Diffusion of large polymeric molecules into wool fibers is confirmed. Penetration occurs through the nonkeratinous regions, similar to dye diffusion, and indicates that selective modification of the mechanical properties of these regions is possible using this technique. Micrographs of affected sections of treated and untreated wool subjected to Martindale abrasion testing show that treated, cured wool has improved resistance to abrasion.
Get full access to this article
View all access options for this article.
References
1.
Allen, L.A., Bacon-Hall. R.E., Ellis, B.C., and Leeder, J.D., The Abrasion Resistance of Wool Fabrics, in "Proc. 6th Int. Wool Text. Res. Conf, Pretoria," vol. IV, 1980. pp. 185-197.
2.
Baumann, H., in "Fibrous Proteins, Scientific, Industrial and Medical Aspects," vol. II, D. A. D. Parry and L. H. Creamer, Eds., Academic Press. New York. 1979.
3.
Cook, J.R., and Fleischfresser, B.E., Sorption of Water-Soluble Anionic Polymers by Wool, Textile Res. J54, 441-446 (1984).
4.
Filshle, B.K. , and Rogers, G.E., The Fine Structure of a-Keratin, J. Mol. Biol.III (6). 784-786 (1961).
5.
Guise, G.B., and Jackson, M.B., TheShrinkproofing of Wool with the Bisulphite Adduct of Polyisocyanates, J. Textile Inst.64, 665-667 ( 1973).
6.
Leeder, J.D. , and Rippon, J.A., Histological Differentiation of Wool Fibres in Formic Acid, J. Textile Inst, 73, 149-151 (1982).
7.
Leeder, J.D. , and Rippon, J.A., Some Observations on the Dyeing of Wool from Aqueous Formic Acid, J. Soc. Dyers Color.99, 64-65 (1983).
8.
Leeder, J.D., Rippon, J.A., Rothery, F.E., and Staple-ton, I.W. , Use of the Transmission Electron Microscope to Study Dyeing and Diffusion Processes, in "Proc. 7th Int. Wool Text. Res. Conf, Tokyo," vol. V, 1985, pp. 99-108.
9.
Orwin, D.F.G. , and Thomson, R.W., The Electron Microscopy of Two Types of Fibre Damage and Its Relationship to Some Cell Components. in "Proc. 5th Int. Wool Text. Res. Conf, Aachen ," vol. II, 1975, pp. 173-183.
10.
Rippon, J.A. , and Rushforth, M.A., Recent Developments in Polymer Shrinkresist Processes for Wool. Part I: Use of the Water-soluble Bisulphite Addition Product of a Polyisocyanate, Textileveredlung11 (6), 224-229 . (1976).
11.
Tester, D., Observations on the Fracture Ptanes of Fibers from Martindale Abraded Wool Fabrics, Textile Res. J.54, 75-76 (1984).
12.
Zahn, H., Wool is Not Keratin Only, in "Proc. 6th Int. Wool Text. Res. Conf., Pretoria," 1980.