaw , and J. Timar . 1986. Elastomerics, 118:20.

24.

24. Cook, W. D. 1981. J. Biomed. Mater. Res., 15:449.

25.

25. Stenberg, B. , F. Björkman , and O. Dickman . 1982. Polymer Testing, 3:63.

26.

26. Björk, F. and B. Stenberg . 1988. Plast. Rubber Process. Appl., 9:227.

27.

27. Björk, F. and B. Stenberg . 1990. Polymer, 31:1649.

28.

28. Björk, F. and B. Stenberg . 1988. Kautschuk Gummi Kunststoffe, 41:44.

29.

29. Björk, F. , O. Dickman , and B. Stenberg . 1989. Rubber Chem. Tech., 62:387.

30.

30. ASTM D 395. 1987. Rubber Property—Compression Set, Vol. 9.01, p. 34.

31.

31. ISO 815-1972. 1972. "Vulcanized Rubbers—Determination of Compression Set under Constant Deflection at Normal and High Temperature," Intern. Standards Organization.

32.

32. NF T46-011. 1977. "Test for Residual Deformation After Compression at Constant Deformation," Norme Francaise.

33.

33. Prabhu, A. M. , A. W. Birley , and R. H. Sigley . 1991. Polymer Testing, 10:39.

34.

34. Dunn, D. R. and H. A. Pfisterer . 1977. J. Elast. Plast., 9:193.

35.

35. Dunn, J. R. 1983. Paper #42, presented at the 124th Meeting of the ACS, Rubber Division, Houston, Texas, October.

36.

36. Scheerer, K. 1990. Kunststoffe German Plastics, 80:25.

37.

37. Williams, G. and D. C. Watts . 1970. Trans. Faraday Soc, 66:80.

38.

38. Brostow, W. 1981. Macromol. Chem., Macromol. Symp., 41:119.

39.

39. Ho, T. , J. Mijovic , and C. Lee . 1991. Polymer, 32:619.

40.

40. Aston, M. W. 1975. Lucas Eng. Review, 6:90.

41.

41. Brown, R. P. 1986. Physical Testing of Rubber, Elsevier, London, 2nd Edition.

42.

42. Buchter, H. H. 1979. Industrial Sealing Technology, Wiley, New York.

43.

43. Hughes, W. D. 1985. Rubber Plast. News, Aug. 26.

44.

44. Nagdi, K. 1990. Kautschuk Gummi Kunststoffe, 43:228.

45.

45. Nagdi, K. 1989. Kautschuk Gummi Kunststoffe, 42:144.

46.

46. Brink, R. V. , D. K. Czernik , and L. A. Horve . 1993. Handbook of Fluid Sealing McGraw-Hill, New York.