Influence of Glycols on the Glycolysis Process and the Structure and Properties of Polyurethane Elastomers

Abstract

In this work, the influence of glycols on the glycolysis process and the properties of obtained polyurethanes were investigated. The glycolysates were produced via glycolysis of waste polyurethane foam in the reaction with one of the following glycols: 1,3-propanediol, 1,5-pentanediol, and 1,6-hexanediol.The reactions were carried out for different mass ratios of polyurethane wastes to glycolysis agent, i.e. 6:1, 8:1, and 10:1. Polyurethanes were synthesized from the obtained intermediates by a one-step method of mixing polymeric di-isocyanate and the glycolysis products with molecular masses ranging from 700 to 1000, while a polyol (Poles 55/20) was used as a chain elongation agent. The influence of glycolysates on tensile strength and elongation at break of polyurethanes was investigated using a Zwick universal tensile tester. Thermal decomposition of the obtained glycolysates and polyurethanes was investigated by thermogravimetry coupled with Fourier transform infrared spectroscopy. It has been found that of all used glycols, 1,6-hexanediol gives the best improvement in the thermal stability of polyurethanes during the glycolysis process. The mean hardness of polyurethanes decreases but rebound resilience increases with chain length of the glycol used for obtaining glycolysates.

Keywords

polyurethane foam wastes chemical recycling glycolysates polyurethane elastomers FTIR–ATR mechanical properties

Get full access to this article

View all access options for this article.

References

Czupryński

(2004). Polyurethane Chemistry and Technology, Poland, University of Bydgoszcz Publishing.

Datta

(2010). Synthesis and Investigation of Glycolysates and Obtained Polyurethane Elastomers. J. Elast. Plast., 42: 117–127.

Modesti

Simioni

Munari

Baldoin

(1995). Recycling of Flexible Polyurethane Foams With a Low Aromatic Amine Content. React. Funct. Polym., 26: 157–163.

Gerlock

Braslaw

Zinbo

(1984). Polyurethane Waste Recycling. Glycolysis and Hydroglycolysis of Water Blown Foams. Ind. Eng. Chem. Process Dev., 23: 545–551.

Datta

Pasternak

(2005). Oligourethane Glycols Obtained in Glycolysis of Polyurethane Foam as Semi-finished Products for Cast Urethane Elastomers Preparation. Polimery, 50: 346–352.

Datta

Kacprzyk

(2007). Chemical Modification of Polyurethanes by Glycolysates Intermediates. In: XVIII Scientific Konference. Polymer Modification. Today and in the Future, Wroclaw University of Technology, 23–26 September.

Lee

J.Y.

Kim

(2000). Desaminated Glycolysis of Water-Blown Rigid Polyurethane Foams. J. Appl. Polym. Sci., 77: 2646–2651.

Datta

Rohn

(2007). Glycolysis of the Polyurethane Wastes. Part I. Glycolysis Agents and Catalyst. Polimery, 52: 627–633.

Parrinello

Thorpe

Verhelst

Hopper

J.F.G.

de Witte

M.B.A.

(1997). Recycling of Flexible Foam. U.S. Pat. 5 691 389.

10.

C.-H.

Chang

C.-Y.

J.-K.

(2002). Glycolysis of Rigid Polyurethane From Waste Refrigerators. Polym. Degrad. Stab., 75: 413–417.

11.

C.-F.

Chang

C.-Y.

Cheng

C.-M.

Huang

H.-C.

(2003). Glycolysis of Waste Flexible Polyurethane Foam. Polym. Degrad. Stab., 80: 103–108.

12.

Datta

Rohn

(2007). Thermal Properties of Polyurethanes Synthetized Using Waste Polyurethane Foam Glycolysates. J. Therm. Anal. Calorim., 88: 437–440.

13.

Nikje

M. M.

Haghshenas

Garmarudi

A. B.

(2006). Preparation and Application of Glycolysed Polyurethane Integral Skin Foams Recyclate From Automotive Wastes. Polym. Bull., 56: 257–261.

14.

Borda

Racz

Zsuga

(2002). Recycled Polyurethane Elastomers: A Universal Adhesive. J. Adhesion Sci. Technol., 16: 1225–1232.

15.

Modesti

Simioni

(1996). Chemical Recycling of Reinforced Polyurethane From the Automotive Industry. Polym. Eng. Sci., 36: 2173–2178.

16.

Naber

Schmiade

Gassan

(2000). Production of Rigid Polyurethane Foams. U.S. Pat. 6 087 409.