Effect of Water on High-Strength and High-Modulus Poly(vinyl Alcohol ) Fibers from Crosslinking Wet Spinning /Multistep Drawing

Abstract

The presence of water in poly (vinyl alcohol ) fibers spun from a water-soluble poly mer was investigated using differential scanning calorimetry, polarizing microscopy, scanning electron microscopy, and x-ray diffraction techniques. Poly( vinyl alcohol ) fibers were produced using the crosslinking wet spinning technique, which is an im provement on conventional noncrosslinked wet spinning. Borate ion-aided crosslinks were introduced during the coagulation process. Fibers had a higher drawability with the advanced wet-hot process and multi-step drawing. The tensile strength and modulus of drawn poly(vinyl alcohol ) fibers were 1.82 and 51.76 GPa, respectively. The presence of water in the fibers damaged their structure and drastically disturbed the orientation of their molecular chains. After tensile testing, there was a fractured circular layer in the fibers.

Get full access to this article

View all access options for this article.

References

Alexander, L.E. , "X-ray Diffraction Method in Polymer Science," John Wiley and Sons, NY, 1969.

Fujiwara, H. , Shibayama, M. , Chen , J.H. , and Nomura, S. , Preparation of High-Strength Poly( vinyl Alcohol) Fibers by Crosslinking Wet Spinning . J. Appl. Polym. Sci. 37, 1403-1414 (1989 ).

Hayasaki, T. , Shibayama, M. , Sakurai , S. , Nomura, S. , Fujiwara, H. , and Suehiro, S. , Structure and Molecular Orientation of High Strength Poly(vinyl Alcohol) Fibers Prepared by Cross-linking/Wet Spinning , Sen-i Gakkaishi 47 (1), 5 ( 1991).

Hwang, K. S., Lin, C. A., and Lin, C. H., to be published.

Japanese patent 46-11457, March 23, 1971.

Japanese patent 46-28220, August 16, 1971.

Japanese patent 47-50337, December 18, 1972.

Japanese patent 62-104912, May 15, 1987.

Japanese patent 62-149909, July 3, 1987.

10.

Pritchard, J.G. , "Poly ( vinyl alcohol) Basic Properties and Uses," Gordon and Breach Science Publishers, London, 1970.

11.

Samuels, R.J. , "Structured Polymer Properties," John Wiley and Sons, NY, 1974.

12.

Shibyama, M. , Hayasaki, T. , Chen , J.H. , Nomura, S. , and Fujiwara, H. , Structure and Properties of High Strength Poly( vinyl Alcohol) Fibers Prepared by Cross-linking/Wet Spinning, I: Mechanical and Thermal Properties, Sen-i Gakkaishi 46(1), 15 ( 1990).

13.

US patent 3660556, May 2, 1969.